Aramid 1313 Flame Retardant Viscose Multifunctional Blended Printed Camouflage Fabric

A flame-retardant viscose, multi-functional technology, applied in textiles, textiles, papermaking, fabrics, etc., can solve the problems of fabric flame-retardant performance degradation, hard hand feeling, poor color fastness, etc., and achieve good bulkiness and good drape , good color fastness

Inactive Publication Date: 2011-12-28
SHAOXING SHULILE TEXTILE PROD
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Obviously, the flame-retardant and fire-resistant fabrics manufactured by the above-mentioned traditional methods are difficult to achieve satisfactory technical indicators such as continuous burning time, damage length, wear resistance level, and tear resistance. uncomfortable to wear
[0004] Generally, aramid 1313 fabrics are dyed by convent...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aramid 1313 Flame Retardant Viscose Multifunctional Blended Printed Camouflage Fabric
  • Aramid 1313 Flame Retardant Viscose Multifunctional Blended Printed Camouflage Fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] Such as figure 1 As shown, the vertical grid represents the longitude, and the horizontal grid represents the latitude.

[0025] The invention adopts ultra-high temperature and high pressure technology to dye aramid 1313 short fiber first, then mix the dyed aramid 1313 color short fiber with flame-retardant viscose fiber and carbon black conductive fiber according to the process ratio, and use the mixed raw material Yarn is spun by the method of spinning.

[0026] The warp and weft are all selected from 32S / 2 aramid 1313 color short fiber / flame retardant viscose fiber / carbon black conductive fiber blended yarn.

[0027] The composition ratios of the warp and weft are: 50% of aramid 1313 color staple fiber, 48% of flame-retardant viscose fiber, and 2% of carbon black conductive fiber.

[0028] The grammage of the warp is 196.5g / m, and the grammage of the weft is 159.7g / m.

[0029] The warp density is 320 threads / 10cm, and the weft density is 260 threads / 10cm.

[0030...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aramid 1313 flame-retardant viscose multifunctional blended printed camouflage fabric, which is formed by interweaving warp threads and weft threads. As the fibers constituting the fabric, aramid 1313 color staple fibers/flame-retardant viscose fibers/carbon are selected. Black conductive fiber blended yarn, the above yarn has special permanent function, and adopts special dyeing, finishing and printing technology and process, which solves the problem of poor color fastness, difficult printing, hard hand feeling and flame retardant performance of traditional aramid 1313 blended fabric Poor and other problems, therefore, the spun fabric has permanent flame retardancy, high temperature resistance, high strength, wear resistance, insoluble drops in case of fire carbonization, good color fastness, good drapability, antistatic, antibacterial, moisture absorption, breathable, hand feeling Soft, good bulkiness and other functions and characteristics, and the fabric is soft, easy to put on and take off when making clothes, and move freely. Preferred fabric.

Description

technical field [0001] The invention relates to an aramid 1313 flame-retardant viscose multifunctional blended printed camouflage fabric. Background technique [0002] Previously, flame-retardant fabrics consisted of a flame-retardant layer, a waterproof and breathable layer, a heat-insulating layer and a comfort layer, which were stitched together to combine four layers of materials with different functions. [0003] Obviously, the flame-retardant and fire-resistant fabrics manufactured by the above-mentioned traditional methods are difficult to achieve satisfactory technical indicators such as continuous burning time, damage length, wear resistance level, and tear resistance. It is uncomfortable to wear. [0004] Generally, aramid 1313 fabrics are dyed by conventional methods. The color fastness is poor, printing is difficult, and the hand feels hard, and the cost is high. Rubber fiber is mostly flame retardant additive type, which is blended with aramid fiber. If it is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/12D03D13/00D02G3/04D03D15/225D03D15/283D03D15/47D03D15/513D03D15/533
Inventor 吴水明徐宝法
Owner SHAOXING SHULILE TEXTILE PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap