Dipping liquid used for dipping glass fiber twistless roving at external layer of steel rail polishing grinding wheel, and its preparation method
A technology of glass fiber and roving, which is applied in grinding/polishing equipment, grinding devices, manufacturing tools, etc. It can solve the problems of grinding wheel breakage, low dipping amount, shedding, etc., and achieve enhanced strength, good wettability, The effect of prolonging the service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0015] Example 1
[0016] A method for preparing an immersion liquid for dipping an outer layer glass fiber roving of a rail grinding wheel. The preparation steps are as follows: 40 parts by mass of PF2127 liquid phenolic resin, 19.5 parts by mass of PF2123 novolak resin powder , 40 parts by mass of industrial alcohol (the mass percentage concentration is 75%) and 0.4 part by mass of γ-ethylenediaminopropyltrimethoxysilane were stirred in a stirrer for 2.5 hours at room temperature, and the stirring speed was 200 rev / min, the impregnating liquid can be prepared.
Example Embodiment
[0017] Example 2
[0018] A method for preparing an immersion liquid for dipping an outer layer glass fiber roving of a rail grinding wheel, the preparation steps are as follows: 38 parts by mass of PF2127 liquid phenolic resin, 22 parts by mass of PF2123 novolak resin powder , 45 parts by mass of industrial alcohol (the mass percentage concentration is 75%) and 0.3 part by mass of γ-ethylenediaminopropyltrimethoxysilane were stirred in a stirrer for 2 hours at room temperature, and the stirring speed was 170 rev / min, the impregnating liquid can be prepared.
Example Embodiment
[0019] Example 3
[0020] A method for preparing an immersion liquid for dipping an outer layer glass fiber roving of a steel rail grinding wheel. , 35 parts by mass of industrial alcohol (the mass percentage concentration is 75%) and 0.5 part by mass of γ-ethylenediaminopropyltrimethoxysilane were stirred in a stirrer for 3 hours at room temperature, and the stirring speed was 220 rev / min, the impregnating liquid can be prepared.
[0021] The technical performance index that the dipping solution prepared by the method of the present invention can reach through the test is as follows:
[0022] The glass fiber roving is passed through the impregnating liquid prepared by the present invention at a speed of 0.5-0.8 m / s. The time for the impregnation liquid to penetrate into the roving does not exceed 2 seconds, and the glass fiber roving is completely wetted. Untwisted roving with full immersion liquid is evenly wound on the outer circumference of the grinding wheel body with a...
PUM
Property | Measurement | Unit |
---|---|---|
Peel strength | aaaaa | aaaaa |
Peel strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap