Preparation method of optical amplitude limiting C60/POSS (Polyhedral Oligomeric Silsesquioxane) composite film

A technology of optical limiting and composite film, which is applied in the field of preparation of composite film, can solve the problems of low solubility, reduce optical nonlinearity, etc., and achieve the effects of high transparency, good film formation and high thermal stability

Inactive Publication Date: 2012-11-14
HARBIN INST OF TECH
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But its low solubility will reduce the optical nonlinearity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of optical amplitude limiting C60/POSS (Polyhedral Oligomeric Silsesquioxane) composite film
  • Preparation method of optical amplitude limiting C60/POSS (Polyhedral Oligomeric Silsesquioxane) composite film
  • Preparation method of optical amplitude limiting C60/POSS (Polyhedral Oligomeric Silsesquioxane) composite film

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0033] Specific implementation mode 1: Optical clipping C in this implementation mode 60 The preparation method of / POSS composite film is carried out according to the following steps:

[0034] 1. Preparation of POSS sol: Mix formic acid solution, ethanol and silane coupling agent according to the mass ratio of 1:3:3, and then react in a water bath at 35°C for one week to prepare POSS sol;

[0035] Second, the synthesis of intermediates:

[0036] Will C 60 Dissolved in an organic solvent to obtain a concentration of 1g / L of C 60 solution, the C 60 The solution is mixed with the POSS sol according to the ratio of 1ml:1g, and then the mixture is heated in a water bath at 80°C for 0.5-1 hour to obtain the intermediate;

[0037] 3. Compounding of intermediate and matrix:

[0038] According to the mass ratio of intermediate, POSS sol and matrix of 1:4:3, mix the intermediate, POSS sol and matrix evenly to obtain a mixed solution, and then apply the mixed solution evenly on the ...

specific Embodiment approach 2

[0045] Embodiment 2: This embodiment differs from Embodiment 1 in that in step 2, the mixture is heated in a water bath at 80° C. for 0.8 hours. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0046] Embodiment 3: This embodiment differs from Embodiment 1 in that in step 3, the glass is dried in an oven at 80° C. for 7 hours. Others are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of an optical amplitude limiting C60 / POSS (Polyhedral Oligomeric Silsesquioxane) composite film and relates to a preparation method of a composite film. The invention aims to solve the technical problems that C60 taken as an optical amplitude limiting material is lower in dissolubility, and the optically nonlinear properties are reduced. The preparation method comprises the following steps of: 1, preparing POSS sol; 2, synthesizing a midbody; and 3, compounding the midbody and a substrate. The preparation method has the beneficial effects that the C60 is connected with POSS together by utilizing a group containing an amino group to realize the property superposition of the C60 and the POSS; and a synthesized product has good film forming property and high transparency and can be used as a coating film on an optical device.

Description

technical field [0001] The invention relates to a preparation method of a composite membrane. Background technique [0002] Laser has excellent properties such as high monochromaticity, high directivity and high coherence, so it has a wide range of applications in communication, ranging, guidance, radar, etc. Laser weapons are a new milestone after cold weapons, firearms, and nuclear weapons. Laser jamming and blinding weapons have been applied in Western countries, and they will surely shine in the 21st century. This type of weapon mainly destroys ground military installations and blinds military personnel, achieving the purpose of making the opponent lose combat effectiveness. With the rapid development of modern laser technology, laser protection has been paid more and more attention. Various optical limiting materials containing large π conjugated systems, such as fullerenes, phthalocyanines, porphyrins, stilbene derivatives, organometallic compounds, etc. It has becom...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J5/18C08L33/12C08K9/06C08K3/04C08K5/549C08F120/14
Inventor 张兴文张欢喜吴振维杨旭可卢艳
Owner HARBIN INST OF TECH