Lithium battery and electrode for same, and preparation method of solid electrolyte film
A solid electrolyte membrane and lithium-ion battery technology, applied in the field of materials, can solve the problems of high requirements for thin-film electrode equipment, organic solvent pollution, complex process, etc., and achieve the effects of simple equipment and process, pollution reduction, and simple equipment
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0030] Embodiment 1: In this embodiment, the positive electrode of the lithium ion battery is LiCoO 2 The preparation method of the electrode is carried out according to the following steps:
[0031] According to the mass ratio of 8.7:0.5:0.8, the active material LiCoO 2 , Conductive agent acetylene black and binder PVDF powder are weighed, the ball milling speed is 200~450r / min, and the ball mill is mixed evenly for 1 hour, and then the mixed material is transferred to the laser printing cartridge. The aluminum foil is fixed on the substrate with tape, and the uniform electrode to be prepared can be obtained by printing.
Example Embodiment
[0032] Specific embodiment 2: The preparation method of the positive electrode of the lithium ion battery in this embodiment is carried out according to the following steps:
[0033] According to the mass ratio of 8:1:1, the active material LiNi 1 / 3 Co 1 / 3 Mn 1 / 3 O 2, Conductive agent acetylene black and binder PVDF powder are weighed, the ball milling speed is 200~450r / min, and the ball mill is mixed evenly for 1 hour, and then the mixed material is transferred to the laser printing cartridge. The copper foil is fixed on the substrate with tape, and the uniform electrode to be prepared can be obtained by printing.
Example Embodiment
[0034] Specific embodiment three: the preparation method of the lithium ion battery negative graphite electrode in this embodiment is carried out according to the following steps:
[0035] According to the mass ratio of 8:1:0.5:0.5, the active material graphite, conductive agent acetylene black and binder (CMC, SBR) powder are weighed, and the ball milling speed is 200~450r / min. of substances transferred to the laser print cartridge. The copper foil was fixed on the substrate with tape, and the printing was repeated twice to obtain the uniform electrode to be prepared.
[0036] figure 1 The electrodes are laser-printed in this embodiment. The substrate is white paper, the base is the current collector copper foil, and the black is the active material electrode. from figure 1 It can be seen that electrodes can be printed according to the method and the size of the printed electrodes can be controlled by a computer.
[0037] figure 2 The SEM photograph of the electrode p...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap