Preparation method of super storage battery lead-carbon negative plate

A super battery and negative plate technology, applied in the direction of lead-acid battery electrodes, electrode manufacturing, etc., can solve the problems that the carbon content of the plate cannot be guaranteed, it is not easy to mass-produce, and it is difficult to charge the buffer, etc., to achieve low cost, Improve the utilization rate and eliminate the effect of spike discharge

Active Publication Date: 2015-04-15
TIANNENG GRP JIANGSU TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The external parallel type is mainly to add a capacitor outside the battery, which acts as a charge buffer and memory when the battery is charged and discharged. This method needs to add additional electrical components, and the cost of the battery is relatively high; the internal hybrid type is mainly to mix the capacitor material into the battery. into the battery electrode material to make a capacitive battery plate, its biggest advantage is that it can effectively delay the salinization of the negative plate of the battery, but the plate produced by this method cannot guarantee that the plate has a high The amount of carbon is difficult to play the role of a charge buffer, and the addition of carbon materials will lead to the intensification of hydrogen evolution on the plate; the internal combination type is to attach the capacitor material to the plate of the battery and exist in a parallel manner. When the battery is charged and discharged, it plays the role of a charge buffer and a memory, eliminates the high-current spike discharge during start-up, improves the overall output power of the battery pack, improves the utilization rate of active materials, and increases the specific energy and energy density. However, the existing There are two main types of internal integration technology: one is to dig out part of the lead paste on the plate and replace it with carbon paste, which is more complicated to operate and difficult to carry out large-scale production; the other is to directly replace the battery plate with a pure carbon plate, reduced battery capacity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An embodiment of the present invention provides a method for producing a lead-carbon negative plate, comprising the following steps:

[0024] (1) First, add 100 parts of activated carbon, 4 parts of acetylene black, 4 parts of nano-graphite, 1 part of barium stearate, and 1 part of indium oxide into a stirring container, add water, stir with a latex machine for 1 hour, and then carry out vacuum filtration ;Add 1 part of binder PTFE, 10 parts of LA-133, add 100 parts of water and stir evenly to make a binder diluent; then add the binder diluent to the solid mixture after vacuum filtration, add 100 parts of water and stir evenly After that, the required carbon paste is obtained;

[0025] (2) Apply the carbon paste prepared in step (1) evenly on both sides of the lead negative plate green sheet conventionally produced by Tianneng Battery (Jiangsu) Co., Ltd., and the weight of the paste is 4% of the weight of the lead negative plate green sheet;

[0026] (3) Wrap the plate...

Embodiment 2

[0029] An embodiment of the present invention provides a method for producing a lead-carbon negative plate, comprising the following steps:

[0030] (1) First, add 50 parts of carbon black, 50 parts of carbon nanotubes, 2 parts of acetylene black, 2 parts of spherical graphite, and 1 part of indium oxide into a stirring container, add water, stir with a latex machine for 1 hour, and then carry out vacuum filtration; Add 1 part of binder CMC, 4 parts of CLA-1, add 50 parts of water and stir evenly to make a binder diluent; then add the binder diluent to the solid mixture after vacuum filtration, add 50 parts of water and stir evenly , to obtain the required carbon paste;

[0031] (2) Apply the carbon paste prepared in step (1) evenly on both sides of the lead negative plate green sheet conventionally produced by Tianneng Battery (Jiangsu) Co., Ltd., and the weight of the paste is 2% of the weight of the lead negative plate green sheet;

[0032] (3) Wrap the plate coated with c...

Embodiment 3

[0034] An embodiment of the present invention provides a method for producing a lead-carbon negative plate, comprising the following steps:

[0035] (1) First, add 20 parts of carbon black, 10 parts of activated carbon fiber, 70 parts of super activated carbon, 4 parts of acetylene black, 4 parts of nano-graphite, 4 parts of spherical graphite, 2 parts of barium stearate and 1 part of indium oxide into the stirring Add water to the container, stir with a latex machine for 1 hour, and then carry out vacuum filtration; add 5 parts of binder PTFE, 15 parts of CLA-1 and 200 parts of water and stir evenly to make a binder diluent; then dilute the binder diluent Add it to the solid mixture after vacuum filtration, add 100 parts of water and stir evenly to obtain the required carbon paste;

[0036] (2) Apply the carbon paste prepared in step (1) evenly on both sides of the lead negative plate green sheet conventionally produced by Tianneng Battery (Jiangsu) Co., Ltd., and the weight ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of super storage battery lead-carbon negative plate. The method comprises the following steps of: firstly, mixing and evenly stirring the carbon, the additive and the water, filtering under vacuum condition, adding binder diluents and stirring evenly to obtain the carbon paste; evenly spreading the carbon paste on two sides of a raw lead-carbon negative plate, then, tightly wrapping the negative plate coated by the carbon paste with a coating paper, applying pressure on the negative plate for compaction, then, drying the compacted negative plate for 1-2 hours at the temperature of 45-120 degrees centigrade, and obtaining a lead-carbon negative plate with bipolarity of 'battery character' and 'capacitive character'. In comparison with the method of gouging a part of the lead paste on the negative plate and substituting the gouged part by the carbon paste, the method provided by the invention is convenient to operate and easy to carry out, and simultaneously, avoids bad influence on the battery performance caused by directly adding a carbon plate in the battery, so that the prepared super storage battery is high in performance and long in service life. The method provided by the invention is strong in operability, suitable for bulk production in workshops and extremely low in cost in comparison with the external parallel type super battery.

Description

technical field [0001] The invention relates to the field of storage battery production, in particular to a method for preparing a negative plate of a super storage battery. Background technique [0002] Today's lead-acid battery industry has developed innovatively, combining supercapacitors with existing batteries, so that the high-power characteristics of supercapacitors and the high energy density characteristics of batteries can be concentrated. [0003] The super batteries currently researched are mainly divided into three categories: external parallel type, internal hybrid type, and internal parallel type. The external parallel type is mainly to add a capacitor outside the battery, which acts as a charge buffer and memory when the battery is charged and discharged. This method needs to add additional electrical components, and the cost of the battery is relatively high; the internal hybrid type is mainly to mix the capacitor material into the battery. into the battery...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/04H01M4/16
CPCY02E60/126Y02E60/10
Inventor 赵冬冬陈飞梁佳翔宫江平方明学杨惠强
Owner TIANNENG GRP JIANGSU TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products