Thermoplastic foaming polyurethane fiber board, production method and uses thereof

A foaming polyurethane and thermoplastic technology, applied in the field of thermoplastic foaming polyurethane fiberboard, its production and application, can solve the problems of easy coloring and so on

Active Publication Date: 2013-05-01
JIANGSU BIDE SCI & TECH CO LTD
View PDF6 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] c). E

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermoplastic foaming polyurethane fiber board, production method and uses thereof
  • Thermoplastic foaming polyurethane fiber board, production method and uses thereof
  • Thermoplastic foaming polyurethane fiber board, production method and uses thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0102] Thermoplastic foamed polyurethane fiberboards were prepared as follows:

[0103] Preparation of A surface layer:

[0104]

[0105] Stir the above raw materials with a mixer for 5-10 minutes, then use a 10,000-horsepower machine (internal mixer) to heat at 140°C for 5-8 minutes, squeeze and mature, and then heat and knead at 150°C with a double-roller mill. The four-roller calender presses the tablet, the thickness is adjusted to about 0.30mm, embossed, cooled, and the coiling is about 250m per bundle. Finally, use a printing machine to print graphics and text to obtain the A surface layer.

[0106] Preparation of B middle layer sheet:

[0107]

[0108] Stir and mix the above raw materials with a mixer for 5-10 minutes, then use a 10,000-horsepower machine (internal mixer) to heat to 140°C-150°C and squeeze the material for 5-7 minutes, the temperature of the material is 140°C-145°C, and then pass through the double-roller Roller kneading, four-roller calender c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a thermoplastic foaming polyurethane fiber board, a production method and uses thereof. The thermoplastic foaming polyurethane fiber board comprises an A surface layer, a B middle layer and a C bottom layer, wherein the A surface layer, the B middle layer and the C bottom layer are integratedly compounded from top to bottom, the A surface layer is a sheet material prepared by carrying out mixing calendaring on a TPU resin, a filler, a fire retardation agent, a stabilizer, a lubricant and a colorant according to a certain ratio, the B middle layer is a layer prepared by foaming the sheet material prepared by carrying out mixing calendaring on a TPU resin, a filler, a fire retardation agent, a stabilizer, a lubricant and a colorant according to a certain ratio, and the C bottom layer is a layer prepared by drying a fiber cloth impregnated with a TPU composition. The thermoplastic foaming polyurethane fiber board can be used as flooring boards, wall panels, roof hanging plates and indoor partition boards, and can be used for production of furniture materials and various building materials.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a thermoplastic foamed polyurethane fiber board, its production method and application. The thermoplastic foamed polyurethane fiber board includes A surface layer, B middle layer and C bottom layer which are combined from top to bottom , wherein, the A surface layer is a sheet prepared by mixing and calendering TPU resin, filler, flame retardant, stabilizer, lubricant and colorant in proportion, and the B middle layer is made of TPU resin, filler, flame retardant, stabilizer Agent, lubricant, foaming agent and colorant are mixed and calendered in proportion to the layer obtained by foaming the prepared sheet, and the C bottom layer is the layer obtained by drying the fiber cloth impregnated with the TPU composition. The thermoplastic foamed polyurethane fiber board according to the present invention can be used as a floor board, a wall board, a roof hanging board, an i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/04B32B27/06B32B27/18B32B27/40B32B37/06C08L75/04C08J9/10B29C44/20B29C43/24B29C59/00E04F15/10E04F13/075E04C2/284
Inventor 刘家勋
Owner JIANGSU BIDE SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap