Method for casting corrosion-resisting butterfly valve body

A butterfly valve, corrosion-resistant technology, applied in the field of valve casting, can solve the problems of short service life, low pass rate, complex process, etc., and achieve the effect of long service life, high pass rate and simple process

Inactive Publication Date: 2012-10-24
ANHUI FANCHANG COUNTY WANNAN VALVE CASTING
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Butterfly valve, also known as flap valve, is a regulating valve with simple structure. It can also be used for switch control of medium in low-pressure pipelines. Flow function; butterfly valve has the characteristics of simple structure, small size, light weight, low material consumption, small installation size, fast switching, small driving torque, etc. It is used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: the casting method of corrosion-resistant butterfly valve valve body, comprises the following steps:

[0013] (1) According to the weight ratio of raw materials, pig iron is 25-32%, scrap steel is 25-32%, recycled material is 15-25%, rare earth ferroalloy is 5-8%, ferrosilicon is 1.7-2.0%, recarburizer is 0.2-0.24% and Ferromanganese alloy 5-10% Weigh raw materials, the total of the upper components is 100%, and control its chemical composition C: 2.83-3.2%, Si: 1.0-1.3%, Mn: 0.6-1.0%, P: 0.8-1.0%, S : 0.03-0.09%, Si 8-15.5%, Cr 0.27-0.33%, Sn 0.01-0.02%, Cu 0.8-1.2%;

[0014] (2) Heat the above-mentioned raw materials to 1400-1600°C, melt them into molten metal, detect the content of chemical components, then add corresponding deficient elemental metals into the above-mentioned molten metal, mix them evenly, and form a pouring liquid;

[0015] (3) Pour the pouring liquid into the sand mold through the gate, cool and solidify, so that the temperature of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for casting a corrosion-resisting butterfly valve body. Firstly, raw materials including pig iron 25-32%, steel scrap 25-32%, foundry returns 15-25%, rare earth iron alloy 5-8%, silicon iron 1.7-2.0%, carburant 0.2-0.24% and ferromanganese 5-10% are weighed by weigh ratio, wherein the sum of ingredients is 100%; chemical components including C2.83-3.2%, Si 1.0-1.3%, Mn 0.6-1.0%, P 0.8-1.0%, S 0.03-0.09%, Si 8-15.5%, Cr 0.27-0.33%, Sn 0.01-0.02% and Cu 0.8-1.2% are controlled; the temperature is heated to be 1400-1600 DEG C to melt the ingredients into molten metal, the content of the chemical components is detected, and then corresponding lacking metal elements are added into the molten metal to be mixed evenly to form pouring liquid; and pouring and cooling solidification are performed, and steam treatment is performed to a taken-out coagulum to obtain the corrosion-resisting butterfly valve body. The raw materials are reasonable in formula, the process is simple, produced corrosion-resisting butterfly valve body is good in performance, long in service life and high in qualified rate, the product quality is improved greatly, and the method is suitable for being popularized widely.

Description

technical field [0001] The invention relates to a casting method for a corrosion-resistant butterfly valve body, belonging to the technical field of valve casting. Background technique [0002] Butterfly valve, also known as flip valve, is a regulating valve with simple structure. It can also be used for switch control of low-pressure pipeline medium. Low consumption, small installation size, rapid switching, small driving torque, etc., are used to cut off, connect and adjust the medium in the pipeline, and have good fluid control characteristics and closing and sealing performance. At present, the corrosion-resistant butterfly valve body The casting process mainly adopts conventional casting, which is often accompanied by the disadvantages of complex process, low pass rate and short service life of the product. Contents of the invention [0003] The object of the present invention is to provide a casting method for a corrosion-resistant butterfly valve body. The composi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22D3/00C22C37/10
Inventor 沈升好
Owner ANHUI FANCHANG COUNTY WANNAN VALVE CASTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap