Environment-friendly flame retardant asphalt and preparation method thereof

An environmentally friendly asphalt technology, applied in building insulation materials, building components, buildings, etc., can solve the problems of increasing working steps, low decomposition temperature, and unfavorable construction, so as to reduce the amount of addition, improve flame retardant performance, and flame retardant and good smoke suppression effect

Active Publication Date: 2014-05-21
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN200610082139.0 introduces a kind of halogen-free flame retardant asphalt for road use, wherein the flame retardant is melamine pyrophosphate, zinc borate and magnesium hydroxide. Aluminum hydroxide is added to the material, which increases the work steps and is not conducive to the construction
And because the decomposition temperature of aluminum hydroxide is low (140-150 ℃), it also limits its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly flame retardant asphalt and preparation method thereof
  • Environment-friendly flame retardant asphalt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Step 1: Add magnesium aluminum carbonate hydrotalcite (particle size 20-40nm), appropriate amount of deionized water and titanate coupling agent NDZ-201, which accounts for 5% of the weight of the hydrotalcite, into the reactor in sequence, and a constant temperature water bath at 80℃, Continue to stir and react for 1 hour, filter, wash, and dry to prepare surface modified hydrotalcite.

[0023] Step 2: Add 3 parts of melamine phosphate and 0.6 parts of surface-modified hydrotalcite to 100 parts of 160℃ 4% SBS modified asphalt, and mix for 1 hour with ordinary stirring (450rpm / min) to obtain flame retardant SBS modified asphalt .

Embodiment 2

[0025] The method for preparing the surface-modified hydrotalcite is the same as step 1 in Example 1, the coupling agent is stearic acid, and the amount is 8% of the weight of the hydrotalcite.

[0026] 6 parts of melamine phosphate and 1.2 parts of surface-modified hydrotalcite were added to 100 parts of 160°C SBS modified asphalt, and ordinary stirring (450 rpm / min) was mixed for 1 hour to obtain flame-retardant SBS modified asphalt.

Embodiment 3

[0028] The method for preparing the surface-modified hydrotalcite is the same as step 1 in Example 1. The coupling agent is a silane coupling agent, and the amount is 10% of the weight of the hydrotalcite.

[0029] 9 parts of melamine phosphate and 1.8 parts of surface-modified hydrotalcite were added to 100 parts of 160°C SBS modified asphalt, and ordinary stirring (450 rpm / min) was mixed for 1 hour to obtain flame retardant SBS modified asphalt.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
penetrationaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly flame retardant asphalt and a preparation method thereof. The flame retardant asphalt comprises, by mass, 100 parts of base asphalt, 2 to 15 parts of a fire retardant and 0.5 to 5 parts of a surface modified nano-material hydrotalcite. The preparation method comprises the steps of adding the fire retardant and the nano-material hydrotalcite into the base asphalt at a temperature of 120 to 180 DEG C and carrying out stirring for uniform mixing. According to the invention, the composition of asphalt has good flame retardant performance; additives used in the invention are environment-friendly, cost little and have good stability; a preparation process is simple.

Description

Technical field [0001] The invention relates to a flame-retardant asphalt composition and a preparation method thereof, in particular to an environmentally friendly flame-retardant asphalt composition and a preparation method thereof. Background technique [0002] With the development of highway construction in China, the number of highway tunnels is also increasing. The rigid cement concrete pavement commonly used in tunnels has gradually been replaced by a smooth, wear-resistant, and low-noise flexible asphalt concrete pavement. In the use of tunnel asphalt pavement, the fire safety of asphalt concrete pavement has attracted more and more attention. As asphalt is a flammable material, coupled with poor ventilation conditions in the tunnel, if a traffic accident causes an asphalt pavement to catch fire, the fire will develop rapidly and the evacuation will result in greater casualties, which will inevitably cause damage to the life and property of the country and people. Neces...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08K13/06C08K9/04C08K9/06C08K3/26C08K3/38C08K3/22C08K5/3492C08K3/02
Inventor 李明林郭皎河
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com