Reactive dyeing method for pearl viscose fibers

A viscose fiber and reactive dye technology, applied in the field of dyeing, can solve the problems of low color fastness, difficult dyeing, unsatisfactory dyeing method of pearl viscose fiber, etc., achieve easy dyeing, improve dyeing rate and color. The effect of fastness

Active Publication Date: 2013-07-24
TAICANG RONGWEN SYNTHETIC FIBER
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the dyeing method about this pearl viscose fiber in the prior art is not ideal, mainly is that dyeing difficulty is big, and the color fastness after dyeing is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Add 10 grams of reactive red, 10 grams of sodium carbonate, and 10 grams of sodium sulfate to 1 liter of water to form a dye solution. After the dye solution is heated to 60 degrees, pearl fiber fabrics are put into the dye solution. The bath ratio is 25:1. When the pH is 6, continue to heat up the dye liquor at a rate of 2 degrees per minute. After the dye liquor is heated to 90 degrees, keep the temperature for 100 minutes, then take out the fabric and wash it until neutral, then dry it.

Embodiment 2

[0021] Add 15 grams of reactive red, 15 grams of sodium carbonate, and 20 grams of sodium sulfate to 1 liter of water to form a dye solution. After the dye solution is heated to 55 degrees, pearl fiber fabrics are put into the dye solution. The bath ratio is 30:1. When the pH is 7, continue to heat up the dye liquor at a rate of 2 degrees per minute. After the dye liquor is heated to 100 degrees, keep the temperature for 80 minutes, then take out the fabric, wash it until neutral, and dry it.

Embodiment 3

[0023] Add 25 grams of reactive blue, 20 grams of sodium carbonate, and 30 grams of sodium sulfate to 1 liter of water to form a dye solution. After the dye solution is heated to 50 degrees, pearl fiber fabrics are put into the dye solution. The bath ratio is 28:1. When the pH is 7, continue to heat up the dye liquor at a rate of 2 degrees per minute. After the dye liquor is heated to 70 degrees, keep the temperature for 90 minutes, then take out the fabric and wash it until neutral, then dry it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a reactive dyeing method for pearl viscose fibers. The reactive dyeing method mainly comprises the following steps of: dyeing, wherein reactive dyes, sodium carbonate and sodium sulfate are added in water to form dye liquor, pearl viscose fiber fabric is put into the dye liquor after the dye liquor is heated to be at a temperature ranging from 50 DEG C to 60 DEG C, the liquor ratio equals to (25-30):1, the pH of the dye liquor equals to 6 to 7.5, and then the dye liquor is heated continually to reach a temperature ranging from 70 DEG C to 100 DEG C and is kept at the temperature for 80 minutes to 100 minutes, thereby dyeing the fabric; washing the dyed fabric till the fabric is neutral; and drying the fabric. According to the dyeing method, the composition and component proportion of the dye liquor are optimized, the parameters of the dyeing process are adjusted, the dyeing is easy, and the dye-uptake and color fastness of the pearl viscose fibers are improved.

Description

technical field [0001] The invention relates to a dyeing method, in particular to a pearl viscose fiber reactive dye dyeing method. Background technique [0002] Pearl fiber is a fiber made by blending and spinning nano-pearl particles and viscose. It is a new type of functional fiber. Nano-pearl particles are evenly distributed inside and outside the fiber. Because pearls contain a variety of amino acids needed by the human body And trace elements, long-term contact with the skin, has the effects of nourishing skin and skin care, anti-ultraviolet rays, and emitting far-infrared rays. But the dyeing method about this pearl viscose fiber in the prior art is not ideal, mainly is that it is difficult to dye, and the color fastness after dyeing is low. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies in the prior art and provide a pearl viscose fiber reactive dyeing method that is easy to dye and has high color fastness a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06P3/66
Inventor 全潇
Owner TAICANG RONGWEN SYNTHETIC FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com