Production method of pipeline steel plate with excellent impact toughness
A production method and impact toughness technology are applied in the production field of pipeline steel plates with excellent impact toughness, which can solve the problems of increased time, disadvantageous mass production, increased process cost and time, etc., and achieve the performance of tensile strength and yield strength. , The production process is simple, the effect of improving the internal quality
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0023] Example 1-3
[0024] The example is a method for producing a pipeline steel plate with excellent impact toughness. The components of each example are shown in Table 1 by weight percentage:
[0025] Table 1 Chemical composition (wt%) of each embodiment of the present invention
[0026] ExampleC Si MnPS Alt Nb Ti Ni Example 10.050.251.550.0120.00300.0260.0540.0090.16 Example 20.050.241.530.0120.00250.0300.0580.0110.16 Example 3 0.050.251.520.0120.00280.0280.0530.0090.15
[0027] The production methods of each embodiment are as follows:
Example Embodiment
[0028] Example 1
[0029] The production method includes the following steps:
[0030] (1) Smelting: The process flow of molten iron pretreatment- converter smelting-LF refining-RH furnace vacuum treatment is adopted. After Mg desulfurization treatment, molten iron [S]≤0.005% is required; the final composition of the converter is controlled according to the composition of the above-mentioned pipeline steel plate; LF furnace Purity control target of molten steel in refining: [O]≤15ppm, [N]≤50ppm and [H]≤2ppm; RH vacuum treatment vacuum holding time 20min;
[0031] (2) Continuous casting: adopting dynamic soft reduction technology to produce cast slabs, the degree of central segregation is greatly reduced, reduction amount = 3.5mm, solid phase ratio fs = 0.75;
[0032] (3) Heating: the billet enters the heating furnace, the heating temperature of the billet is 1150℃, the furnace time is 200min, and the discharge temperature is 1180℃;
[0033] (Iv) Rolling: Two-stage rolling is adopted, t...
Example Embodiment
[0034] Example 2
[0035] The production method includes the following steps:
[0036] (1) Smelting: The process flow of molten iron pretreatment- converter smelting-LF refining-RH furnace vacuum treatment is adopted. After Mg desulfurization treatment, molten iron [S]≤0.005% is required; the final composition of the converter is controlled according to the composition of the above-mentioned pipeline steel plate; LF furnace Purity control target of molten steel in refining: [O]≤15ppm, [N]≤50ppm and [H]≤2ppm; RH vacuum treatment vacuum holding time 25min;
[0037] (2) Continuous casting: adopting dynamic soft reduction technology to produce cast slab, the degree of central segregation is greatly reduced, reduction = 3.5mm, solid phase ratio fs = 0.95;
[0038] (3) Heating: the slab enters the heating furnace, the heating temperature of the slab is 1200℃, the furnace time is 220min, and the discharge temperature is 1220℃;
[0039] (Iv) Rolling: Two-stage rolling, rough rolling temperatur...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap