An anodic oxidation and titanium alloy technology, applied in the direction of electrolytic coating, surface reaction electrolytic coating, coating, etc., can solve the problems of difficulty in continuous use, poor stability, etc., and achieve good stability, large carrying capacity, and low consumption. Effect

Active Publication Date: 2012-07-18
JIANGXI HONGDU AVIATION IND GRP
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this method is simple and easy to implement, due to the conditions of heating, strong alkali and impurity ions (iron, manganese, etc.) 2 o 2 Extremely poor stability, difficult to use continuously

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example

[0020] (1) 1L treatment liquid formula

[0021] Potassium hydroxide: 100g,

[0022] Sodium polyepoxysuccinate: 40g, Sodium oxalate: 40g, Sodium gluconate: 60g

[0023] Sodium polyaspartate (40wt%): 40ml

[0024] Sodium Erythorbate: 1g

[0025] water: balance

[0026] (2) Preparation of 1L treatment solution: first add some water and other substances in proportion and mix well, then add water to 1L.

[0027] (3) Processing and results of non-film white paper

[0028] Stir the above treatment solution, and heat it to 70°C, put in titanium and titanium alloy film-free white pieces (60×60×8mm TC4 titanium alloy samples), treat for 8 minutes, take it out and rinse with water, the surface color becomes uniform Blue-gray, anodized for 30 minutes, can form a uniform yellow oxide film, and the thickness of the film layer measured by a thickness gauge is 25.0±3μm. The film-free white parts not treated with this treatment solution were directly anodized for 30 minut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an efficient environment-friendly conditioning fluid for titanium and titanium alloy anodized repair members, which can remove oxidation films and can activate the surface of a workpiece so as to lead anodes of repair members or film-free workpieces to be oxidized and coated with films. The conditioning fluid contains 20-30wt% of strong base, 2-20wt% of antisludging agents, 2-20wt% of dispersing agents and 0.05-1wt% of activating agents, and the balance being water. Temperature of workpeices in the conditioning fluid ranges from 50 DEG C to 80 DEG C, and the processingtime is 1-30min. Stability of bath solution is good, bearing capacity is large, maintenance is easy, and no environment pollution can be caused. Mechanical property of the processed titanium and titanium alloy cannot be reduced, and quality of oxidation films can be ensured.

Description

technical field [0001] The invention relates to an efficient and environment-friendly treatment solution, which can remove the oxide film of titanium and titanium alloy anodic oxidation repair parts, activate the surface of the workpiece to re-anodize the film, and can also activate titanium and titanium alloy non-film white parts The surface is anodized on the film. Background technique [0002] Titanium and titanium alloys have small specific gravity, high specific strength, high temperature resistance, corrosion resistance and other excellent properties, and have been more and more widely used in military, aviation, aerospace, medical, chemical and other fields. The anodized titanium and titanium alloy parts, because of the oxide film formed on the surface, endow them with better corrosion resistance and scratch resistance. [0003] However, titanium and titanium alloys have high chemical activity, and it is easy to form a very thin and dense oxidation protective film in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/20C25D11/26
Inventor 超敏肖胜辉吴筱兰周雅吴光辉王春霞
Owner JIANGXI HONGDU AVIATION IND GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap