Antistatic polyester, preparation method and application of antistatic polyester

An antistatic and polyester technology, applied in the direction of single-component polyester artificial filament, etc., can solve the problem of fiber loss of antistatic, and achieve the effects of good antistatic retention, reduced loss, and excellent antistatic performance

Inactive Publication Date: 2013-05-29
TORAY FIBER RES INST(CHINA) CO LTD
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this polyester, when the fiber is subjected to post-processing such as weight reduction or dyeing, the polyethylene glycol is dissolv

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic polyester, preparation method and application of antistatic polyester

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0043] Example 1

[0044] Add bishydroxyethyl terephthalate into the esterification reaction layer, keep the temperature at 250°C and the pressure at 1.2×10 5 Pa, 10 parts by weight of TPA (terephthalic acid) and 4.5 parts by weight of EG (ethylene glycol) slurry were gradually added to the esterification reaction layer within 4 hours, and then the esterification reaction was carried out for 1 hour. Finally, 12.3 parts by weight were taken from the obtained esterification reaction product and added to the polycondensation reaction layer.

[0045] Keep the esterification reaction product at 250°C under normal pressure, add a defoamer (methyl silicone oil) equivalent to 0.01% of the polyester weight and phosphoric acid equivalent to 18ppm of the polyester weight in terms of phosphorus atoms, and stir for 5 minutes Add antimony trioxide equivalent to 230ppm of polyester weight in terms of antimony atoms, cobalt acetate equivalent to 15ppm of polyester weight in terms of cobalt a...

Example Embodiment

[0046] Example 2

[0047] Add the Y-10000 (structure shown in formula 4 that is equivalent to polyester weight 5wt%) in the polycondensation reaction, R 1 Be ethylene, molecular weight 10000g / mol), other are with embodiment 1.

Example Embodiment

[0048] Example 3

[0049] In the polycondensation reaction, Y-4000 equivalent to 15 wt% of the polyester weight was added, and the others were the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses antistatic polyester, a preparation method and application of the antistatic polyester. The antistatic polyester comprises polyether with amino end groups and sulphonate. The polyether with the amino end groups overcomes the defect of easy hydrolyzation of polyether with hydroxyl end groups, so that the antistatic performance can be still maintained after the antistatic polyester is dyed or reduced. By aid of the sulphonate, the additive amount of the polyether with the amino end groups is reduced to guarantee the spinnability of the antistatic polyester. The antistatic polyester can be widely applied to fibers.

Description

technical field [0001] The invention relates to an antistatic polyester and its production method and application. Background technique [0002] The dielectric constant and electrical conductivity of conventional polymer materials are very low, and fibers made of polymer materials are prone to static electricity when rubbed, which brings difficulties to post-weaving processing and causes easy staining during the use of the fabric. Dirt, sticky dust and other problems. Therefore, it is becoming more and more important to endow these polymer materials with antistatic properties. [0003] The current methods to improve the conductivity of materials include coating antistatic agents on the surface of molded products or using antistatic agents or conductive particles that have antistatic effects during polyester synthesis or blending. However, for the former method, the antistatic agent coated on the surface will slowly fall off with the prolongation of use time, and there is n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G63/685C08G63/78C08K5/42D01F6/92
Inventor 吴亚薇李旭望月克彦
Owner TORAY FIBER RES INST(CHINA) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap