Carbon fiber heating paper and preparation method thereof

A technology of carbon fiber heating and carbon fiber paper, which is applied in fiber raw material processing, synthetic cellulose/non-cellulose material pulp/paper, fiber dispersant addition, etc. , Heating unevenness and other issues, to achieve more uniform heating, improve uniformity, and easy cost control

Active Publication Date: 2012-08-29
WUHAN SAIYANG INDOOR CLIMATE
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The contact points between carbon fibers are completely random, and there is no contact between many carbon fibers and other fibers at all, which results in a considerable proportion of carbon fibers that cannot participate in the overall heating; in addition, the diameter of carbon fibers is very small, and the The point contact between them is often a Schottky contact, and the electrical conduction and thermal conduction efficiency of the Schottky contact are very poor.
To sum up, the random contact between carbon fibers causes some carbon fibers not to participate in heating, while the carbon fibers participating in heating tend to have relatively low thermal conductivity efficiency, resulting in low overall heating and thermal conductivity efficiency of heating paper, as well as uneven heating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon fiber heating paper and preparation method thereof
  • Carbon fiber heating paper and preparation method thereof
  • Carbon fiber heating paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Example 1: Weigh 2 g of polyacrylonitrile-based carbon fibers and 0.02 g of graphene, soak them in 0.01 mol / L NaOH solution for 1 hour, then wash with pure water until the pH is neutral, and mix the solutions of the two substances After mixing with the dispersant, ultrasonically disperse for 10 minutes, and rinse with pure water until neutral. After the above-mentioned mixture was added into a beater for beating, it was then mixed with 8 g of pulp for beating. The mixed pulp is sheeted and dried.

[0032] The mass percent that polyacrylonitrile carbon fiber accounts for in the carbon fiber paper that utilizes this example to make is 20%, graphene 0.2%, plant fiber 78%, other components such as adhesive 1.8%. The specific indicators are as follows: weight per unit area 44 g / m 2 , thickness 0.12 mm, resistivity 0.22 Ω?cm, radiation surface electric power density 0.92 W / cm 2 , The electric-thermal radiation conversion efficiency is 97%, and the temperature unevenness of...

Embodiment 2

[0034] Embodiment 2: Take polyacrylonitrile-based carbon fiber 2 g, graphene 0.002 g, immerse in the NaOH solution of 0.01 mol / L for 2 hours, then wash with pure water until the pH is neutral, the solution of the two substances and After mixing the dispersants, ultrasonically disperse for 10 minutes, and rinse with pure water until neutral. After the above-mentioned mixture is added into a beater for beating, it is then mixed with 8g of pulp for beating. The mixed pulp is sheeted and dried.

[0035] The mass percentage of polyacrylonitrile carbon fiber in the carbon fiber paper made by using this example is 20%, graphene 0.02%, plant fiber 78%, adhesive agent and other components 1.98%. Its specific indicators are as follows: weight per unit area 44.5 g / cm 2 , thickness 0.12 mm, resistivity 0.24 Ω?cm, radiation surface electric power density 0.91 W / cm 2 . The electric-thermal radiation conversion efficiency is 96%, and the temperature uniformity of the radiation surface is...

Embodiment 3

[0037] Example 3 As a comparison without adding graphene: Weigh 2 g of polyacrylonitrile-based carbon fiber, immerse it in 0.01 mol / L NaOH solution for 1 hour, then wash it with pure water until the pH is neutral, and mix the solutions of the two substances After mixing with the dispersant, ultrasonically disperse for 10 minutes, and rinse with pure water until neutral. After the above-mentioned mixture is added into a beater for beating, it is then mixed with 8g of pulp for beating. The mixed pulp is sheeted and dried.

[0038] The mass percent of polyacrylonitrile carbon fiber in the carbon fiber paper prepared by using this example is 20%, plant fiber is 78%, and other components such as adhesive are 2%. Its specific indicators are as follows: weight per unit area 44.9 g / cm 2 , thickness 0.12 mm, resistivity 0.27 Ω?cm, radiation surface electric power density 0.6 W / cm 2. The electric-thermal radiation conversion efficiency is 59%, and the temperature unevenness of the r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a carbon fiber heating paper. The carbon fiber heating paper contains 5 to 60 percent of carbon fibers and 0.01 to 0.50 percent of graphene based on the total weight. A preparation method of the carbon fiber heating paper comprises the following steps of: mixing and pulping the graphene and the polyacrylonitrile-based carbon fibers, putting the mixture into paper pulp, beating the pulp, manufacturing paper with the pulp, and drying the paper to form the carbon fiber heating paper. The carbon fiber heating paper is applied in the field of electric heating paper; and compared with the common carbon fiber heating paper without the graphene, the heating efficiency of the carbon fiber heating paper is improved by nearly 90 percent, and the uniformity of the carbon fiber heating paper is greatly improved.

Description

technical field [0001] The invention belongs to the field of carbon materials, and relates to a carbon fiber heating paper and a preparation method thereof. Background technique [0002] As a new type of carbon material, carbon fiber has a series of excellent characteristics such as low density, high strength, good rigidity, high temperature resistance, chemical corrosion resistance, radiation resistance, fatigue resistance, high thermal conductivity, and small thermal expansion. Known as the fourth category of industrial materials. In terms of application, carbon fiber is rarely used directly, and most of it is made into intermediate products or composite materials through deep processing. Carbon fiber paper is one of the deep-processed products. [0003] Carbon fiber paper refers to the use of carbon fiber and other fibers (plant fiber or non-plant fiber) to add binders, surfactants and fillers, after beating, it is made by wet method, and then dried. The carbon fiber co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H13/50D21H21/08
Inventor 刁炜江莉
Owner WUHAN SAIYANG INDOOR CLIMATE