Coloring photosensitive composition, manufacture method for color filter, color filter, and liquid crystal display device

A technology of photosensitive composition and color filter, which is applied in the photoplate-making process of patterned surface, photosensitive materials used in photomechanical equipment, instruments, etc., can solve the problems of poor light fastness and achieve good color characteristics, The effect of excellent light fastness

Inactive Publication Date: 2011-11-09
FUJIFILM CORP
View PDF57 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, even pigments are known to have poor light resistance when they are miniaturized to increase brightness. For such pig...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coloring photosensitive composition, manufacture method for color filter, color filter, and liquid crystal display device
  • Coloring photosensitive composition, manufacture method for color filter, color filter, and liquid crystal display device
  • Coloring photosensitive composition, manufacture method for color filter, color filter, and liquid crystal display device

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0082] -Preparation of pigment dispersion composition-

[0083] The preparation method of the pigment dispersion composition of the present invention is not particularly limited, for example, by using a vertical or desktop sand mill, nail mill, slit mill (slit mill), ultrasonic disperser, etc., with a particle size of 0.01 The pigment dispersion composition of the present invention is obtained by finely dispersing the pigment, the pigment dispersant, and the solvent with ~1 mm beads formed of glass, zirconia, or the like.

[0084] Two-roll mill, three-roll mill, ball mill, trommel, disperser, kneader, two-way kneader, homogenizer, mixer, single-screw or twin-screw extruder can also be used before bead dispersion. Kneading and dispersing treatment is carried out while applying strong shear force.

[0085] In addition, details about kneading and dispersion are described in "Paint Flow and Pigment Dispersion" by T.C. Patton (Journal of John Wiley and Sons Co., Ltd., 1964).

[0...

Embodiment 1

[0320]

[0321] The colored photosensitive composition of Example 1 was prepared by stirring and mixing the components shown in the following composition 1.

[0322] (composition 1)

[0323] Pigment dispersion PG58: 36.6 parts of pigment dispersion containing green pigment PG58

[0324] Pigment dispersion PY150: 12.6 parts of pigment dispersion containing yellow pigment PY150

[0325] 25.8 parts of solvent (PGMEA)

[0326] · Solvent (EEP) 16.7 parts

[0327] ・Binder resin (allyl methacrylate-methacrylic acid (=copolymerization molar ratio: 8:2) copolymer, weight average molecular weight: 30,000) 1.76 parts

[0328] ・Polymerizable monomer: ARONIX M-520 (manufactured by Toagosei Co., Ltd.) 3.77 parts

[0329] ・Photopolymerization initiator 1: 0.71 parts of IRGACURE OXE01 (manufactured by CIBA Corporation)

[0330] · Photopolymerization initiator 2: 0.35 parts of 2-chlorophenyl-4,5-bisphenylimidazole dimer (manufactured by Hodogaya Chemical Co., Ltd., B-CIM)

[0331] 0.49...

Embodiment 2～37、 comparative example 1～18

[0353] In the composition 1 of Example 1, the type of the pigment dispersion liquid, the type of the photopolymerization initiator 1, the type and the amount of the additives were changed as described in Tables 1 to 3, and it was the same as that of Example 1 except that Each colored photosensitive composition of Examples 2-37 and Comparative Examples 1-18 was prepared accurately. Moreover, except having changed the exposure system in an exposure process as described in Tables 1-3 using each obtained colored photosensitive composition, it carried out similarly to Example 1, and produced the colored pattern.

[0354] In Tables 1-3, the detail of the exposure system described as a proximity type is the exposure system (proximity type exposure) applied to the exposure process in Example 1. In addition, in Tables 1-3, the detail of the exposure system described as a laser is as follows.

[0355] -Exposure process (laser exposure)-

[0356] After the pre-baking process, as a lase...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a coloring photosensitive composition, a color filter using the coloring photosensitive composition, and a liquid crystal display device provided with the color filter, the coloring photosensitive composition comprises (A) a colorant provided with a phthalocyanine frame, (B) a solvent, (C) a polymerizable monomer, (D) an adhesive resin, (E) a photopolymerizable initiator, and (F) a polymerizable compound.

Description

technical field [0001] The present invention relates to a colored photosensitive composition having excellent light resistance and developability / solvent resistance while maintaining the characteristics of high transparency and high color purity of a colorant, and a colored photosensitive composition containing the same in a colored pattern A color filter for objects, a method for manufacturing the color filter, and a liquid crystal display device. Background technique [0002] In the past, in small liquid crystal display devices such as mobile phones, mobile game machines, and PDAs, it was necessary to use a backlight light source with a limited capacity such as a secondary battery or a dry battery, so as a colorant for the color filter used in these display devices, It has been advantageous to use a colorant that has high transparency and can transmit bright lines of a backlight well to display colors. [0003] In recent years, the increase in size of liquid crystal displ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G03F7/004G03F7/032G03F7/00G02B5/20G02F1/1335
Inventor 佐竹亮冈部孝太郎
Owner FUJIFILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap