Preparation method of ternary layered carbide Ti2SC (titanium sulfur carbide) material

A ternary layered, carbide technology, applied in the direction of carbide, carbon oxide/sulfur carbide, etc., to achieve the effect of lowering synthesis temperature, simplifying process and reducing material cost

Inactive Publication Date: 2013-08-21
WUHAN UNIV OF TECH
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In summary, regarding Ti 2 There are many articles on SC theoretical research and calculation, but about the use of elements to synthesize Ti 2 There are almost no reports on the method of SC, especially the synthesis under high temperature and high pressure conditions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of ternary layered carbide Ti2SC (titanium sulfur carbide) material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of ternary layered carbide Ti 2 The preparation method of SC material, using Al as an auxiliary agent to prepare dense Ti by high temperature and high pressure synthesis method 2 SC material, its raw materials include Ti powder, S powder, C powder and Al powder, the molar ratio of the four raw materials is Ti:S:C:Al=2:1.2:1:0.1, the specific steps are as follows:

[0022] (1) Weighing: Weigh Ti powder, S powder, C powder and Al powder, and the molar ratio of the four raw materials is Ti:S:C:Al=2:1.2:1:0.1;

[0023] (2) Mix the weighed raw material powder in alcohol evenly, dry it, and put it into a steel mold for pre-pressing;

[0024] (3) Sintering: Put the formed sample into a pyrophyllite mold, then put it into a high temperature and high pressure furnace for sintering, the heating rate is 150°C / min, the sintering temperature is 1400°C, the pressure is 4GPa, hold for 1h, and then cool naturally with the furnace , the ternary layered carbide Ti can be obtaine...

Embodiment 2

[0028] A kind of ternary layered carbide Ti 2 The preparation method of SC material, using Al as an auxiliary agent to prepare dense Ti by high temperature and high pressure synthesis method 2 SC material, its raw materials include Ti powder, S powder, C powder and Al powder, the molar ratio of the four raw materials is Ti:S:C:Al=2:1.0:1:0.1, the specific steps are as follows:

[0029] (1) Weighing: Weigh Ti powder, S powder, C powder and Al powder. The molar ratio of the four raw materials is Ti:S:C:Al=2:1.0:1:0.1;

[0030](2) Mix the weighed raw material powder in alcohol evenly, dry it, and put it into a steel mold for pre-pressing;

[0031] (3) Sintering: Put the formed sample into a pyrophyllite mold, and then put it into a high-temperature and high-pressure furnace for sintering. The heating rate is 100°C / min, the sintering temperature is 1200°C, the pressure is 6GPa, and the temperature is kept for 10 minutes, and then naturally cooled with the furnace , the ternary l...

Embodiment 3

[0034] A kind of ternary layered carbide Ti 2 The preparation method of SC material, using Al as an auxiliary agent to prepare dense Ti by high temperature and high pressure synthesis method 2 SC material, its raw materials include Ti powder, S powder, C powder and Al powder, the molar ratio of the four raw materials is Ti:S:C:Al=2:1.1:1:0.2, and the specific steps are as follows:

[0035] (1) Weighing: Weigh Ti powder, S powder, C powder and Al powder, and the molar ratio of the four raw materials is Ti:S:C:Al=2:1.1:1:0.2;

[0036] (2) Mix the weighed raw material powder in alcohol evenly, dry it, and put it into a steel mold for pre-pressing;

[0037] (3) Sintering: Put the formed sample into a pyrophyllite mold, and then put it into a high-temperature and high-pressure furnace for sintering. The heating rate is 100°C / min, the sintering temperature is 1300°C, the pressure is 4GPa, and the temperature is kept for 30 minutes, and then naturally cooled with the furnace , the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Vickers hardnessaaaaaaaaaa
compressive strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a ternary layered carbide Ti2SC (titanium sulfur carbide) material. Al (aluminum) is used as an assistant, and a high-temperature high-pressure synthesis method is used for preparing a compact Ti2SC material. Raw materials include Ti (titanium) powder, S (sulfur) powder, C (carbon) powder and Al powder, and the mol ratio of the four raw materials is as follows: Ti: S: C: Al=2: (1-1.4): 1: (0.1-0.2). The Ti2SC block material synthesized by the method is compact in structure, and the content of Ti2SC is more than 80 percent by weight; Al is used as the assistant, so that the melting point can be lowered; and by adopting the high-temperature high-pressure sintering method, the volatilization of the S powder can be maximally inhibited, and the Ti2SC material can be rapidly sintered and synthesized.

Description

technical field [0001] The invention relates to the field of novel structural materials, in particular to a ternary layered carbide Ti 2 Preparation method of SC material. Background technique [0002] Ti 2 SC as layered compound M n+1 AX n (where "M" stands for early transition elements, "A" stands for a main group element, "X" stands for C or N elements, n=1, 2 or 3), and has excellent properties of both metals and ceramics , like metal, has good thermal shock resistance, electrical and thermal conductivity, high temperature and easy plasticity, especially strong damage resistance and good machinability; like ceramics, it has good elasticity and rigidity, light weight, fatigue resistance and high temperature resistance. These excellent properties make them attractive for many applications, such as high-temperature structural materials. And Ti 2 SC is the smallest value of lattice constant c, and S is a non-metallic element, which makes Ti 2 SC has many special excel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/26C01B32/907
Inventor 宋京红涂勇威梅炳初朱文彬
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap