Abstract

The invention relates to a manufacturing method for non-oriented electric steel. The method comprises the following steps of: smelting according to a clean steel process and continuously casting into billets; heating the continuous casting billets; performing hot rolling; reeling; naturally cooling to room temperature; normalizing; performing acid washing conventionally; performing cold rolling for the first time; performing intermediate annealing in the total hydrogen atmosphere or the mixed atmosphere of hydrogen and nitrogen; performing cold rolling for the second time; performing final annealing; and cooling conventionally, coating and finishing for later use. The finished product silicon steel with coarse grains and good texture can be obtained by adopting lower process heat treatment temperature; brittleness of the steel is reduced and cold rolling performance of a steel plate is improved by adopting lower normalizing temperature and intermediate annealing temperature; the problems of surface oxidation of the steel plate, nodulation of a furnace bottom roller and the like can be effectively solved by adopting lower finished product annealing temperature; and the high-grade non-oriented silicon steel with lower iron loss can be produced stably.

Description

technical field [0001] The invention relates to a method for manufacturing non-oriented electrical steel, in particular to a method for producing high-grade non-oriented silicon steel. Background technique [0002] Non-oriented electrical steel is widely used as core material for motors and transformers. In recent years, from the viewpoint of energy saving, there has been a strong demand for improvement in the efficiency of various electric appliances, and lower iron loss is desired as core materials for motors and transformers used in these electric appliances. [0003] As a means to reduce the loss of non-oriented electrical steel, we know that the resistivity of the steel plate can be increased by increasing the content of alloying elements such as Si and Al. However, when the current non-oriented silicon steel reaches the highest level, the brittleness of the steel plate will be increased on the basis of the existing Si and Al content, and the cold rolling performance o...

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problem existing in the prior art that because the hot-rolled plate is too thin, the hot-rolled rolling pressure increases, the shape of the hot-rolled plate is difficult to ensure, and the normalization temperature or intermediate annealing temperature is too high, causing the steel plate to be too brittle and cold-rolled...

Images