Method for making black sound absorption and flame retardation paper through adhesive spraying
A flame-retardant paper and black technology, applied in paper, papermaking, paper coating, etc., can solve the problems of unsatisfactory selection of building materials, uneven surface color, poor performance stability, etc., and achieve excellent performance of finished products, excellent heat resistance, easy coloring effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] 1) Preparation of base paper
[0026] Using wet papermaking technology, mix glass fibers with a length of 3-6 mm and a diameter of 8-10 μm and masson pine fibers with a length of 3.11-4.11 mm and a width of 45-55 μm to obtain a mixture, which is dispersed, dehydrated and dried After drying, the final weight is 40g / m 2 Among them, glass fiber accounts for 30% of the total mass of glass fiber and masson pine fiber, and masson pine fiber accounts for 70% of the total mass of glass fiber and masson pine fiber.
[0027] 2) spray glue
[0028] First, the base paper is sprayed with a styrene-acrylic latex solution with a mass concentration of 4%, and the base paper after spraying the styrene-acrylic latex solution is dried for the first time in an oven for about 2 minutes until the dryness is 75%; then Spray the mixed solution of brominated flame retardant with a mass concentration of 4% and Xianlit M100 color paste with a mass concentration of 1% on the base paper that has ...
Embodiment 2
[0030] 1) Preparation of base paper
[0031] Using wet papermaking technology, mix glass fibers with a length of 3-6 mm and a diameter of 8-10 μm and masson pine fibers with a length of 3.11-4.11 mm and a width of 45-55 μm to obtain a mixture, which is dispersed, dehydrated and dried After drying, the final weight is 41g / m 2 Among them, glass fiber accounts for 32% of the total mass of glass fiber and masson pine fiber, and masson pine fiber accounts for 68% of the total mass of glass fiber and masson pine fiber.
[0032] 2) spray glue
[0033] First, the base paper is sprayed with 5% styrene-acrylic latex solution, and the base paper after spraying the styrene-acrylic latex solution is dried for the first time in an oven for about 2 minutes until the dryness is 76%; then Spray the mixed solution of brominated flame retardant with a mass concentration of 4% and Xianlit M100 color paste with a mass concentration of 1% on the base paper that has been dried for the first time, ...
Embodiment 3
[0035] 1) Preparation of base paper
[0036] Using wet papermaking technology, mix glass fibers with a length of 3-6 mm and a diameter of 8-10 μm and masson pine fibers with a length of 3.11-4.11 mm and a width of 45-55 μm to obtain a mixture, which is dispersed, dehydrated and dried After drying, the final weight is 41g / m 2 Among them, glass fiber accounts for 34% of the total mass of glass fiber and masson pine fiber, and masson pine fiber accounts for 66% of the total mass of glass fiber and masson pine fiber.
[0037] 2) spray glue
[0038] First, the base paper is sprayed with an acrylic latex solution with a mass concentration of 5%, and the base paper after spraying the acrylic latex solution is dried for the first time in an oven for about 2 minutes until the dryness is 77%; The first dried base paper was sprayed with a mixed solution of halogen-phosphorous synergistic flame retardant with a mass concentration of 3% and Xianlit M100 color paste with a mass concentrat...
PUM
Property | Measurement | Unit |
---|---|---|
length | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com