Anti-dropping flame-retardant ABS material and preparation method thereof

An ABS material and anti-drop technology, which is applied in the field of anti-drop flame-retardant ABS material and its preparation, can solve problems such as difficult high-altitude drop testing and failure to meet customer requirements well, and achieve excellent comprehensive performance and good mechanical properties , high efficiency effect

Inactive Publication Date: 2013-01-02
SHENZHEN FUHENG PLASTICS PIGMENT
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Finished products made of flame-retardant ABS materials using this toughening system are difficult to pass the high-altitude drop test and cannot meet customer requirements well

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-dropping flame-retardant ABS material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The present invention also provides a method for preparing an anti-drop flame retardant ABS material, which comprises the following steps:

[0030] a. Weigh each component according to the above mass percentage, specifically, ABS resin: 70-80%; toughening agent: 2-6%; composite flame retardant: 18-25%; antioxidant: 0.2- 0.6%; processing aid: 0.3-1%; anti-dripping agent: 0.1-0.3%, and mix the weighed components in a high-speed mixer and stir for 2-5 minutes;

[0031] b. Add the homogeneously mixed material in step a into the hopper of the twin-screw extruder, melt, blend and extrude through the high-temperature extruder, cool, air-dry, and granulate;

[0032] Among them, the temperature of each heating zone of the twin-screw extruder is respectively set as follows: first zone temperature: 180-190°C; second zone temperature: 185-195°C; third zone temperature: 190-200°C; fourth zone temperature: 200 ~210℃; temperature in zone five: 200~210℃; temperature in zone six: 200~2...

Embodiment 1

[0036] Weigh acrylonitrile-butadiene-styrene copolymer (ABS)--77.3kg, styrene triblock copolymer (SBS)--4kg, composite flame retardant--18kg (bromotriazine--14kg , Sb 2 o 3 --4kg), antioxidant --0.3kg (main antioxidant 1010--0.2kg, secondary antioxidant 168--0.1kg), ethylene bisstearic acid amide (EBS) --0.3kg, containing Polytetrafluoroethylene (PTFE) - 0.1kg.

[0037]Then mix for 3 minutes in a high speed mixer. Then add the mixed material into the hopper of the twin-screw extruder, and control the temperature of each section: Zone 1: 185°C; Zone 2: 185°C; Zone 3: 195°C; Zone 4: 195°C; Zone 5 : 200°C; Sixth zone: 195°C; Seventh zone: 190°C; Eighth zone: 185°C; Machine head temperature: 180°C; Screw speed 400r / min, after melt blending extrusion, water cooling, air drying, pelletizing, drying Dry, and finally packaged into bags to obtain anti-drop flame-retardant ABS material.

Embodiment 2

[0039] Weigh acrylonitrile-butadiene-styrene copolymer (ABS)--74.3kg, styrene triblock copolymer (SBS)--5kg, composite flame retardant--20kg (bromotriazine--15kg , Sb 2 o 3 --5kg), antioxidant --0.3kg (primary antioxidant 1010--0.2kg, secondary antioxidant 168--0.1kg), ethylene bisstearic acid amide (EBS) --0.3kg, containing Polytetrafluoroethylene (PTFE) - 0.1kg.

[0040] Then mix for 3 minutes in a high speed mixer. Then add the mixed material into the hopper of the twin-screw extruder, and control the temperature of each section: Zone 1: 185°C; Zone 2: 185°C; Zone 3: 195°C; Zone 4: 195°C; Zone 5 : 200°C; Sixth zone: 195°C; Seventh zone: 190°C; Eighth zone: 185°C; Machine head temperature: 180°C; Screw speed 400r / min, after melt blending extrusion, water cooling, air drying, pelletizing, drying Dry, and finally packaged into bags to obtain anti-drop flame-retardant ABS material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-dropping flame-retardant ABS material, which comprises the following components by mass: 70-80% of ABS resin; 2-6% of a flexibilizer; 18-25% of a composite flame retardant; 0.2-0.6% of an anti-oxidant; 0.3-1% of a processing additive; and 0.1-0.3% of an anti-dropping agent. The invention also provides the preparation method of the anti-dropping flame-retardant ABS material. The anti-dropping flame-retardant ABS material provided by the invention not only has the advantages of good mechanical properties, high-efficient flame retardance, easy molding processability, and the like, but also has the advantage of no damage after high-altitude drop.

Description

technical field [0001] The invention relates to the technical field of general plastic modification in polymer materials, in particular to a drop-resistant flame-retardant ABS material and a preparation method thereof. Background technique [0002] Acrylonitrile-butadiene-styrene copolymer (ABS) is a material with excellent comprehensive properties, with good toughness, dimensional stability, electrical properties, wear resistance, chemical resistance, dyeability, molding Processability and other advantages. In order to meet the requirements of flame retardancy of ABS materials, flame retardant modification of ABS materials has been carried out. Flame retardant ABS materials are widely used in office equipment, home appliances and other fields. [0003] At present, for flame-retardant ABS materials at home and abroad, the generally used toughening system is ABS high-glue powder. The finished products made of flame-retardant ABS materials using this toughening system are di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L53/02C08K13/02C08K5/136C08K3/22C08K5/3492B29B9/06B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/875B29C48/92B29C2948/92704B29C2948/92895
Inventor 黄裕杰王伟黄春浪
Owner SHENZHEN FUHENG PLASTICS PIGMENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap