Environment-friendly water-based bi-component polyurethane steel-structure anti-corrosion finish paint and preparation method

A two-component polyurethane, environmentally friendly technology, applied in polyurea/polyurethane coatings, anti-corrosion coatings, coatings, etc., can solve the problems of poor water resistance, low hardness and gloss, and achieve improved safety, excellent adhesion, Strong acid and alkali resistance

Inactive Publication Date: 2012-07-25
SHANGHAI MAMPLE NEW MATERIAL
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide an environment-friendly water-based two-component polyurethane steel structure anti-corrosion finish paint and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0039] Embodiment 1:

[0040] The following raw materials were weighed by weight: 58 parts by weight of hydroxyl-containing aqueous resin emulsion, 33 parts by weight of titanium dioxide, 2 parts by weight of defoamer, 1 part by weight of dispersant, and 10 parts by weight of water. Titanium dioxide adopts R-930, defoamer adopts BYK-028, and dispersant adopts BYK-190.

[0041] Under stirring at 1000-1500r / min, titanium dioxide, dispersant and water were mixed and added to 58 parts by weight of hydroxyl-containing aqueous resin emulsion in turn, and 2 parts by weight of defoaming agent were added to disperse the pigment below 20 microns, and then in 1 part by weight of wetting agent was added at a stirring speed of 300r / min-500r / min, and the wetting agent was BYK-345. Stir well, and obtain component A after filtration.

[0042] Add 80 parts by weight of curing agent (the weight ratio of self-emulsifying polyisocyanate and hydrophobic polyisocyanate is 4:1) into 20 parts by we...

Example Embodiment

[0058] Example 2:

[0059] The following raw materials were weighed by weight: 58 parts by weight of hydroxyl-containing aqueous resin emulsion, 33 parts by weight of titanium dioxide, 3 parts by weight of carbon black, 1 part by weight of defoamer, 0.5 part by weight of dispersant, and 17 parts by weight of water. Titanium dioxide adopts R-930, defoamer adopts BYK-028, and dispersant adopts BYK-190.

[0060] Under stirring at 1000-1500r / min, titanium dioxide, carbon black, dispersant and water were mixed and added to 58 parts by weight of hydroxyl-containing aqueous resin emulsion in turn, and 1 part by weight of defoamer was added to disperse the pigment below 20 microns , and then add 0.5 parts by weight of wetting agent at a stirring speed of 300r / min-500r / min, and the wetting agent adopts BYK-345. Stir well, and obtain component A after filtration.

[0061] Add 82 parts by weight of curing agent (the weight ratio of self-emulsifying polyisocyanate and hydrophobic polyis...

Example Embodiment

[0077] Example 3:

[0078] Weigh the following raw materials by weight: 55 parts by weight of hydroxyl-containing aqueous resin emulsion, 27 parts by weight of titanium dioxide, 2 parts by weight of plain blue, 1 part by weight of defoamer, 1 part by weight of dispersant, and 10 parts by weight of water. Titanium dioxide adopts R-930, defoamer adopts BYK-028, and dispersant adopts BYK-190.

[0079] Under stirring at 1000-1500r / min, mix titanium dioxide, plain blue, dispersant and water into 55 parts by weight of hydroxyl-containing aqueous resin emulsion in turn, and add 1 part by weight of defoamer to disperse the pigment to below 20 microns , and then add 0.5 parts by weight of wetting agent at a stirring speed of 300r / min-500r / min, and the wetting agent adopts BYK-345. Stir well, and obtain component A after filtration.

[0080] Add 80 parts by weight of curing agent (the weight ratio of self-emulsifying polyisocyanate and hydrophobic polyisocyanate is 4:1) into 20 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Impact resistanceaaaaaaaaaa
Login to view more

Abstract

The invention provides environment-friendly water-based bi-component polyurethane steel-structure anti-corrosion finish paint and a preparation method. The anti-corrosion finish paint comprises a component A and a component B, wherein the component A comprises, by weight, 55-58 parts of hydroxyl water-based resin emulsion, 27-33 parts of titanium oxide, 0-2 parts of Prussian blue, 0-3 parts of carbon black, 1-2 parts of defoamer, 0.5-1 part of dispersing agent, 0.5-1 part of wetting agent and 10-17 parts of water; the component B comprises, by weight, 80-82 parts of curing agent and 18-20 parts of cosolvent; and the two components are mixed in the weight proportion of 4.4:1. The anti-corrosion finish paint is highly waterproof, high in hardness and glossiness and full in color, has the advantages of good leveling property, high covering power, firmness in adhesion, acid-resistant and alkali-resistant coatings, safety in construction and the like, and can be widely used for steel structures of all walks of life, such as mechanical equipment, rolling stock, constructions such as departure halls, stadiums, railway station rooms, convention centers, commercial buildings, bridges and the like of steel structures, thereby having a huge market prospect.

Description

technical field [0001] The invention belongs to the technical field of industrial anticorrosion coatings, in particular to an environment-friendly water-based two-component polyurethane steel structure anticorrosion topcoat and a preparation method thereof. Background technique [0002] With the increasingly stringent requirements for environmental protection, the research on water-based coatings with low or zero VOC and low or zero HAPs (hazardous air pollution) has become the focus and an important development direction of coatings. [0003] At present, in the supporting system of anti-corrosion coatings for steel structures in China, organic products are basically used for the top coat. The volatilization of organic solvents can easily lead to construction safety problems, and the emission of VOC affects the living environment of human beings. With the strengthening of the awareness of global environmental protection, people vigorously develop water-based coatings to repl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/14C09D5/08C09D7/12
Inventor 王振华陆为平徐英
Owner SHANGHAI MAMPLE NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap