High-strength laser transmission connecting method

A technology of laser transmission and connection method, which is applied in the direction of laser welding equipment, welding equipment, manufacturing tools, etc., can solve problems such as weld damage, achieve local connection firmness, and improve the effect of connection strength

Inactive Publication Date: 2013-05-01
JIANGSU UNIV
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The document "The Effect of Laser Shock Surface Strengthening on the Mechanical Properties of Welded Joints" describes a method for surface strengthening treatment of welded joints to improve tensile strength. This method is to improve the strength of welded connections after welding. In transmission welding Inevitably cause damage to the weld seam after welding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength laser transmission connecting method
  • High-strength laser transmission connecting method
  • High-strength laser transmission connecting method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] Below in conjunction with specific embodiment the present invention is further described, weld transparent nylon and 304 stainless steels with the present invention

[0018] Welding preparation: The selected welding transparent transparent material nylon 12 has a size of 10x10x2mm, the light-absorbing material 304 stainless steel 14 has a size of 10x10x0.6mm, and the laser transmission welding laser uses a continuous energy semiconductor laser generator 7 with a maximum power of 130w and a wavelength of 980nm±10nm, 43-type micro-hole drilling machine parameters are spindle speed n: 15000-20000r / min, feed speed f: 0.5-1mm / s, drill diameter 0.1-0.5mm, drill material is high-speed steel.

[0019] Surface treatment of the weldment: ultrasonically clean the sample 304 stainless steel 15 to remove surface impurities, put it on the workbench of the 43-type micro-hole drilling machine, and select the parameters as spindle speed n: 20000r / min, feed speed f: 0.5mm / s, each depth i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength laser transmission connecting method, belongs to the technical field of laser transmission welding, and especially relates to the laser transmission welding between polymers. The method comprises the following steps: treating a to-be-welded surface of a metal material by adopting a drilling machining method and forming pits on the surface; at a welding moment, taking the metal with the surface subjected to the drilling machining treatment as a lower-layer light-absorbing material and taking the polymer as an upper-layer light-transmitting material; adopting a lapped connecting mode and using a restraint layer for clamping and applying welding pressure; and using a semiconductor laser device for performing laser transmission welding, causing the surface temperature to quickly reach the melting point of the upper-layer polymer and melting the surface of the polymer. The pits are formed on the polymer surface through drilling mechanical treatment, so that under the action of a welding pressure, the melted polymer flows into the pits, an occlusion interface with a riveted structure is formed at a welding joint, and the high-strength laser transmission welding is realized. The high-strength laser transmission connecting method can be widely applied to the field of the laser transmission welding with higher demand on the connecting strength.

Description

technical field [0001] The invention belongs to the technical field of laser transmission welding, in particular to a method capable of improving the connection strength of metal and polymer laser transmission welding. A pit with a certain depth is formed on the metal surface by drilling and machining holes. During laser transmission welding, the molten light-transmitting polymer flows into the pit under the action of welding pressure, forming a riveted structure at the weld. The occlusal interface increases the connection contact area between the polymer and the polymer, thereby promoting the better combination of the gold polymer and the polymer, and obtaining high-strength laser transmission welding. Background technique [0002] At present, laser transmission welding technology is a high-tech processing with many advantages such as airtightness, watertightness, fast welding speed, high precision, high weld strength, no flash, no residue, no vibration, small thermal stres...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K26/20B23K26/18B23K26/42B29C65/16
CPCB29C65/1616B29C65/1635B29C65/1654B29C65/44B29C66/02B29C66/1122B29C66/30325B29C66/41B29C66/43B29C66/71B29C66/742B29C66/74283B29C66/8122B29C66/81267B29C66/8322B29C66/836B29C66/9221B29C66/929B29C66/939B29K2077/00B29K2909/08
Inventor 刘会霞赵振关陈浩黄创严长顾宇轩孟冬冬伍彦伟蔡野李品王霄
Owner JIANGSU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com