A special solvent-based primer for 3c product magnesium-aluminum alloy materials and preparation method thereof

A magnesium-aluminum alloy and solvent-based technology, applied in the field of solvent-based primers and their preparation, can solve the problems of expensive magnesium-aluminum alloy materials, cannot be easily scrapped, and high porosity, and achieves good interlayer adhesion and excellent resistance to boiling water. performance effect

Active Publication Date: 2011-12-07
东莞大宝化工制品有限公司 +1
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And because of its high porosity and easy water absorption, it is difficult to achieve excellent water boiling resistance, so it has high performance requirements for the primer in direct contact with it.
[0003] Although the traditional primers for magnesium-aluminum alloys can improve some properties, there are still some shortcomings: on the one hand, due to the good high-temperature resistance of magnesium-aluminum

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A special solvent-based primer for 3c product magnesium-aluminum alloy materials and preparation method thereof
  • A special solvent-based primer for 3c product magnesium-aluminum alloy materials and preparation method thereof
  • A special solvent-based primer for 3c product magnesium-aluminum alloy materials and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A special solvent-based black primer for magnesium-aluminum alloy materials of 3C products, calculated by weight percentage, including the following substances: saturated polyester (polymer polyester resin) 65%, pigment (carbon black) 3%, dispersant 1.8% , anti-settling agent (polyethylene wax) 1%, filler (aluminum tripolyphosphate) 10%, adhesive agent (bisphenol A epoxy resin) 1%, leveling agent (modified polysiloxane) 2%, even Joint agent (epoxy silane cocondensate) 0.5%, solvent 15.7%.

[0029] The method for preparing a special solvent-based black primer for magnesium-aluminum alloy materials of 3C products comprises the following preparation steps:

[0030] Step A, first mix the dispersant, pigment, 35% saturated polyester and 2% solvent of the amount, and stir at a high speed for 12 minutes at 1200rpm with a stirrer to obtain a uniformly dispersed mixed slurry I, then use sand The mill grinds the mixed slurry I to a fineness of less than 10 microns to obtain the ...

Embodiment 2

[0039] A special solvent-based black primer for magnesium-aluminum alloy materials of 3C products, calculated by weight percentage, including the following substances: saturated polyester (polymer polyester resin) 52%, pigment (carbon black) 20%, dispersant 1% , anti-settling agent (polyethylene wax) 3%, filler (aluminum tripolyphosphate) 5%, adhesive agent (bisphenol A epoxy resin) 2%, leveling agent (modified polysiloxane) 5%, even Joint agent (epoxy silane cocondensate) 2%, solvent 10%.

[0040] The method for preparing the solvent-based black primer dedicated to the magnesium-aluminum alloy material of the 3C product includes the following preparation steps:

[0041] Step A, first mix the dispersant, pigment, 20% saturated polyester and 2% solvent of said amount, and stir at a high speed for 15 minutes at 1000rpm with a stirrer to obtain a uniformly dispersed mixed slurry I, and then use sand The mill grinds the mixed slurry I to a fineness of less than 10 microns to obta...

Embodiment 3

[0048] A special solvent-based black primer for magnesium-aluminum alloy materials of 3C products, calculated by weight percentage, including the following substances: saturated polyester (polymer polyester resin) 59.5%, pigment (carbon black) 10%, dispersant 1.5% , anti-settling agent (polyethylene wax) 2.5%, filler (aluminum tripolyphosphate) 8%, adhesive (bisphenol A epoxy resin) 0.5%, leveling agent (modified polysiloxane) 3.5%, even Joint agent (epoxy silane cocondensate) 1%, solvent 5%.

[0049] The method for preparing the solvent-based black primer dedicated to the magnesium-aluminum alloy material of the 3C product includes the following preparation steps:

[0050] Step A, first mix the dispersant, pigment, 29.5% saturated polyester and 2% solvent of the amount, and stir at a high speed for 13 minutes at 1500rpm with a stirrer to obtain a uniformly dispersed mixed slurry I, then use sand The mill grinds the mixed slurry I to a fineness of less than 10 microns to obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of solvent priming paints, in particular to a solvent priming paint special for a 3C (China Compulsory Certification) product magnesium-aluminum alloy material and a preparation method thereof. The solvent priming paint comprises substances such as saturated polyester, a pigment, a dispersing agent, an anti-settling agent, a filling, an adhesive agent,a flattening agent, a coupling agent, a solvent and the like, is prepared by performing procedures such as batch mixing, stirring, grinding and the like on different substances in different quantity relative ratios, can meet the requirements of customers on high-low temperature production lines, can be repeatedly coated and remade without causing cracking of a paint film, and has high ply adhesion and particularly high boiling water boiling resistance.

Description

technical field [0001] The invention relates to the technical field of solvent-based primers, in particular to a special solvent-based primer for magnesium-aluminum alloy materials of 3C products and a preparation method thereof. Background technique [0002] As we all know, magnesium-aluminum alloy materials are widely used in high-end 3C products such as notebook computers, mobile phones, and digital cameras due to their light weight, high temperature resistance, fast heat dissipation, and high strength (the so-called 3C products refer to computers (Computers), communications ( Communication) and Consumer Electronics (the abbreviation of the three types of electronic products). And because of its high porosity and easy water absorption, it is difficult to achieve excellent water boiling resistance, so it has higher performance requirements for the primer in direct contact with it. [0003] Although the traditional primers for magnesium-aluminum alloys can improve some pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/00C09D7/12
Inventor 陈贺生邱晓宏
Owner 东莞大宝化工制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap