Low-temperature melting block finished glaze and preparation method thereof

A low-temperature frit and finished product technology, which is applied in the field of low-temperature frit finished glaze and its preparation, can solve the problem of high firing temperature, and achieve the effects of reducing temperature resistance requirements, bright color, and production cost.

Active Publication Date: 2011-07-27
JIANGSU BAIFU TECH CO LTD
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a low-temperature frit finished glaze and its production method in view of the problems existing in the prior art. This low-temperature frit finished glaze can realize the qualified firing of ceramic glazes at 850°C to 900°C. The product solves the problem of high firing temperature when firing ceramic glazes in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] (1) Preparation of low-temperature frit: according to the weight percentage of the following raw materials:

[0038] Industrial Quartz 30% Aluminum Hydroxide 5%

[0039] Potassium carbonate 5.5% Lithium carbonate 2.5%

[0040] Lithium fluoride 1.5% Calcium carbonate 3.5%

[0041] Zinc oxide 4% Boric acid 20%

[0042] Borax 8% Red lead 20%

[0043] Weigh the raw materials of the above components, sieving (above 40 mesh), stir and mix the materials for 20-30 minutes to homogenize, and melt them at a temperature of 1400°C with a melting cycle of 6 hours to obtain the invention. Of low-temperature frit.

[0044] (2) Low-temperature frit finished glaze:

[0045] By mixing 90 parts by weight of low-temperature frit and 10 parts by weight of kaolin, uniformly mixing, ball milling and pressing, drying and powdering at a drying temperature of 145°C, the low-temperature frit product glaze of the present invention can be prepared.

Embodiment 2

[0047] (1) Preparation of low-temperature frit: according to the weight percentage of the following raw materials:

[0048] Industrial Quartz 26.5% Aluminum Hydroxide 4.5%

[0049] Potassium carbonate 3.8% Lithium carbonate 3%

[0050] Lithium fluoride 0.3% Calcium carbonate 1.3%

[0051] Zinc oxide 2.4% Boric acid 21.2%

[0052] Borax 10.5% Red lead 26.5%

[0053] Weigh the raw materials of the above components, sieving (above 40 mesh), stir and mix the mixture for 20-30 minutes to homogenize, then melt at 1450°C with a melting period of 7 hours to obtain the invention Of low-temperature frit.

[0054] (3) Low-temperature frit finished glaze:

[0055] 92 parts by weight of low-temperature frit and 8 parts by weight of kaolin are mixed uniformly, and then ball milled, press-filtered, dried and powdered at a drying temperature of 140° C., to obtain the low-temperature frit product glaze of the present invention.

Embodiment 3

[0057] (1) Preparation of low-temperature frit: according to the weight percentage of the following raw materials:

[0058] Industrial Quartz 25.5% Aluminum Hydroxide 5%

[0059] Potassium carbonate 4.6% Lithium carbonate 4%

[0060] Lithium fluoride 0.9% Calcium carbonate 2%

[0061] Zinc oxide 3% Boric acid 15%

[0062] Borax 12% Red lead 28%

[0063] Weigh the raw materials of the above components, sieving (above 40 mesh), stir and mix the mixture for 20-30 minutes to homogenize, and then melt it at a temperature of 1500°C with a melting period of 5.5 hours to obtain the invention. Of low-temperature frit.

[0064] (2) Low-temperature frit finished glaze:

[0065] 91 parts by weight of low-temperature frit and 9 parts by weight of kaolin are mixed uniformly, ball-milled, filtered, dried and powdered, and the drying temperature is 150° C. to obtain the low-temperature frit product glaze of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-temperature melting block finished glaze and a preparation method thereof. The low-temperature melting block finished glaze is prepared by uniformly mixing the following materials in parts by weight: 90-94 parts of low-temperature melting block and 6-10 parts of kaolin, wherein the low-temperature melting block comprises mineral materials, mineralizing agents and fluxing agents; the mineral materials are industrial quartz and aluminium hydroxide; the mineralizing agents are potassium carbonate, lithium carbonate and lithium fluoride; and the fluxing agents are calcium carbonate, zinc oxide, boric acid, sodium borate and red lead. In the low-temperature melting block finished glaze prepared by the invention, qualified ceramic can be glaze-fired at the temperature of 850-900 DEG C, so that the temperature resistance requirement on kiln furnace equipment is reduced, the energy consumption of a ceramic product is reduced, further the manufacturing cost is reduced and ceramic pigment generates brighter color on the ceramic product.

Description

Technical field [0001] The invention relates to the technical field of frit glaze for ceramic products, in particular to a low-temperature frit finished glaze and a preparation method thereof. Background technique [0002] At present, in the production of ceramic products, most of the firing of ceramic products uses secondary firing: primary firing and primary glaze firing. In order to achieve the purpose of energy saving, many businesses have conducted research on how to reduce the firing temperature during the ceramic glaze firing process. Since the 1970s, the firing temperature of ceramic products has dropped significantly, saving a lot of precious energy and ensuring the continuous and stable development of the ceramic industry. [0003] A low-temperature biscuit firing and a high-temperature glaze firing process are adopted. When the high-temperature glaze is fired, the bisque-fired inside will volatilize, so that pinholes will appear on the surface of the product, resulting i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 范盘华徐和良
Owner JIANGSU BAIFU TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap