A kind of foamed ceramic material made of polishing porcelain slag as main material and preparation method thereof

A technology of polishing porcelain slag and foaming ceramics, which is applied in the field of foaming materials, can solve the problems of high product cost, and achieve the effects of high fire resistance, good heat insulation performance, and low water absorption

Active Publication Date: 2011-12-28
甘伟
View PDF4 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The above-mentioned inorganic foaming materials consume more precious natur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Raw material dry material (percentage by weight):

[0042] Polishing porcelain slag 100%.

[0043] Preparation:

[0044] (1) Porcelain slag pretreatment: collect the polishing porcelain slag slurry discharged from the polishing process by using emery polishing grinding head in the ceramic industry production line, and then carry out the treatment of impurity removal, dehydration, drying and crushing, so that the polishing porcelain slag forms a fine powder ;

[0045] (2) raw material measurement: carry out the measurement and weighing of polishing porcelain slag according to the weight percentage of above-mentioned raw material;

[0046] (3) Batching: the polishing porcelain slag in step (2), then add the water that consumption is 7% of raw material dry material gross weight and carry out stirring and mixing, make it form loose, uniform water content and be the wet mix of 7% material;

[0047] (4) Blank forming: the wet mixture of step (3) is sent into the mixer for...

Embodiment 2

[0051] Raw materials (percentage by weight):

[0052] Polishing porcelain slag 80% slag powder 20%.

[0053] Preparation:

[0054] (1) Raw material pretreatment:

[0055] ① Pretreatment of polished porcelain slag: collect the polished porcelain slag slurry discharged from the polishing process by using emery polishing grinding head in the ceramic industry production line, and then carry out the treatment of impurity removal, dehydration, drying and crushing to make the polished porcelain slag into fine powder;

[0056] ② Pretreatment of slag powder: crush the slag into slag powder with a particle size of about 0.125-0.5 mm. The slag is the slag discharged from a coal-fired furnace or a coal-to-gas furnace, with a coal content of about 12%;

[0057] (2) raw material measurement: carry out the measurement and weighing of polishing porcelain slag according to the weight percentage of above-mentioned raw material;

[0058] (3) Batching: the polishing porcelain slag in step (2),...

Embodiment 3

[0063] Raw materials (percentage by weight):

[0064] Polishing porcelain slag 70%, china clay powder 30%.

[0065] Preparation:

[0066] (1) Raw material pretreatment:

[0067] ① Pretreatment of polished porcelain slag: collect the polished porcelain slag slurry discharged from the polishing process using diamond grinding heads for polishing in the ceramic industry production line, and then perform impurity removal, dehydration, drying and crushing treatments to make the polished porcelain slag form fine powder;

[0068] ②Porcelain clay powder pretreatment: remove sand or impurities from the collected china clay waste residue in the ceramic industry, and homogenize it into powder to obtain china clay powder. The mud and other uncalcined porcelain clay waste;

[0069] (2) raw material measurement: carry out the measurement and weighing of polishing porcelain slag and admixture according to the weight percentage of above-mentioned raw material;

[0070] (3) Ingredients: Mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Maximum particle sizeaaaaaaaaaa
Densityaaaaaaaaaa
Thermal conductivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a foaming ceramics material prepared through adopting polishing ceramic slags as a main raw material. The material is prepared through the following steps: mixing the following raw materials and water, wherein the raw materials comprise, by weight, 60-100% of polishing ceramic slags and 0-40% of an admixture; then carrying out compacting and forming, high temperature forming and puffing. The invention further discloses a preparation method for the foaming ceramics material. The foaming ceramics material provided by the present invention can replace the existing forming material, and has good fireproof performance and good heat insulation performance. In addition, the preparation cost is low.

Description

technical field [0001] The invention relates to a foaming material, in particular to a foaming ceramic material made of polished porcelain slag as the main material and a preparation method thereof. Background technique [0002] A large amount of ceramic solid waste slag will be produced in the production of ceramic industry, among which, the amount of polishing porcelain slag discharged by building ceramic factories during the polishing process of porcelain tiles is the largest. For example: there are more than 300 large-scale building ceramic factories in Foshan, Guangdong Province, with more than 2,000 production lines of various types, and the annual discharge of porcelain slag is more than 4 million tons. Among them, the amount of waste slag produced by a porcelain plate polishing production line is about 6-8 tons per day. In the past, these porcelain slags were mostly disposed of by stacking and landfilling. At present, the accumulated polishing porcelain slag has exc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/02C04B35/622
Inventor 张传镁甘伟徐城坤
Owner 甘伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap