A kind of halogen-free environment-friendly power cable material for wind power generation and preparation method thereof

An environment-friendly, cable material technology, applied in the field of cable materials, can solve problems such as hindering safe evacuation and fire fighting work, loss of life and property, etc., and achieves the effects of small expansion and deformation, good wear resistance and excellent electrical properties

Active Publication Date: 2016-08-03
苏州益普敦新材料科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the cable burns, it releases a large amount of smoke and toxic and corrosive gases, which are dangerous factors in the fire, which hinders people's safe evacuation and fire fighting work, and causes serious losses to life and property.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: Halogen-free environment-friendly power cable material for wind power generation, the parts by weight of the raw materials are: polyolefin elastomer POE8450 / U.S. DuPont 90-110, PVC resin powder 50-60, wollastonite powder 40-60, nano Attapulgite 60-80, EPDM rubber 50-80, nitrile rubber 40-50, nano clay 20-30, aluminum hydroxide 30-40, precipitated white carbon black 1-4, light calcium carbonate 60 -80, insoluble sulfur 3-5, triallyl isocyanurate 1-4, antioxidant TPPD3-5, dicumyl peroxide DCP4-6, dibasic lead phosphite 3-8, anti-oxidant Oxygen agent 10105-7, monoglyceride stearate 2-5 and antimony trioxide 50-70.

[0011] The preparation method of the halogen-free environment-friendly power cable material for wind power generation comprises the following steps: weighing each raw material according to the weight of the constituent raw materials, and then banburying at a temperature of 100-120° C. for 5-7 minutes, and then banburying The finished product is o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
breakdown field strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a halogen-free environmentally-friendly power cable material for wind power generation, and its preparation method. The cable material comprises the following raw materials, by weight, 90-110 parts of a polyolefin elastomer (POE) 8450 / American DuPont, 50-60 parts of PVC resin powder, 40-60 parts of wollastonite powder, 60-80 parts of nanometer attapulgite, 50-80 parts of ethylene-propylene-diene terpolymer rubber, 40-50 parts of nitrile butadiene rubber, 20-30 parts of nanometer pottery clay, 30-40 parts of aluminum hydroxide, 1-4 parts of precipitated white carbon black, 60-80 parts of light calcium carbonate, 3-5 parts of insoluble sulfur, 1-4 parts of triallyl isocyanurate, 3-5 parts of an antiager TPPD, 4-6 parts of dicumyl peroxide (DCP), 3-8 parts of dibasic lead phosphite, 5-7 parts of an antioxidant 1010, 2-5 parts of monoglycerin stearate and 50-70 parts of antimony trioxide. The cable material has the advantages of simple preparation method, excellent electrical property, good heat, ageing and wear resistances, small swelling deformation at a high temperature, secondary vulcanizing processing benefiting, low smoke and fire resistance, and environmental protection and safety.

Description

technical field [0001] The invention relates to a halogen-free environment-friendly power cable material for wind power generation and a preparation method thereof, belonging to the technical field of cable materials. Background technique [0002] With the rapid development of the economy, wires and cables are widely used in various industries and fields. With the frequent occurrence of electrical fire accidents, the flame retardant problem of wires and cables has gradually attracted the attention of countries all over the world. When the cable burns, it releases a large amount of smoke and toxic and corrosive gas, which is a risk factor in a fire. It hinders people's safe evacuation and fire fighting work during a fire, causing serious loss of life and property. At the same time, with the development of the communication industry, the automobile industry and the computer industry, especially in many occasions such as aviation wires, automobile wires, high-temperature instr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/00C08L27/06C08L23/16C08L9/02C08K13/02C08K3/34C08K3/22C08K3/36C08K3/26C08K5/14C08K3/06
Inventor 魏善恒李小康陶天宝陈国林王敏
Owner 苏州益普敦新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com