Three-layer co-extruded EVA (ethylene-vinyl acetate copolymer) long-life fog-dissipation environment-friendly multifunctional greenhouse film
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A three-layer co-extrusion, multi-functional technology, applied in the field of agricultural greenhouse film and its preparation, can solve the problems of single function, prone to fog droplets, short life and other problems, achieve good transparency, improve flexibility, coloring and molding processing good effect
Active Publication Date: 2015-04-29
HENAN YINFENG PLASTIC
View PDF4 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] Improving the current agricultural film to overcome defects such as single function, prone to fog droplets, and short life has become an urgent demand in the agricultural plastic product market
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0038] The raw material formula is as follows: each component is by weight percentage,
[0042] The double anti-masterbatch is 20% of dripping agent (glyceryl monostearate); 10% of light stabilizer (polysuccinate); 5% of talcum powder; 5% of polyethylene wax; 60% of PVC resin powder %;
[0043] The three-proof masterbatch is 20% of dripping agent (glyceryl monostearate); 10% of light stabilizer (pol...
Embodiment 2
[0046] Outer layer raw material formula: each component is calculated by weight percentage
[0047] Linear Low Density Polyethylene (LLDPE) 50%,
[0058] Linear Low Density Polyethylene (LLDPE) 30%,
[0059] Low density polyethylene (LDPE) 40%,
[0060] Three-proof masterbatch 10%;
[0061] The double anti-masterbatch is 20% of dripping agent (glyceryl monostearate); 10% of light stabilizer (polysuccinate); 5% of talcum powder; 5% of polyethylene wax; PVC resin powder? 60%;
[0062] The three-proof masterbatch is ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a nano fog-dissipation multifunctional greenhouse agricultural film, and in particular relates to a three-layer co-extruded EVA (ethylene-vinyl acetate copolymer) long-life fog-dissipation environment-friendly multifunctional greenhouse film, belonging to the field of agricultural mulching films. The raw material formula of an outer layer comprises the following components in percentage by weight: 20-50% of linear low-density polyethylene (LLDPE), 20-50% of low-density polyethylene (LDPE), 10-20% of metallocene polyethylene (mPE) and 5-10% of double-prevention masterbatch; the raw material formula of a middle layer comprises the following components in percentage by weight: 30-40% of ethylene-vinyl acetate copolymer (EVA), 20-40% of linear low-density polyethylene (LLDPE), 20-40% of low-density polyethylene (LDPE) and 5-10% of three-prevention masterbatch; the raw material formula of an inner layer comprises the following components in percentage by weight: 30-40% of ethylene-vinyl acetate copolymer (EVA), 10-20% of linear low-density polyethylene (LLDPE), 20-50% of low-density polyethylene (LDPE) and 5-10% of three-prevention masterbatch; and the formulas of the outer layer, the middle layer and the inner layer are uniformly mixed respectively, master batches are prepared by using a double-head thread screw double-screw extruding machine, a three-layer film is formed through a co-extrusion die head and is extruded out to prepare the multifunctional agricultural greenhouse film. Every quality technical index of the film reaches or exceeds a national standard, and a small part of the indexes is more than 2 times better than the national standard, so that the film is excellent in antiaging performance and cannot generate fog drops, and the service life of the film reaches more than 3 years.
Description
technical field [0001] The invention relates to an agricultural greenhouse film and a preparation process thereof, in particular to the preparation of a nanometer anti-fog greenhouse agricultural film by using EVA as a raw material, and belongs to the field of agricultural plastic films. Background technique [0002] Agricultural film is an important means of production in agriculture after seeds, fertilizers, and pesticides. Its application has brought a revolution to my country's agricultural production and has made important contributions to increasing agricultural efficiency and increasing farmers' income. Commonly used films are ordinary polyvinyl chloride film, polyvinyl chloride non-drip film, ordinary polyethylene film, polyethylene non-drip film, polyethylene multi-functional composite film and EVA multi-functional composite film. However, there are generally defects such as single function, prone to fog droplets, and short life. [0003] At present, domestic agric...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more