Salt sculpture raw material and method adopting raw material to produce salt sculpture

A technology of salt carving and raw materials, which is applied in the field of salt carving, can solve the problems of high technical requirements for sculptors, fragile ice cubes, and insufficient aesthetics, and achieve the effect of reducing costs, reducing usage, and having great artistic appreciation value

Inactive Publication Date: 2013-08-07
上海盐商集团有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] There are many kinds of sculpture materials, such as stone, wood, ice, plastic, mud, etc. Each material has its own advantages and disadvantages in actual carving. For example, ice sculptures are crystal clear, but ice is fragile and difficult to repair. Ice carvings have high technical requirements, and ice sculpture products must be preserved under specific conditions; jade carvings and root carvings, etc., all have high requirements for carving skills, and need to carry out natural design and carving according to the shape of the material itself; clay sculptures have the lowest requirements, but the aesthetic feeling is not enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) Take 100-mesh high-purity sodium chloride with a total weight of 80%, put it in a microwave oven, and dry it at 200°C for 8 minutes to make its moisture content lower than 0.5%;

[0024] (2) Pour the salt powder into the container, add 0.8% of the total weight of sodium alkylsulfonate, put it in a resistance furnace and heat it to 1000°C to completely melt the sodium chloride;

[0025] (3) When the temperature in the container drops to 800°C, add 0.4% of the total weight of fluorescent whitening agent VBL and 0.5% of selenium micropowder into the container, and then slowly cool down to form massive salt crystals;

[0026] (4) Use massive salt crystals as raw materials, and carve them into salt carving crafts of a certain shape according to requirements;

[0027] (5) Weigh rosin pentaerythritol ester, aminoethylpiperazine, N,N-dimethylaminopropyl acrylamide and zinc oxide with a total weight of 16%, 0.8%, 1%, and 0.5%, respectively, and mix the above components Unif...

Embodiment 2

[0033] (1) Take 100-mesh high-purity sodium chloride with a total weight of 88%, put it in a microwave oven, and dry it at 200°C for 8 minutes to make its moisture content less than 0.5%;

[0034] (2) Pour the salt powder into the container, add 1% of the total weight of sodium alkylsulfonate, put it into a resistance furnace and heat it to 950°C to completely melt the sodium chloride;

[0035] (3) When the temperature in the container drops to 800°C, add 1% of the total weight of fluorescent whitening agent TA and 0.5% of selenium micropowder into the container, and then slowly cool down to form massive salt crystals;

[0036] (4) Use massive salt crystals as raw materials, and carve them into salt carving crafts of a certain shape according to requirements;

[0037] (5) Weigh 8%, 0.5%, 0.5%, and 0.5% of the total weight of rosin pentaerythritol ester, aminoethylpiperazine, N, N-dimethylaminopropyl acrylamide and zinc oxide, and mix the above components Uniform, made into re...

Embodiment 3

[0041] (1) Take 70% of the total weight of 100-mesh high-purity sodium chloride, put it in a microwave oven, and dry it at 200°C for 8 minutes to make the moisture content lower than 0.5%;

[0042] (2) Pour the salt powder into the container, add 1% of the total weight of sodium alkylsulfonate, put it into a resistance furnace and heat it to 900°C to completely melt the sodium chloride;

[0043] (3) When the temperature in the container drops to 800°C, add 2% of the total weight of fluorescent whitening agent VBL and 0.5% of selenium micropowder into the container, and then slowly cool down to form massive salt crystals;

[0044] (4) Use massive salt crystals as raw materials, and carve them into salt carving crafts of a certain shape according to requirements;

[0045] (5) Weigh rosin pentaerythritol ester, aminoethylpiperazine, N,N-dimethylaminopropyl acrylamide and calcium oxide with a total weight of 25%, 0.5%, 0.4%, and 0.6%, respectively, and mix the above components Un...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a salt sculpture raw material and a method adopting the raw material to product a salt sculpture. The raw material comprises the components: 70% to 90% of salt powder, 0.5% to 2% of inorganic salt crystallization promoter agent, 8% to 25% of white water resin, 0.2 to 1% of curing agent, 0.2% to 2% of modifying agent, 0.5% to 1.5% of deacidification agent, 0.5% to 2% of fluorescent whitening agent and 0.5% to 1% of selenium micropowder. The raw material solves the problem that the conventional salt sculpture raw material is low in recrystallization performance, non-uniform in texture and easy to absorb moisture; the curved artwork is glittering, translucent and snow-white; and the salt sculpture raw material is very suitable for being taken as a high-grade slat sculpture artwork raw material.

Description

technical field [0001] The invention relates to a sculpture raw material and a method for producing sculpture by using the raw material, in particular to a sculpture raw material using salt as the main material and a method for producing salt sculpture by using the raw material. Background technique [0002] There are many kinds of sculpture materials, such as stone, wood, ice, plastic, mud, etc. Each material has its own advantages and disadvantages in actual carving. For example, ice sculptures are crystal clear, but ice is fragile and difficult to repair. Ice carvings have high technical requirements, and ice sculpture products must be preserved under specific conditions; jade carvings and root carvings, etc., all have high requirements for carving skills, and need to carry out natural design and carving according to the shape of the material itself; clay sculptures have the lowest requirements, but the aesthetic feeling is not enough . Aiming at the many deficiencies ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/10
Inventor 夏一栋
Owner 上海盐商集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap