Composite board and manufacturing method thereof
A manufacturing method and composite board technology, applied in chemical instruments and methods, building structures, wood layered products, etc., can solve the problems of easy combustion, easy corrosion, poor waterproof performance, etc., and achieve light weight and good flame retardancy , The effect of simple manufacturing method
Active Publication Date: 2015-04-29
FOSHAN NANHAI RACER NEW MATERIALS RES INST
View PDF6 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0006] The invention proposes a composite board and its manufacturing method, which solves the problems of poor waterproof performance, easy combustion, poor wear resistance, and easy corrosion in the prior art. It has flame retardancy, waterproof, anticorrosion, high wear resistance, and light weight. , good flame retardant performance, non-toxic and non-polluting advantages, can be mass-produced in batches
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0033] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.
[0034] refer to figure 1 , a composite board 1 comprising a substrate layer 2, a wood veneer layer 3, a panel layer 4 and a surface layer 5; the substrate layer 2 is a magnesium oxide board, and the substrate layer 2 includes a first surface 21 and the second surface 22, the first surface 21 and the second surface 22 are coated with adhesive (not shown); the wood veneer layer 3 includes the first wood veneer layer 31 and the second The wood veneer layer 32, t...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
Login to View More
Abstract
The invention provides a composite board which comprises a base material layer, a wood veneer layer, a panel layer and a surface layer, wherein the base material layer is a magnesium oxide board and comprises a first surface and a second surface; adhesives are coated on the first surface and the second surface; the wood veneer layer comprises a first wood veneer layer and a second wood veneer layer; the first wood veneer layer is adhered to the first surface; the second wood veneer layer is adhered to the second surface; the panel layer comprises a first panel layer and a second panel layer; the first panel layer is adhered to the first wood veneer layer; the second panel layer is adhered to the second wood veneer layer; and the surface layer is adhered to the panel layer. The composite board has the advantages of high fire resistance, high water resistance, high corrosion resistance, high wear resistance, light weight, high flame retardant property, harmlessness and no pollution, and large-scale mass production can be formed.
Description
technical field [0001] The invention relates to the field of architectural decoration, in particular to a composite board, in particular to a flame-retardant and wear-resistant composite board and a manufacturing method thereof. Background technique [0002] The existing indoor composite boards are divided into solid wood boards, composite boards, reinforced boards, etc., and the production technology has become increasingly mature. With the continuous improvement of people's lives, people's requirements for quality of life are also getting higher and higher. Boards are also increasingly favored by people, but they all have defects during use, and the defects are as follows: [0003] Solid wood board: During the processing from log to finished product, the overall structural form of natural wood and its natural plant biological activity are retained. It is precisely because of the natural active characteristics of wood that this kind of solid wood composite board is afraid ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): B32B21/04E04F13/075B32B9/04
Inventor 陈志明
Owner FOSHAN NANHAI RACER NEW MATERIALS RES INST