A kind of graphene coating agent and the preparation method of this coating agent making super lead-acid storage battery negative plate
A technology of super lead-acid and vinyl coating agent, which is applied in the direction of lead-acid battery electrodes, battery electrodes, circuits, etc. It can solve the problems of easy expansion and deformation of the grid, reduction of maintenance-free performance, and aggravated hydrogen evolution of the negative electrode, so as to achieve bonding reliability. High, improve the specific energy, reduce the effect of charging time
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] Embodiment 1, a kind of graphene paint that makes super lead-acid storage battery negative plate, it is made by following method: following composition is all calculated by weight ratio, (1) the graphene powder of 120, the lignin of 6 Add sodium sulfonate SLS, 10% indium oxide and 1000% water into the mixing tank, and stir at a high speed to form a ready-to-use mixture; (2) add 20% polyvinylpyrrolidone PVP, 10% lithium ion water-based conductive adhesive CLA -1 and 500% of water are added to another mixing tank and stirred evenly to make the binder diluent; (3) Add the binder diluent to the evenly stirred mixture, then add 300 parts of water, and stir at a high speed to make Obtain graphene paint.
[0015] A kind of preparation method that above-mentioned graphene paint makes super lead-acid storage battery negative plate, it comprises the following steps: (1) the prepared graphene paint is evenly coated on raw negative plate both sides through pasting machine , the we...
Embodiment 2
[0017] Embodiment 2, a kind of graphene paint that makes super lead-acid battery negative plate, it is made by following method: following composition is all calculated by weight ratio, (1) with 20 graphene powder, 1 lignin Sodium sulfonate SLS, indium oxide of 2, barium stearate of 3 and water of 1000 are added in the mixing tank, and the mixture is uniformly prepared by high-speed stirring; (2) sodium carboxymethyl cellulose CMC of 8, sodium carboxymethyl cellulose of 2 The lithium ion water-based conductive adhesive LA-133 and 500 water are added to another stirring tank and stirred evenly to make a binder diluent; (3) Add the binder diluent to the evenly stirred mixture, and then add 850 of water, after stirring at a high speed, the graphene paint was prepared.
[0018] A kind of preparation method that above-mentioned graphene coating agent is made super lead-acid storage battery negative plate, it comprises the following steps: (1) the prepared graphene coating agent is ...
Embodiment 3
[0020] Embodiment 3, a kind of graphene paint that makes super lead-acid storage battery negative plate, it is made by following method: following composition is all calculated by weight ratio, (1) the graphene slurry of 60, the woodiness of 3 Add sodium sulfonate SLS, 4% indium oxide, 3% barium stearate and 1000% water into the mixing tank, and stir at a high speed to form a ready-to-use mixture; (2) then add 12% polyvinylpyrrolidone PVP, 8% lithium Add the water of ionic water-based conductive adhesive LA-133 and 500 into another mixing tank and stir evenly to make the binder diluent; (3) Add the binder diluent to the evenly stirred mixture, and then add 1000 water, after stirring at a high speed to obtain a graphene paint.
[0021] A kind of preparation method that above-mentioned graphene coating agent is made super lead-acid storage battery negative plate, it comprises the following steps: (1) the prepared graphene coating agent is evenly coated on raw negative plate both...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com