Process for spaying MoS2 on bearing bush without alloy layer

A technology of alloy layer and process, which is applied in the direction of coating, liquid coating device on the surface, surface pretreatment, etc., can solve the problems such as difficulty in spraying MoS2, achieve the effect of reducing scratches, reducing pollution and prolonging the service life

Active Publication Date: 2014-12-17
YANTAI CHUNSHENG SLIDING BEARING
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention proposes a technique of spraying MoS2 on bearing pads with no alloy layer, which solves the problem that it is difficult to spray MoS2 on bearing pads without alloy layers in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for spaying MoS2 on bearing bush without alloy layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0021] Such as figure 1 Shown, is the flow chart of the alloy-free layer bearing pad spraying MoS2 process of the present invention, which includes the following steps:

[0022] 1) Cleaning; place the finely bored steel back layer in an ultrasonic cleaning machine filled with a neutral cleaning agent for cleaning at a temperature of 60-70°C for 2-8 minutes;

[0023] 2) Pickling; put the steel back layer in 100-120g / L dilute hydrochloric acid, and wash it at room t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a process for spaying MoS2 on a bearing bush without an alloy layer, and aims to solve the problem in the prior art of spaying MoS2 on the bearing bush without the alloy layer. The process comprises the following steps of cleaning, pickling, fresh water cleaning, steel titanizing, cold water rinsing, hot water rinsing, spraying, oven-drying, steel back burnishing, sintering and the like of a steel back layer, wherein before pickling, the steel back layer after being cleaned can be firstly placed in tap water for cleaning; and before spraying, steel back layer after being rinsed by hot water can be firstly placed in an oven for oven-drying. The process is safe and environment-friendly in the implementation process; as galvanizing is omitted, pollution to the environment can be efficiently reduced; and the bearing bush produced by adopting the process has better dry grinding resistance, meshing resistance, corrosion resistance and wear resistance, and can reduce scuffing on the inner surface of the bearing bush in the installation and use process, so that the service lives of the bearing bush and lubricant in the bearing bush can be prolonged.

Description

technical field [0001] The invention relates to the technical field of bearing pad production, in particular to a technique for spraying MoS2 on a bearing pad without an alloy layer. Background technique [0002] At present, there are generally two types of bearing pad materials used in high-horsepower diesel engines in our country, one is aluminum-based materials, and the other is copper-lead materials. In general, the pressure on the main bearing bush is relatively small, so the main bearing bush is generally made of aluminum-based materials, and the connecting rod bush is generally made of copper-lead material because of the high blast pressure that the engine bears during the operation of the engine. . The fatigue strength of copper-lead materials is above 125 MPa, which is far greater than that of aluminum-based materials. Since the alloy layer of aluminum-based materials is relatively soft, electroplating is generally not required, while copper-lead materials have hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B05D3/00B05D1/36
Inventor 于贵海孙淑利
Owner YANTAI CHUNSHENG SLIDING BEARING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com