Cation viscose vortex spun woven fabric and preparation method thereof

A manufacturing method, vortex spinning technology, applied in textiles and papermaking, textiles, fabrics, etc., can solve problems such as inconvenient operation, low production efficiency, and easy pilling of fabrics

Active Publication Date: 2013-04-03
HANGZHOU AOHUA TEXTILE
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem solved by the present invention is that the fabrics provided by the prior art have long hairiness and poor evenness, and the resulting fabrics are extremely easy to pill, have poor washability and wear resistance, and the clothes are easily deformed, which cannot meet People have higher and higher requirements for clothing fabrics, and the production efficiency is low, the operation is inconvenient, and the product yield is low, and then a method for manufacturing a cathodic vortex spinning woven fabric and a fabric woven by this manufacturing method are provided. Catagory vortex woven fabric

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention is preferably specifically described below through examples, but the protection scope of the present invention is not limited thereto.

[0026] The present invention relates to a kind of manufacturing method of cathodic vortex spinning woven fabric, and described manufacturing method comprises the following steps:

[0027] Step 1: use a carding machine to produce cationic polyester fiber raw slivers and viscose fiber raw slivers respectively, draw on a drawing frame according to the ratio to obtain cationic viscose cooked slivers;

[0028] In this step, the cationic polyester fiber has a density of 1.2-1.4D and a length of 38mm, and the viscose fiber has a density of 1.2-1.4D and a length of 38mm; The ratio of fiber raw sliver drawing is 10-90% for cationic fiber raw sliver and 10-90% for viscose fiber raw sliver. In this step, the ratio of the cationic fiber raw sliver to the viscose fiber raw sliver can be 90 / 10, 80 / 20, 70 / 30, 65 / 35, 50 / 50, etc....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for manufacturing a cationic vortex spinning woven fabric. The cationic vortex is spun out at a certain speed by drawing cationic polyester fibers and viscose fibers on a drawing frame according to the ratio. Spun single yarn, after warping, paralleling, and sizing, obtain the catabolic vortex spun single yarn as the warp beam of the cationic vortex spun woven fabric, and use the single warp beam loom to make the above-mentioned cathodic vortex spun single yarn Warp threads and other raw materials are used as weft threads, which are woven into one according to the requirements of different tissues. After secondary light desizing, secondary dyeing and drying, the dyed cathodic eddy current woven fabric is obtained. The cathodic vortex woven fabric prepared by this method is suitable for clothing fabrics, with smooth surface, soft hand feeling, excellent anti-pilling, washability and hygroscopicity, which is better than ordinary polyester-viscose fabrics in surface quality. Improvement, cost reduction, saving the energy consumption of two-for-one twisted strands, improving the various index requirements of fabrics, suitable for large-scale fabric processing and weaving.

Description

technical field [0001] The invention belongs to the technical field of textiles and textile manufacturing, and in particular relates to a method for manufacturing a catabolic vortex woven fabric and a cathodic vortex woven fabric produced by the manufacturing method. Background technique [0002] Yang-bonded vortex woven fabric is also called Yang-bonded cloth, which is mainly used for clothing manufacturing fabrics, because it has the effect of wool-like fabrics, has good breathability and moisture permeability and is easy to wash, so it is a wool-like top for men and women, The main fabric in trousers. [0003] Along with the continuous improvement of people's living standards, in the fast-paced, high-efficiency, heavy-duty modern society, people desire to pursue randomness, comfort and practicality in nature. If it is not well dried, it is very easy to pilling, has poor washability and wear resistance, and is easy to deform after several washings, which cannot meet peopl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04D03D15/00D06M15/11D06P1/00D06P1/38D06P1/30D06P3/87D06M101/32D06M101/06D03D15/225D03D15/283
Inventor 朱生贤
Owner HANGZHOU AOHUA TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap