Biomass-regenerated-fiber-blended soft smooth fabric and production method

A technology of regenerated fibers and blended fabrics, applied in the direction of fabrics, textiles, textiles and papermaking, etc., to achieve the effect of good strength, smooth cloth surface and soft hand feeling

Active Publication Date: 2013-07-10
RUGAO CITY DINGYAN TEXTILE
View PDF8 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there are patents disclosing that one of the pupa protein fiber and the bamboo fiber is blended with other one or more fibers to make a blended fabric, but the pupa protein fibe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] "Pupus Protein Fiber / Lay Bamboo Fiber" Poplin

[0021] The proportion of each component in the blended fabric:

[0022] Pupa protein fiber 1.33dtex×38mm 60%

[0023] Bamboo fiber 1.33dtex×38mm 40%

[0024] Yarn: 14.8tex

[0025] Fabric: Width 165cm, warp density 523.5 threads / 10cm, weft density 283 threads / 10cm, one-up and one-down plain weave woven poplin smooth fabric, fabric weight 130 .

[0026] (1) Carding process: cylinder speed is 330r / min, licker-in speed is 650r / min;

[0027] (2) Roving process: the drafting ratio of the roving is 8, and the drafting ratio in the rear area should be selected as small as 1.20 times;

[0028] (3) Spinning process: the compact spinning process and low-torque spinning technology are adopted, and the sum of the low-torque false twist belt speed and the output speed of the front roller is 1: 1.1;

[0029] (4) Warping: batch warping, warping tension 20dN, warping speed 400r / min;

[0030] (5) Sizing: Potato starch size is selec...

Embodiment 2

[0033] "Pupus protein fiber / bamboo fiber / milk fiber" twill

[0034] The proportion of each component in the blended fabric:

[0035] Pupa Protein Fiber 30%

[0036] Lay Bamboo Fiber 40%

[0037] Milk Fiber 30%

[0038] Yarn: 16.7tex

[0039] Fabric: 168cm, 342.5 threads / 10cm, weft density 181 threads / 10cm, three-up and one-down twill woven smooth fabric, fabric weight 85 .

[0040] (1) Carding process: cylinder speed is 330r / min, licker-in speed is 650r / min;

[0041] (2) Roving process: the drafting ratio of the roving is 8, and the drafting ratio in the rear area should be selected as small as 1.21 times;

[0042] (3) Spinning process: compact siro spinning process and low torque spinning technology are adopted, the spinning spindle speed is 13500rpm, a suction slot is installed in the spinning triangle area, and the suction negative pressure is controlled to 1900Pa, and the suction double slots are symmetrically arranged , the distance between the outlets of the doub...

Embodiment 3

[0047] "Pupus protein fiber / bamboo fiber / chitin fiber" poplin

[0048] The proportion of each component in the blended fabric:

[0049] Pupa Protein Fiber 30%

[0050] Lay Bamboo Fiber 40%

[0051] Chitin Fiber 30%

[0052] The processing steps of this embodiment are the same as those in Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a biomass-regenerated-fiber-blended soft smooth fabric and a production method thereof. The blended fabric is prepared from raw materials of pupa protein fiber and Lyocell bamboo fiber, and a finished fabric comprises, by weight, 20-80% of the pupa protein fiber and 20-80% of the Lyocell bamboo fiber. By utilizing high blending performance of the pupa protein fiber and the Lyocell bamboo fiber, one or more other biomass regenerated fibers can be added into the blended fabric, and by weight, total content of the pupa protein fiber and the Lyocell bamboo fiber in the finished fabric is 30-70% (wherein one of the pupa protein fiber and the Lyocell bamboo fiber is not less than 15%) while total content of the other biomass regenerated fibers in the finished fabric is 30-70%. The biomass-regenerated-fiber-blended soft smooth fabric is green, environment-friendly, soft, smooth and good in moisture absorption, breathability and strength, has natural antibacterial property, and can be used for high-grade products of clothes, home textiles, decoration and the like.

Description

technical field [0001] The invention relates to a soft and smooth fabric blended with regenerated biomass fibers and a production method thereof, belonging to the field of textile engineering. Background technique [0002] Under the background of environmental protection and healthy fashion trends, human beings return to nature and advocate green. People pay more and more attention to natural fiber and environmentally friendly fiber textiles. People have higher requirements for clothing and home textiles. These demands continue to promote and promote With the development of textile fiber raw materials and clothing fabrics, the use of several fiber blends to produce new yarns and fabrics with new functions has become an important source of textile raw materials. [0003] Pupa protein fiber is a kind of protein fiber with stable skin-core structure, which is made by blending silkworm pupa protein and natural cellulose fiber by comprehensive utilization of polymer modification ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/00D02G3/04D03D15/20D03D15/225D03D15/233D03D15/292D03D15/47D03D15/50
Inventor 陈坚朱张林
Owner RUGAO CITY DINGYAN TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap