A kind of water-based emulsion antirust liquid and preparation method thereof

An emulsion type, anti-rust liquid technology, applied in the field of anti-rust, can solve the problems of carcinogenicity, easy oxidation and discoloration, and inability to prevent long-term rust, etc., and achieve the effect of less harmful substances, not easy to stain, and not easy to fall off

Active Publication Date: 2016-05-25
盐城新汇村镇建设发展有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary anti-rust water contains a large amount of sodium nitrite, which is carcinogenic and is not conducive to environmental protection and human health. However, the use of humectants to prolong the life of anti-rust water brings the disadvantages of sticking hands and dust, and cannot prevent rust for a long time; Although the general dura-film anti-rust oil is suitable for long-term anti-rust, and the film is transparent and beautiful, there are few types of colorless and transparent resins, which are unstable and easy to oxidize and change color. They also need organic solvents to dissolve, which brings the danger of flammability and explosion. It is not conducive to environmental protection and health; the general anti-rust oil uses mineral oil, which is difficult to degrade, and it will also cause the problem of difficult degreasing when used for short-term anti-rust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] A water-based emulsion type antirust liquid, made of the following raw materials in parts by weight (kg): urethane acrylate 13, dodecenyl succinic acid 4.5, monoethanolamine 1.5, sodium molybdate 1.2, octylphenol polyoxygen Vinyl ether 2, hydroquinone 1.5, ditetradecyl alcohol 3.5, disodium EDTA 1.5, additive 4.5, water 300. The auxiliary agent is made of the following raw materials in parts by weight (kg): 5 alkylphenol polyoxyethylene ethers, 0.1 nanometer titanium dioxide, catechol 1, morpholine 2, gum arabic 2, sodium silicate 1, urea 3 1. Ammonium persulfate 1. Water 20. The preparation method is to dissolve ammonium persulfate in water, then add other remaining materials, stir for 10-15 minutes, heat to 70-80°C, and stir for 1-2 hours to obtain the product.

[0010] The preparation method of the water-based emulsion type antirust liquid comprises the following steps: heating water to 46°C, adding octylphenol polyoxyethylene ether; continuing to heat to 87°C, addin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based emulsion-type antirust liquid and a preparation method thereof. The water-based emulsion-type antirust liquid is prepared from 12-15 parts by weight of urethane acrylate, 4-5 parts by weight of dodecenylsuccinic acid, 1-2 parts by weight of monoethanolamine, 0.9-1.4 parts by weight of sodium molybdate, 1.5-3 parts by weight of polyoxyethylene octylphenol ether, 1-2 parts by weight of hydroquinone, 3-4 parts by weight of ditetradecane alcohol ester, 1-2 parts by weight of ethylenediaminetetraacetic acid disodium salt, 4-5 parts by weight of an assistant and 300 parts by weight of water. The polymer monomer forms a stable emulsion under the action of a chelating agent and a nonionic surfactant and the emulsion forms a film on the metal surface, does not fall off easily, resists oxidation, is not polluted easily and can be cleaned easily. The water-based emulsion-type antirust liquid contains less harmful substances, has a low cost and is suitable for long / short-period rust prevention of metal products and machinery parts.

Description

technical field [0001] The invention relates to the field of antirust technology, in particular to a water-based emulsion type antirust liquid and a preparation method thereof. Background technique [0002] Rust prevention on metal surfaces is an important subject in industrial production. Traditional antirust liquids and antirust oils have both advantages and disadvantages. Ordinary anti-rust water contains a large amount of sodium nitrite, which is carcinogenic and is not conducive to environmental protection and human health. However, the use of humectants to prolong the life of anti-rust water brings the disadvantages of sticking hands and dust, and cannot prevent rust for a long time; Although the general dura-film anti-rust oil is suitable for long-term anti-rust, and the film is transparent and beautiful, there are few types of colorless and transparent resins, which are unstable and easy to oxidize and change color. They also need organic solvents to dissolve, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23F11/04
Inventor 李国友
Owner 盐城新汇村镇建设发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products