High-performance water-soluble acrylic resin and preparation method thereof

A water-soluble acrylic, high-performance technology, applied in the direction of coating, can solve the problems of alkali resistance, low boiling water resistance, difficult to meet requirements, etc., and achieve the effect of good gloss

Active Publication Date: 2012-12-26
江阴恒兴涂料有限公司
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the various indicators of conventional water-soluble acrylic resins can only be met in normal conditions. Once encountering harsh working conditions, conventional water-soluble acrylic resins have low alkali resistance and boiling water resistance, which is difficult to meet the requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0021] The preparation method of this high-performance water-soluble acrylic resin is as follows:

[0022] Step 1. Configure the mixed solution

[0023] Hydroxyethyl methacrylate, hydroxyethyl acrylate, methyl methacrylate, isooctyl methacrylate, n-butyl acrylate, ethyl acrylate, acrylic acid, glycidyl tert-carbonate, hexafluorobutyl methacrylate And the initiators accounting for 60%-70% of the total amount of initiators are mixed to form a mixed solution.

[0024] Step 2. Water-soluble acrylic resin molding

[0025] In the reaction vessel, use isopropanol and deionized water accounting for 5-15% of the total amount of deionized water as the base material to raise the temperature to 85-90 °C, and add the mixed solution prepared in step 1 to the reaction vessel dropwise, and the dropping time is 150-200min, then the reaction vessel is kept warm for 150-280min, then the remaining initiator in step 1 is dissolved in isopropanol, and it is added in the reaction vessel, then the ...

Embodiment 1

[0030] Embodiment 1, a kind of high-performance water-soluble acrylic resin, it is prepared by the raw material of following mass fraction: 2 parts of hydroxyethyl methacrylate, 2 parts of hydroxyethyl acrylate, 5 parts of methyl methacrylate, methyl 3.5 parts of isooctyl acrylate, 7 parts of n-butyl acrylate, 4 parts of ethyl acrylate, 1 part of acrylic acid, 2 parts of glycidyl tertiary carbonate, 2 parts of hexafluorobutyl methacrylate, 0.08 parts of initiator, neutralizer 1.5 parts, 0.02 parts of defoamer, 10 parts of isopropanol and 20 parts of deionized water.

Embodiment 2

[0031] Embodiment 2, a kind of high-performance water-soluble acrylic resin, it is prepared by the raw material of following mass fraction: 3 parts of hydroxyethyl methacrylate, 1 part of hydroxyethyl acrylate, 6 parts of methyl methacrylate, methyl 3 parts of isooctyl acrylate, 6 parts of n-butyl acrylate, 3 parts of ethyl acrylate, 2 parts of acrylic acid, 3 parts of glycidyl tertiary carbonate, 2.5 parts of hexafluorobutyl methacrylate, 0.1 part of initiator, neutralizer 1.2 parts, 0.01 parts of defoamer, 15 parts of isopropanol and 10 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to high-performance water-soluble acrylic resin, which is characterized in that the high-performance water-soluble acrylic resin is prepared by using the following raw materials in parts by weight: 2-5 parts of 2-hydroxyethyl methacrylate, 1-3 parts of hydroxyethylacrylate, 5-8 parts of methyl methacrylate, 3-4 parts of 2-ethylhexyl methacrylate, 6-9 parts of n-butyl acrylate, 3-6 parts of ethyl acrylate, 1-2 parts of acrylic acid, 2-5 parts of tertiary carboxylic glycidyl ester, 1-3 parts of hexafluorobutyl methacrylate, 0.08-0.4 part of initiator, 1-2 parts of neutralizer, 0.01-0.02 part of defoaming agent, 8-15 parts of isopropanol and 10-50 parts of deionized water. By adding two modifiers, i.e. the tertiary carboxylic glycidyl ester and the hexafluorobutyl methacrylate in raw materials for conventional water-soluble acrylic resin, the prepared water-soluble acrylic resin has high alkali resistance and high boiling water resistance, the gloss of products coated with the water-soluble acrylic resin is good and the needs of people are met.

Description

technical field [0001] The invention relates to a high-performance water-soluble acrylic resin and a preparation method thereof, belonging to the field of coatings. Background technique [0002] Compared with traditional solvent-based coatings, water-soluble coatings have the advantages of low price, safe use, saving resources and energy, reducing environmental pollution and public hazards, etc., so it has become the main direction of the current development of the coatings industry. Water-soluble acrylic resin coatings have many advantages such as good leveling, high gloss, good film formation, and good film compactness, which can significantly improve the safety and reliability during construction and curing, and retain the mechanical properties of solvent-based acrylic resin coatings. , protective performance and decorative performance, etc., has become the fastest-growing and most diverse non-polluting coating among water-soluble coatings. [0003] However, the various ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F220/18C08F220/14C08F220/28C08F220/22C09D133/08
Inventor 林乾隆葛丽珠
Owner 江阴恒兴涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com