A wood-plastic co-extrusion profile and its production method

A technology for extruding profiles and plastic-wood, applied in the field of plastic-wood co-extrusion profiles and their production, can solve the problems of improving aging resistance, high water absorption, easy pulverization, etc. The effect of weather resistance

Active Publication Date: 2015-12-02
NINGBO HELONG NEW MATERIAL
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] 2) The service life of wood-plastic products can be used for more than 30 years according to theoretical calculations. At present, the service life of wood-plastic products produced by various manufacturers is 10 to 15 years, and the aging resistance performance needs to be improved;
[0012] 3) In a humid environment, it is easy to mildew;
[0013] 4) It is easy to pulverize when soaked in water all the time;
[0014] 5) Compared with pure plastic products, the water absorption rate is relatively high;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] The core body of the present invention is an ordinary plastic wood profile, which is composed of wood powder, plastics, lubricant and toner, and its percentage by parts: wood powder is 66, plastic is 30, lubricant is 3, and toner is 1.

[0051]The functional layer of the present invention is composed of sarin resin, plastics, toner, antioxidant, anti-ultraviolet agent and inorganic filler modifier, and the percentage by parts: sarin resin is 30, HDPE is 50, toner is 5, The antioxidant is 1, the anti-ultraviolet agent is 0.6, and the inorganic filler modifier is 13.4.

[0052] The production method of plastic-wood co-extrusion profile of the present invention, comprises the following steps:

[0053] Step 1. Core raw material preparation:

[0054] a. The wood powder is dried through a drying system at a temperature of 175°C so that the moisture content is within 1%;

[0055] b. Ingredients, according to the percentage of parts, wood powder is 66, plastic is 30, lubrican...

Embodiment 2

[0069] The core body of the present invention is an ordinary plastic wood profile, which is composed of wood powder, plastics, lubricant and toner, and its percentage by parts: wood powder is 50, plastic is 40, lubricant is 3, and toner is 1.

[0070] The functional layer of the present invention is composed of sarin resin, plastics, toner, antioxidant, anti-ultraviolet agent and inorganic filler modifier, and the percentage by parts: sarin resin is 30, HDPE is 50, toner is 5, The antioxidant is 1, the anti-ultraviolet agent is 0.6, and the inorganic filler modifier is 13.4.

[0071] Another production method of the wood-plastic co-extrusion profile of the present invention comprises the following steps:

[0072] Step 1. Core raw material preparation:

[0073] a. The wood powder is dried through a drying system at a temperature of 175°C so that the moisture content is within 1%;

[0074] b. Ingredients, according to the percentage of parts: 50 for wood powder, 40 for plastic...

Embodiment 3

[0088] The core body of the present invention is an ordinary plastic wood profile, which is composed of wood powder, plastics, lubricant and toner, and its percentage by parts: wood powder is 66, plastic is 30, lubricant is 3, and toner is 1.

[0089] The functional layer of the present invention is composed of sarin resin, plastics, toner, antioxidant, anti-ultraviolet agent and inorganic filler modifier, and the percentage by parts: sarin resin is 50, HDPE is 30, toner is 5, The antioxidant is 1, the anti-ultraviolet agent is 0.6, and the inorganic filler modifier is 13.4.

[0090] Another production method of the wood-plastic co-extrusion profile of the present invention comprises the following steps:

[0091] Step 1. Core raw material preparation:

[0092] a. The wood powder is dried through a drying system at a temperature of 175°C so that the moisture content is within 1%;

[0093] b. Ingredients, according to the percentage of parts: 66 for wood powder, 30 for plastic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a plastic-wood coextrusion section material and a production method thereof, belongs to the technical field of composite materials. The coextrusion section material provided by the invention comprises a core body and a functional layer, wherein the functional layer covers outside a section material core layer; and the thickness of the functional layer is 0.5-1.5 mm, the surface hardness of the functional layer is 55-72 shore D, the thickness of the core body is 3-100 mm, and the width of the core body is 8.5-300 mm. Compared with the prior art, the plastic-wood coextrusion section material provided by the invention has the excellent surface abrasive resistance and scratch-resistant property and weather ability, the fadedness is greatly reduced as compared with the common plastic-wood coextrusion section material, and a mildew phenomenon does not appear in an application process.

Description

technical field [0001] The patent of the invention belongs to the technical field of composite materials, and in particular relates to a wood-plastic co-extrusion profile and a production method thereof. Background technique [0002] Wood-plastic composite materials use renewable biomass resources such as woody plants, grasses, vines and their processing residues as the main raw materials. Through high-tech means such as physics, chemistry and biology, a certain proportion of plastic-based Wood & Biofiber Plastic Composites, commonly known as WPC, is a reversible, recyclable, multi-purpose new material that is processed and formed by a special process. At present, there are several types of wood-plastic materials / products that are widely used, including structural, decorative, packaging and special types, including wires, sheets, plates, pipes, profiles / profiles, etc., and their scope of application It can cover almost all fields where logs, plastics, plastic steel, aluminu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/06B32B27/18B29B9/02B29C47/00B29C47/08B29C59/02C08L97/02C08L101/00
Inventor 张之敬
Owner NINGBO HELONG NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products