Anti-static odorless odor-resistant dithio sponge rubber material as well as preparation method and application thereof

A disulfide sponge and anti-static technology is applied in the field of rubber processing to achieve the effects of low cost, elimination of odor and good use effect

Active Publication Date: 2013-09-11
际华制鞋工业有限公司
View PDF9 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide an antistatic, tasteless and deodorant disulfide sponge compound and its preparation method and application. Ya" technical problems to overcome the deficiencies of existing technologies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-static odorless odor-resistant dithio sponge rubber material as well as preparation method and application thereof
  • Anti-static odorless odor-resistant dithio sponge rubber material as well as preparation method and application thereof
  • Anti-static odorless odor-resistant dithio sponge rubber material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Embodiment 1 of the present invention: Antistatic tasteless and deodorant disulfide sponge rubber material, calculated in parts by weight, includes 100 parts of 1# standard rubber, 2.5 parts of sulfur, 1.9 parts of vulcanization accelerator, 8 parts of nano-zinc oxide, 13.5 parts of hard Fatty acid, 90 parts of clay, 4.5 parts of odorless foaming agent, 20 parts of high wear-resistant carbon black, 5 parts of conductive carbon black, 15 parts of 5# spindle oil, 10 parts of dibutyl phthalate, 2.5 parts of antibacterial and deodorant powder And 1.2 parts of sanxiangguan organic antibacterial agent XT-11; every 1.9 parts of vulcanization accelerator is composed of 0.5 parts of accelerator M, 1.2 parts of accelerator DM and 0.2 parts of accelerator TT; every 4.5 parts of odorless foaming agent is composed of 3 parts of hair Composition of foaming agent AC and 1.5 parts of foaming agent OBSH.

[0038] The preparation method of anti-static, odorless and deodorant disulfide sp...

Embodiment 2

[0040]Embodiment 2 of the present invention: Antistatic tasteless and deodorant disulfide sponge rubber material, calculated in parts by weight, includes 90 parts of 1# standard glue, 2 parts of sulfur, 1.7 parts of vulcanization accelerator, 7 parts of nano-zinc oxide, 11 parts of hard Fatty acid, 100 parts of clay, 4 parts of odorless foaming agent, 18 parts of high wear-resistant carbon black, 4 parts of conductive carbon black, 12 parts of 5# spindle oil, 10 parts of dibutyl phthalate, 2.2 parts of antibacterial and deodorant powder And 1 part of sanxiangguan organic antibacterial agent XT-11; every 1.7 parts of vulcanization accelerator is composed of 0.5 parts of accelerator M, 1.0 parts of accelerator DM and 0.2 parts of accelerator TT; every 4.5 parts of odorless foaming agent is composed of 3 parts of hair Composition of foaming agent AC and 1.5 parts of blowing agent OBSH.

[0041] The preparation method and application are the same as in Example 1.

Embodiment 3

[0042] Embodiment 3 of the present invention: Antistatic tasteless and deodorant disulfide sponge rubber material, calculated in parts by weight, includes 110 parts of 1# standard glue, 3 parts of sulfur, 2 parts of vulcanization accelerator, 9 parts of nano-zinc oxide, 15 parts of hard Fatty acid, 80 parts of clay, 6 parts of odorless foaming agent, 22 parts of high wear-resistant carbon black, 6 parts of conductive carbon black, 17 parts of 5# spindle oil, 12 parts of dibutyl phthalate, 2.8 parts of antibacterial and deodorant powder And 1.5 parts of sanxiangguan organic antibacterial agent XT-11; every 2.0 parts of vulcanization accelerator is composed of 0.5 parts of accelerator M, 1.3 parts of accelerator DM and 0.2 parts of accelerator TT; every 4.5 parts of odorless foaming agent is composed of 3 parts of hair Composition of foaming agent AC and 1.5 parts of blowing agent OBSH.

[0043] The preparation method and application are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-static odorless odor-resistant dithio sponge rubber material as well as a preparation method and an application thereof. The anti-static odorless odor-resistant dithio sponge rubber material comprises the following components in parts by weight: 90-110 parts of standard rubber, 2-3 parts of sulfur, 1.7-2 parts of vulcanization accelerator, 7-9 parts of nano zinc oxide, 11-15 parts of stearic acid, 80-100 parts of argil, 4-5 parts of odorless foaming agent, 18-22 parts of carbon black with high wear resistance, 4-6 parts of conductive black, 12-17 parts of spindle oil, 8-12 parts of dibutyl phthalate, 2.2-2.8 parts of anti-bacterial and odor-resistant powder and 1-1.5 parts of sanxiang organic guanidine antimicrobial XT-11. The dithio sponge rubber material formula and preparation process disclosed by the invention are searched and screened to obtain the optimal combination, so that a product obtained according to the technical scheme of the invention not only has the anti-static effect, but also can eliminate the peculiar smell of the dithio sponge and effectively inhibit the odor of hong kong feet. The preparation method is simple and easy, wide in material source and low in cost, and the product is good in use effect.

Description

technical field [0001] The invention relates to the field of rubber processing, in particular to an antistatic, odorless and deodorant disulfide sponge rubber material, a preparation method and application thereof. Background technique [0002] In general, in the manufacturing process of rubber shoes, the rubber sponge, which is the key component of rubber shoe shock absorption, is usually manufactured by one-time vulcanization molding or mold vulcanization (referred to as disulfide) process, while the sponge used in anti-static rubber shoes is a one-time vulcanization sponge. Due to the limitation of technological conditions, the primary vulcanized sponge rubber has low product grade and insufficient fashion, which cannot meet people's beautiful needs. Due to the usual use of pore forming agent H and the use of materials such as 2# standard glue, the sponge glue has an odor and produces "Hong Kong foot". Also there is no tasteless and deodorizing antistatic sponge of secon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/00C08K13/02C08K3/34C08K3/04C08K5/12C08K3/22C08K3/06C08J9/10C08J3/24B29B7/74A43B13/04
Inventor 晋齐怀石银平陈松雄田吉彭德彪廖甫江王春桥安廷飞
Owner 际华制鞋工业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com