Method for processing high-strength fastener and hot-treating process

A fastener and high-strength technology, which is applied in the processing method and heat treatment process of high-strength fasteners, can solve the problems of reducing productivity, wasting energy, prolonging production cycle, etc., to improve performance, improve production efficiency, save energy energy effect

Active Publication Date: 2013-03-20
南通翔宇健身器材科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, no matter it is annealing before cold working or heat treatment of quenching and tempering after cold working, it not only wastes energy, but also prolongs the production cycle and reduces productivity, especially the annealing before cold working will cause surface oxidation after annealing. It is necessary to further implement the process of removing the oxide film by pickling and covering the surface with a lubricating film. These are obviously not suitable for the requirements of the modern society for the steel industry, and urgent improvements are needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0017] Step 1), design and smelt raw material steel with suitable chemical composition, the raw material steel of the present invention contains, by mass percentage, C 0.23, Si 0.07, Mn 0.35, Al 0.09, Mo 0.60, Cr 1.30, Ti 0.06, Nb 0.06 , V 0.06, Cu 0.70, W 0.70, B 0.001, P 0.006, S 0.007;

[0018] Step 2), the raw material steel is subjected to hot rolling processing, wherein soaking at 1200°C for 2 hours, the starting rolling temperature is about 1010°C, the final rolling temperature is about 930°C, the coiling temperature is 720°C, and the cooling rate is about 1°C / S. After hot rolling Steel diameter is about 10mm;

[0019] Step 3), the hot-rolled steel is subjected to wire drawing processing with a processing rate of 8%;

[0020] Step 4), cold processing the steel after wire drawing processing to become a part blank with a desired shape;

[0021] Step 5), processing and forming threads at a specific part of the part blank by means of thread rolling or the like;

[0022] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to an economical and timesaving, low-cost and high-performance method for processing a fastener and a hot-treating process. The raw material steel of the fastener contains the following ingredients in percentage by mass: 0.2-0.25% of C, 0.05-0.1% of Si, 0.3-0.4% of Mn, 0.08-0.1% of Al, 0.5-0.8% of Mo, 1.2-1.4% of Cr, less than 0.5% of Ni, 0.05-0.07% of Ti, 0.05-0.07% of Nb, 0.05-0.07% of V, 0.6-0.8% of Cu, 0.5-0.8% of W, 0.001-0.002% of B, less than 0.008% of P and less than 0.008% of S. An economical preparing process which has no need of carrying out annealing treatment before cold-processing is realized by using the unique processing steps, such as hot-rolling processing, drawing processing, cold-processing, quenching and tempering and the like and the excellent-malleability fastener with high tensile strength over 1300 MPa and over 4% percentage elongation.

Description

technical field [0001] The invention relates to a preparation and heat treatment process of mechanical parts, in particular to a processing method and heat treatment process of high-strength fasteners. Background technique [0002] With the rapid development of modern industry, various production departments such as automobiles, machinery, construction, and light industry have put forward higher requirements for various fasteners (such as bolts, nuts, etc.). Especially in the field of the automobile industry, in order to meet the increasingly strong requirements for high performance and lightweight of various structural parts, it is undoubtedly the most effective to implement high-strength and lightweight bolts and nuts that are used to manufacture fastening parts. means. In addition, due to the requirements of weather resistance, corrosion resistance and other aspects, there are more and more strict requirements for the corresponding performance of bolts and nuts. [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/54C22C38/32C21D1/25
Inventor 曾美霞
Owner 南通翔宇健身器材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com