Polyvinyl chloride transparent weather-resistant sheet

A polyvinyl chloride and transparent technology, applied in the field of PVC transparent weather-resistant sheet, can solve the problems of poor weather resistance of the sheet and restrict the rigid PVC transparent sheet, and achieve the effect of improving strength, novel idea and good effect

Inactive Publication Date: 2013-02-13
苏州集奥贸易有限公司
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the presence of double bonds in this modifier, the weather resistance of the prepared sheet product is very poor, and it can only be used indoors, which greatly limits the rigid PVC transparent sheet.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The polyvinyl chloride transparent weather-resistant sheet of the present invention is formulated according to the following process procedures:

[0015] 1. The preparation of each component and parts by weight of the polyvinyl chloride transparent weather-resistant sheet:

[0016] 1. Preparation of weather resistance modifier:

[0017] According to the weather modifier ratio mentioned above, take vinyl acetate-vinyl chloride ternary copolymer resin (SRC) 1.5, aluminate resin coupling agent 0.5, put them together in the mixer, stir at room temperature, and stir evenly It can be discharged and ready for use.

[0018] 2. The preparation of each component and parts by weight:

[0019] PVC resin: 100; plasticizer: 3; heat stabilizer: 1.5; external lubricant: 0.2; internal lubricant: 0.6; weather modifier: 2.

[0020] two. The preparation of the polyvinyl chloride transparent weather-resistant sheet:

[0021] 1. Mixing: Mix the above-mentioned components by weight, put ...

Embodiment 2

[0024] This embodiment is basically the same as Embodiment 1, the difference is that:

[0025] 1. The preparation of each component and parts by weight of the polyvinyl chloride transparent weather-resistant sheet:

[0026] 1. Preparation of weather resistance modifier:

[0027] Take vinyl acetate-vinyl chloride ternary copolymer resin (SRC) 2 and aluminate coupling agent 0.7 according to the weather modifier ratio, put them together in the mixer, stir at room temperature, and stir evenly It can be discharged and ready for use.

[0028] 2. The preparation of each component and parts by weight:

[0029] PVC resin: 100; plasticizer: 3.2; heat stabilizer: 1.8; external lubricant: 0.21; internal lubricant: 0.61; weather resistance modifier: 2.1.

Embodiment 3

[0031] This embodiment is basically the same as Embodiment 1, the difference is that:

[0032] 1. The preparation of each component and parts by weight of the polyvinyl chloride transparent weather-resistant sheet:

[0033] 1. Preparation of weather resistance modifier:

[0034] Take vinyl acetate-vinyl chloride ternary copolymer resin (SRC) 2.5 and aluminate coupling agent 1 according to the weather modifier ratio mentioned above, put them into the mixer together, stir at room temperature, and stir evenly It can be discharged and ready for use.

[0035] 2. The preparation of each component and parts by weight:

[0036] PVC resin: 100; plasticizer: 3.5; heat stabilizer: 2; external lubricant: 0.25; internal lubricant: 0.65; weather resistance modifier: 3.5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polyvinyl chloride transparent weather-resistant sheet comprising the following components in part by weight: 100 parts of PVC resin, 3 to 4 parts of plasticizer, 1.5 to 2.5 parts of heat stabilizer, 0.2 to 0.3 part of external lubricant, 0.6 to 0.8 part of internal lubricant and 2 to 4 parts of weather-resistant modifier. The production process of the polyvinyl chloride transparent weather-resistant sheet comprises mixing, stirring, heating, cooling and unloading packaging of the components. The polyvinyl chloride transparent weather-resistant sheet disclosed by the invention has reasonable concept and standard technique, can be put into industrial mass production as soon as possible, and has the benefits of high strength, strong toughness, good weather resistance, no deformation because of heat resistance and no embrittlement because of cold resistance. The polyvinyl chloride transparent weather-resistant sheet can be widely applied in the fields of outdoor advertisements, decoration, automobiles curtain walls and the like.

Description

technical field [0001] The invention relates to a plastic sheet, in particular to a transparent weather-resistant polyvinyl chloride sheet. Background technique [0002] So far, the toughening modifier for rigid PVC (polyvinyl chloride) transparent sheet can only be methyl methacrylate, butadiene, styrene ternary graft copolymer (MBS). Due to the presence of double bonds in this modifier, the weather resistance of the prepared sheet product is very poor, and it can only be used indoors, which greatly limits the rigid PVC transparent sheet. Therefore, it is an urgent demand in the market to develop a transparent, weather-resistant, high-toughness rigid polyvinyl chloride transparent weather-resistant sheet. Contents of the invention [0003] The purpose of the present invention is to overcome the defects of the above-mentioned background technology and provide a transparent weather-resistant polyvinyl chloride sheet, which has high strength and good toughness, heat resista...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L31/04
Inventor 马青赛朱山宝邓忠权
Owner 苏州集奥贸易有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap