High-heat-resistance high-rigidity environmentally-friendly polystyrene resin composition and preparation method thereof

The technology of polystyrene resin and composition is applied in the field of polystyrene resin composition and preparation thereof, and can solve the problems of easy gasification and overflow of a stripping agent at a feeding port, no air stripping, difficult operation and the like, Achieve the effects of low production cost, improved heat resistance and rigidity, and simple preparation process

Active Publication Date: 2013-11-06
WUHAN JINFA TECH CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the stripping agent process can realize industrialized production, a large amount of stripping agent cannot be immersed in the raw material when the stripping agent is directly added to the raw material. On the one hand, it is difficult to add the screw extruder to operate. Screw extruder, due to the high temperature of the extruder, the stripping agent is easy to vaporize and overflow at the feeding port, and the effect of air lift cannot be achieved, so special injection nozzles with adjustable flow and ejection functions are required At the same time, it is necessary to add a pressurized mixing zone to improve the distribution of the stripping agent and limit the overflow of the stripping agent vapor from the target exhaust section, resulting in high cost and difficult operation of the above methods.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Prepare the stripping agent masterbatch according to the formula composition in Table 1, place the matrix used in the stripping agent masterbatch in a negative pressure (pressure <0.1MPa) environmental container, and then inject a certain amount of stripping agent into the negative pressure environmental container to obtain the steam Extraction agent masterbatch;

[0037] Various raw materials were weighed according to the weight percentage distribution ratio of the components shown in Table 2, and the rest were the same as the comparative examples.

Embodiment 2

[0039] Prepare the stripping agent masterbatch according to the formula composition in Table 1, weigh various raw materials according to the weight percentage distribution ratio of the components shown in Table 2, and the rest are the same as the comparative examples.

Embodiment 3

[0041] Prepare the stripping agent masterbatch according to the formula composition in Table 1, weigh various raw materials according to the weight percentage distribution ratio of the components shown in Table 2, and the rest are the same as the comparative examples.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
flash pointaaaaaaaaaa
flexural modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-heat-resistance high-rigidity environmentally-friendly polystyrene resin composition and a preparation method thereof. The polystyrene resin composition contains the following components in percentage by weight: 59-99 percent of polystyrene resin, 0.5-30 percent of SMA (Styrene-Maleic Anhydride) resin, 0-10 percent of stripping agent master batch and 0.01-1 percent of antioxidant, wherein the stripping agent master batch consists of a matrix and a stripping agent. The preparation method has the advantages of simple production process, reduced production cost and capabilities of effectively improving heat resistance and rigidity of polystyrene resin without reducing mechanical property thereof and meanwhile reducing smell and VOC (Volatile Organic Compound) content of the polystyrene resin; and the prepared polystyrene resin composition can be used in the fields of materials with strict requirements on heat resistance and environmental friendliness in packaging materials, daily articles, household appliances, OA (Office Automation), toys, electronic parts and components and equipment, building materials and automobile materials.

Description

technical field [0001] The invention relates to a polystyrene resin composition and a preparation method thereof. Background technique [0002] As one of the five general-purpose plastics, polystyrene resin has the advantages of excellent formability, moderate performance, electrical insulation, low moisture absorption, easy dyeing, and low price. It is widely used in packaging, electronics, automobiles, home appliances, instruments, daily necessities, Toys, construction and other industries. However, polystyrene resin has poor heat resistance and rigidity, and its heat distortion temperature (HDT) is around 80°C (ASTM D648, load 1.82MPa), which limits the use of polystyrene resin in high heat-resistant applications, such as microwave Food packaging field, hot drink packaging field and structural components of some electrical products, etc. At the same time, with the increasing size, thinner wall and lightweight development trend of electronic and electrical product casing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L25/06C08L51/04C08L53/02C08L35/06C08L97/02C08L3/02C08L23/12C08L67/00C08K3/34C08K3/22C08J3/22B29C47/92B29C48/92
CPCB29C48/40B29C48/92B29C2948/92514B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 付锦锋王林蔡彤旻刘奇祥郭少华陈日平胡志华
Owner WUHAN JINFA TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products