Agate-imitating spray coating material

A technology for spraying materials and materials, applied in polyester coatings, powder coatings, coatings, etc., can solve the problems of high cost and inability to be widely used, and achieve the effect of convenient operation, good promotion prospects and economic value, and exquisite coatings

Active Publication Date: 2012-07-11
海宁经开产业园区开发建设有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, agate is limited to making accessories and jewelry, which is expensive and cannot be widely used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A spraying material imitating agate is mainly made of the following raw materials in parts by weight:

[0054] Ortho-phthalic unsaturated polyester resin: 18;

[0055] Isophthalic unsaturated polyester resin: 10;

[0056] Benzoyl peroxide: 1;

[0057] Tributyl phosphate: 0.07;

[0058] Quartz sand: 25;

[0059] Aluminum powder: 14;

[0060] Tung oil: 0.2;

[0061] Calcium carbonate: 4.5;

[0062] Glycerol: 1.5;

[0063] Talc: 8.

[0064] The above raw materials are fully stirred and mixed evenly to make a powder coating.

[0065] The method of using the above-mentioned imitation agate material spraying material is to weigh 1 part by weight of the powder coating first, and then add 4 parts by weight of water to prepare; when preparing, first soak the powder coating with a part of the total water in cold water, and after moistening, put the remaining part Heat the cold water to boiling, rush into the wet powder coating, stir quickly to make the colloid in it fully ...

Embodiment 2

[0067] A spraying material imitating agate is mainly made of the following raw materials in parts by weight:

[0068] Ortho-phthalic unsaturated polyester resin: 22;

[0069] Isophthalic unsaturated polyester resin: 6;

[0070] Benzoyl peroxide: 4;

[0071] Tributyl phosphate: 0.03;

[0072] Quartz sand: 35;

[0073] Aluminum powder: 10;

[0074] Tung oil: 0.4;

[0075] Calcium carbonate: 3.0;

[0076] Glycerol: 3.0;

[0077] Talc: 4.

[0078] The above raw materials are fully stirred and mixed evenly to make a powder coating.

[0079] The method of using the above-mentioned imitation agate material spraying material is to weigh 1 part by weight of the powder coating first, and then add 4 parts by weight of water to prepare; when preparing, first soak the powder coating with a part of the total water in cold water, and after moistening, put the remaining part Heat the cold water to boiling, rush into the wet powder coating, stir quickly to make the colloid in it fully...

Embodiment 3

[0081] A spraying material imitating agate is mainly made of the following raw materials in parts by weight:

[0082] Ortho-phthalic unsaturated polyester resin: 20;

[0083] Isophthalic unsaturated polyester resin: 8;

[0084] Benzoyl peroxide: 2;

[0085] Tributyl phosphate: 0.05;

[0086] Quartz sand: 30;

[0087] Aluminum powder: 12;

[0088] Tung oil: 0.3;

[0089] Light calcium carbonate: 4.0;

[0090] Glycerol: 2.0;

[0091] Talc powder: 6;

[0092] Pigment: 0.1.

[0093] The above raw materials are fully stirred and mixed evenly to make a powder coating.

[0094] The method of using the above-mentioned imitation agate material spraying material is to weigh 1 part by weight of the powder coating first, and then add 4 parts by weight of water to prepare; when preparing, first soak the powder coating with a part of the total water in cold water, and after moistening, put the remaining part Heat the cold water to boiling, rush into the wet powder coating, stir qu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
freezing pointaaaaaaaaaa
boiling pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to a new spray coating material and a preparation method of the spray coating material. The spray coating material can endow a surface layer with agate luster and texture and is fully elegant when used on the surface layer to be spray-coated. The spray coating material can be used as an inner wall paint, or directly spray-coated on the outer layer of sanitary wares; the use method of the spray coating material is identical to that of common paint; and the spray coating material has the characteristics of delicate coating, convenience for operation, corrosion resistance and the like.

Description

technical field [0001] The invention relates to the field of architectural decoration, in particular to an imitation agate material spraying material and a preparation method thereof. Background technique [0002] Agate is a precious stone with smooth texture, hard material and good gloss. It has always been used as a high-end decoration. However, agate is limited to making accessories and jewelry, which is expensive and cannot be widely used. [0003] With the gradual improvement of people's living standards, people pay more and more attention to their home environment. All kinds of home decoration materials emerge in an endless stream. As far as the paint is concerned, the variety is very rich. There are many classification methods for coatings, and there are usually the following classification methods: [0004] (1) According to the form of coatings, it can be divided into water-based coatings, solvent-based coatings, powder coatings, high-solid content coatings, etc....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/06C09D7/12C09D5/00C09D5/03C09D7/14C09D7/80
Inventor 文杰
Owner 海宁经开产业园区开发建设有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap