Method for preparing vinylacetylene

A technology of vinyl acetylene and acetylene, which is applied in the field of preparation of vinyl acetylene, which can solve the problems of large polymers, difficult to further increase the yield of vinyl acetylene, unsatisfactory vinyl acetylene yield, etc., and achieve the suppression of associated high polymer The effect of the generation of compound, the increase of MVA one-way yield, and the increase of MVA selectivity

Inactive Publication Date: 2013-03-13
CHONGQING YOUCUI SCI & TECH
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the yield of vinyl acetylene (MVA) in this prior art is not satisfactory, and its specific technical indicators are that the single-pass yield of MVA and the selectivity of MVA are all low—the accompanying The large amount of polymer is one of the reasons for the unsatisfactory yield o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing vinylacetylene
  • Method for preparing vinylacetylene
  • Method for preparing vinylacetylene

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] A method for preparing vinyl acetylene, the method is to continuously fill a closed reactor containing a catalyst system with acetylene gas under heating conditions, so that acetylene can undergo a dimerization reaction under the action of the catalyst system to generate ethylene The catalyst system includes main catalyst cuprous chloride, auxiliary solvent ammonium chloride, hydrochloric acid and water. In the present invention, there is also promoter cerium chloride in the catalyst system; the steps of the method are as follows:

[0012] ① Put co-solvent ammonium chloride, co-catalyst cerium chloride and water into the reactor. 3 Nitrogen bubbling and stirring at a flow rate of / h to fully dissolve the ammonium chloride and cerium chloride (under the following proportioning conditions, it can be fully dissolved after 30 minutes);

[0013] ② While maintaining the temperature of 70-90°C, add cuprous chloride and hydrochloric acid to the reactor in turn, and at the same...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing vinylacetylene. According to the method, cerium chloride serving as a promoter is added to the catalyzing system on the basis of a nieuwland catalyst system, and the mixing ratio of components and the processing steps of the vinylacetylene are correspondingly adjusted. During the dimerization reaction of acetylene, the generation of associated polymers can be inhibited well, and the amount of generated associated polymers is greatly reduced; and furthermore, the selectivity of the vinylacetylene (MVA) which is the target product can be effectively improved, and the output is raised as well.

Description

technical field [0001] The present invention relates to a process for the preparation of vinyl acetylene by dimerization of acetylene. Background technique [0002] Chloroprene rubber (CR) is an important variety of synthetic rubber. At present, most of the enterprises producing CR use acetylene as the main raw material, and under the action of a catalyst, they first synthesize the intermediates for the production of CR through acetylene dimerization reaction. - Vinyl acetylene. That is to say, if you want to increase the yield of chloroprene rubber, you must first find a better catalyst to increase the yield of vinyl acetylene. This kind of catalyst has already existed, and it is the famous Newland (Nieuwland) catalyst system, which is made of main catalyst cuprous chloride (Cu 2 Cl 2 ), co-solvent ammonium chloride (NH 4 Cl) and hydrochloric acid (HCl) in an acidic aqueous solution. The so-called acetylene dimerization reaction is to continuously fill the closed react...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C07C11/30C07C2/38B01J27/122
Inventor 杜军刘作华陶长元
Owner CHONGQING YOUCUI SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap