Size preparation method, size and paper made of size

A slurry and high-consistency refining technology, used in pulp beating/refining methods, papermaking, textiles and papermaking, etc., can solve the problem of fiber cutting, unfavorable to improve pulping yield, pulp strength, and fiber bundles are difficult to be dissociated. Brooming and other problems, to achieve the effect of improving strength, improving the rate of splitting and brooming, and fine surface

Active Publication Date: 2012-10-10
GOLD EAST PAPER JIANGSU
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the power of the refiner is too high, the tooth disc of the refiner rotates too fast, and the fibers are easily cut off, which makes it difficult for the fiber bundles to be dissociated and scorched, which is not conducive to improving the pulping yield and the strength of the pulp

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Size preparation method, size and paper made of size
  • Size preparation method, size and paper made of size
  • Size preparation method, size and paper made of size

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] See figure 1 , a preferred embodiment of the present invention provides a kind of preparation method of slurry, mainly comprises the following steps:

[0020] S101: Prepare raw pulp, the specific method is as follows: use at least one of wood chips such as hardwood chips and coniferous wood chips as raw materials, and perform conventional washing, steaming, crushing, tearing and other treatments on the raw materials to obtain Original slurry. The raw stock mainly contains stock fibers 10 and water. The mass percentage of the original slurry is 25%-50%.

[0021] S102: Provide hard grinding aid 30 (see figure 2 ). The mass of the hard grinding aid 30 is 3%-20% of the absolute dry mass of the original slurry, preferably 6%-10%. The hard grinding aid 30 can be any one or a mixture of precipitated calcium carbonate (PCC), ground calcium carbonate (GCC), talc (Talc) and titanium dioxide. The particle size of the above-mentioned hard grinding aid 30 is 0.2-50 μm. Among...

Embodiment 1

[0039] The original slurry was prepared, the raw material of the original slurry was poplar wood chips, and the mass percentage of the original slurry was 45%. A hard grinding aid 30 is provided, and the hard grinding aid 30 is grade 65 GCC. Add 8% 65-grade GCC of the dry weight of the original slurry to the original slurry and mix evenly to obtain a mixed slurry. The mixed pulp is subjected to high-consistency refining treatment. The power of the refiner is 18MW. After the high-consistency refining treatment, the mixed pulp is bleached, low-consistency refined, washed, screened, and slag-removed to obtain the required pulp. And before the screening and slag removal treatment, the fiber bundle content and the quality of the slurry in the slurry were tested by sampling.

Embodiment 2

[0047] The steps and process parameters of Example 1 are basically the same, the difference is that in this embodiment, the filler grade PCC with an absolute dry mass of 10% of the original slurry is added to the original slurry. During the high-consistency refining process, the refiner The power is 25MW.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a size preparation method. The size preparation method includes the following steps of providing raw size, subjecting the raw size to high-consistency size treatment, adding hard grinding aid by weight of 3-20% of that of completely dried raw size, wherein the grain diameter of the hard grinding aid ranges from 0.2-50 micrometers. The invention further provides size made by the size preparation method and paper made of the size.

Description

technical field [0001] The invention relates to a method for preparing papermaking slurry, a papermaking slurry and paper prepared therefrom. Background technique [0002] The traditional Alkaline Peroxide Mechanical Pulp (APMP) pulping process mainly dissociates the fibers in the pulp through the mechanical action of the refiner, and usually by increasing the refiner The power to increase the fibrous rate of fibres. However, when the power of the refiner is too high, the tooth disc of the refiner rotates too fast, and the fibers are easily cut off, which makes it difficult for the fiber bundles to be dissociated and scorched, which is not conducive to improving the pulping yield and the strength of the pulp. Especially when a variety of wood chips of different materials are mixed and pulped, the above-mentioned problems are particularly prominent. Contents of the invention [0003] In view of this, a preparation method of slurry is provided to improve fiber scuffing rat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21D1/20
Inventor 韦丹王仁荣张明
Owner GOLD EAST PAPER JIANGSU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap