Enhanced faucet and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A faucet, enhanced technology, applied in the field of faucets, can solve the problems of many consumables, troublesome production, high production cost, etc.
Active Publication Date: 2013-02-06
XIAMEN RUNNER IND CORP
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
There are many steps to make the above-mentioned plastic faucet, which is cumbersome, time-consuming and labor-intensive, and the production cost is relatively high; in addition, the water inlet and outlet channels of the second type of faucet above are only composed of simple grooves, and the other parts of the upper and lower body are entities. More, the upper and lower bodies are prone to deformation during injection molding, and it is troublesome to accurately match the grooves of the upper and lower bodies, and the joint surface of the upper and lower bodies will expand with heat and contract with cold water, causing gaps to appear on the joint surface. Water strings or leaks are likely to occur between the hot water channels, which will affect the use of the faucet
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] 1. First, mix and stir 1000g of polyurethaneelastomer and 4000g of ferrite, and make granular high-density elastomer material through an extruder;
[0019] 2. Dry the granular high-density elastomer material and put it into the injection molding machine to prepare the three-component body reinforcement by injection molding;
[0020] 3. The three-component body reinforcement is coated on the waterway component made of polyoxymethylene resin (POM) by ultrasonic welding;
[0021] 4. Finally, assemble the prepared components of conventionally produced faucets-ABS shell (surface is electroplated), shell assembly, valve core assembly, handle assembly, water softener assembly, sealing ring, etc., according to the conventional assembly method. Complete set of faucets.
[0022] figure 1 It is a schematic diagram of the structural composition of the enhanced faucet reinforcement coated water channel assembly prepared in Example 1 of the present invention. exist figure 1 Amon...
Embodiment 2
[0024] 1. First mix 2000g of polyolefin elastomer and 3000g of bariumsulfate, and make it into granular high-density elastomer material through extruder;
[0025] 2. Dry the granular high-density elastomer material and put it into the injection molding machine to prepare the three-component body reinforcement by injection molding;
[0026] 3. The three-component body reinforcement is coated on the water channel component made of polyphenylene sulfide (PPS) material by self-locking method;
[0027] 4. Finally, prepare the conventionally produced faucet supporting parts - stamped stainless steel shell (vacuum coating on the surface), shell components, valve core components, handle components, water softener components, sealing rings, etc. according to the conventional Assembly method Assemble as a complete faucet.
[0028] figure 2 It is a schematic diagram of the structural composition of the enhanced faucet reinforcement coated water channel assembly prepared in Example 1 ...
Embodiment 3
[0030] 1. First mix and stir 2000g of silicone rubber and 5000g of bariumsulfate, add cross-linking agent, coupling agent and other auxiliary agents, knead in the open mill to make a lump material;
[0031] 2. Cast the lump material in the mold of split body, take it out after cooling and forming;
[0032] 3. The two-component body reinforcement is coated on the waterway component made of polyphenylene oxide (PPO) material by glue bonding;
[0033] 4. Finally, prepare the conventionally produced faucet supporting parts-aluminum alloy shell (electroplating and vacuum coating on the surface), shell components, valve core components, handle components, water softener components, sealing rings, etc. according to the conventional Assembly method Assemble as a complete faucet.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention provides an enhanced faucet and a preparation method thereof and relates to a faucet. The invention provides the enhanced faucet and the preparation method thereof. The enhanced faucet is equipped with a shell component, a valve core component, a handle component, a water softening device component, a seal ring, a water channel component and a split reinforcement, wherein the split reinforcement wraps the water channel component by virtue of ultrasonic welding, a self-locking device, sticking and other modes; and the split reinforcement is used for enhancing the water channel component and simultaneously increasing the weight of the whole faucet. The preparation method comprises the following steps: preparing the split reinforcement by adopting an injection molding or casting mode; wrapping the split reinforcement on the water channel component; installing the split reinforcement coated with the water channel component on the shell component; and assembling the prepared faucet fittings which are conventionally produced into the enhanced faucet according to the conventional assembly mode, wherein the faucet fittings comprise the valve core component, the handle component, the water softening device component, the seal ring and the like.
Description
technical field [0001] The invention relates to a faucet, in particular to an enhanced faucet and a preparation method thereof. Background technique [0002] Most of the plastic faucets on the existing market are made of ABS plastic, and the surface treatment (electroplating, vacuum coating, etc.) Reaction molding at room temperature. The disadvantage of this kind of plastic faucet is that the weight is not enough, and the burst pressure resistance of the water channel is not enough, so it cannot fully meet the requirements of customers. [0003] At present, there are various plastic faucets on the market. There are roughly two kinds of mixed plastic faucets that can enter hot and cold water. Chinese patent ZL200710070171.1); the other is mainly composed of upper and lower bodies, and the upper and lower bodies are respectively provided with mutually matching grooves. After the upper and lower bodies are combined, the mutually matching grooves form the water inlet and outl...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).