Dry-mixed masonry mortar for industrial dust

A dry-mixed mortar and dust technology, which is applied in the field of industrial dust dry-mixed mortar, can solve the problems of mortar cracking and inability to be applied in the field of dry-mixed mortar production, and achieve the effects of increasing strength, reducing shrinkage and cracking, and reducing volatilization

Active Publication Date: 2011-09-28
山东丞华企业投资控股有限公司
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, the aggregate finer than 200 mesh fine powder used in mortar should not exceed 4%, otherwise the mortar will crack quickly during the drying process
Therefore, although industrial dust contains a large amount of beneficial substances, it still cannot be applied in the field of dry-mixed mortar production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dry-mixed masonry mortar for industrial dust
  • Dry-mixed masonry mortar for industrial dust
  • Dry-mixed masonry mortar for industrial dust

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1 (interior wall plastering dry-mixed mortar):

[0024] formula:

[0025] Ordinary silicon cement 425#: 9Kg Mining industrial dust: 12Kg

[0026] Machine-made sand: 80Kg (fineness less than 4mm) Composite activator: 0.35Kg

[0027] Composite water retaining agent: 0.08Kg Perlite (40 mesh): 0.1Kg

[0028] The composite activator is: triethanolamine, triisopropanolamine and polycarboxylate water reducer compounded in a weight ratio of 1:1:1.

[0029] The composite water-retaining agent is composed of hydroxypropyl methylcellulose and polyacrylamide in a weight ratio of 3:5.

[0030] Preparation:

[0031] After accurately measuring various raw materials according to the above formula, mix and force mechanical stirring to obtain the target product.

Embodiment 2

[0032] Embodiment 2 (external wall plastering dry-mixed mortar):

[0033] Ordinary silicon cement 425#: 9Kg Mining industrial dust: 12Kg

[0034] Machine-made sand: 80Kg (fineness less than 4mm) Composite activator: 0.35Kg

[0035] Composite water retaining agent: 0.08Kg Perlite (40 mesh): 0.1Kg

[0036] Sodium stearate: 0.1Kg

[0037] The composite activator is: triethanolamine, triisopropanolamine and polycarboxylate water reducer compounded in a weight ratio of 1:1:1.

[0038] The composite water-retaining agent is composed of hydroxypropyl methylcellulose and polyacrylamide in a weight ratio of 3:5.

[0039] Preparation:

[0040] After accurately measuring various raw materials according to the above formula, mix and force mechanical stirring to obtain the target product.

Embodiment 3

[0041] Embodiment three (interior wall plastering dry-mixed mortar):

[0042] formula:

[0043] Ordinary silicon cement 425#: 10Kg Sand and gravel crushing industrial dust: 15Kg

[0044] Construction waste crushed particles: 74Kg (fineness less than 4mm) Composite activator: 0.4Kg

[0045] Composite water retaining agent: 0.085Kg Microcrystalline paraffin: 0.15Kg

[0046] Fly ash: 1Kg

[0047] The composite activator is: triethanolamine, triisopropanolamine and polycarboxylate water reducer compounded in a weight ratio of 1:1:1.

[0048] The composite water-retaining agent is composed of hydroxypropyl methylcellulose and polyacrylamide in a weight ratio of 3:5.

[0049] Preparation:

[0050] After accurately measuring various raw materials according to the above formula, mix and force mechanical stirring to obtain the target product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses dry-mixed masonry mortar for industrial dust, belonging to a premixed dry-mixed masonry mortar material for a building. The dry-mixed masonry mortar is prepared from the following ingredients in parts by weight: 8-12 parts of cement, 10-20 parts of industrial dust, 0-3 parts of coal ash, 65-82 parts of aggregate, 0.3-0.5 part of compound activator, 0.08-0.1 part of compound water-retaining agent, 0.1-0.2 part of crack-resisting agent and 0-0.3 part of water repellent agent. Compared with the prior art, the dry-mixed masonry mortar can be additionally added with 10-20 percent fine powder with granularity of less than 200mu without causing cracking, therefore, the traditional provision that the addition amount of the fine powder with the granularity of less than 200mu is not more than 4 percent is thoroughly broken, and a bran-new path for utilization of industrial dust is developed.

Description

technical field [0001] The invention relates to a ready-mixed dry-mixed mortar material for construction, in particular to an industrial dust dry-mixed mortar. Background technique [0002] With the development of society, people's requirements for project quality, environmental protection requirements and civilized construction are constantly improving, and the advantages of dry-mixed mortar are favored by more and more people. [0003] Mine mining, sandstone crushing, block grinding, factory production, etc. form a large amount of ultra-fine dust finer than 200 mesh every year, especially in the process of gold mining, a large amount of tailings fine powder of about 400 mesh is formed, which occupies a large amount of Cultivated land seriously pollutes the air. [0004] In the prior art, the aggregate finer than 200 mesh fine powder used in the mortar should not exceed 4%, otherwise the mortar will crack quickly during the drying process. Therefore, although industrial d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B18/04
CPCC04B28/02Y02W30/91C04B14/02C04B14/18C04B18/08C04B18/16C04B20/0076C04B24/08C04B24/122C04B24/2641C04B40/0608C04B2103/0052C04B2103/46C04B24/2652C04B24/36C04B24/383
Inventor 王爱民王庆珍赵兵赵同习张培清张萍
Owner 山东丞华企业投资控股有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com