Organic silicon heat-resistant finish paint and preparation method thereof

A silicone, heat-resistant technology, used in anti-corrosion coatings, coatings, etc., can solve the problems of poor mechanical strength, adhesion and corrosion resistance, poor drying, small use range and application, etc., to enhance adhesion and resistance. High temperature performance, good thermal stability

Inactive Publication Date: 2013-10-09
TIANCHANG JULONG TRAVEL PAINT
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the commonly used silicone high-temperature resistant coatings have excellent high-temperature resistance, this requirement is far from meeting the heat-resistant requirements of some special products; in addition, these heat-resistant coatings cannot be used without high-temperature baking. Barbecue with an open flame, otherwise a lot of smoke will be generated, and it cann

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic silicon heat-resistant finish paint and preparation method thereof
  • Organic silicon heat-resistant finish paint and preparation method thereof
  • Organic silicon heat-resistant finish paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Silicone heat-resistant topcoat consists of the following raw materials in parts by weight:

[0023]

[0024] The specific preparation method is as follows:

[0025] (1) Mix silicone resin, aluminum powder, mica powder, talcum powder, zinc phosphate, anti-sedimentation agent and some solvents according to the proportion and stir them into a paste;

[0026] (2) Put the uniformly mixed material in (1) into a sand mill for grinding for 20 minutes, so that the particle size of the material is not greater than 30 μm;

[0027] (3) Add a co-solvent and the remaining solvent to the material in (2) to disperse, and filter to obtain a silicone heat-resistant topcoat.

Embodiment 2

[0029] Silicone heat-resistant topcoat consists of the following raw materials in parts by weight:

[0030]

[0031] The specific preparation method is as follows:

[0032] (1) Mix silicone resin, aluminum powder, mica powder, talcum powder, zinc phosphate, anti-sedimentation agent and some solvents according to the proportion and stir them into a paste;

[0033] (2) Put the uniformly mixed material in (1) into a sand mill for grinding for 25 minutes, so that the particle size of the material is not greater than 30 μm;

[0034] (3) Add a co-solvent and the remaining solvent to the material in (2) to disperse, and filter to obtain a silicone heat-resistant topcoat.

Embodiment 3

[0036] Silicone heat-resistant topcoat consists of the following raw materials in parts by weight:

[0037]

[0038] The specific preparation method is as follows:

[0039] (1) Mix silicone resin, aluminum powder, mica powder, talcum powder, zinc phosphate, anti-sedimentation agent and some solvents according to the proportion and stir them into a paste;

[0040] (2) Put the uniformly mixed material in (1) into a sand mill for grinding for 30 minutes, so that the particle size of the material is not greater than 30 μm;

[0041] (3) Add a co-solvent and the remaining solvent to the material in (2) to disperse, and filter to obtain a silicone heat-resistant topcoat.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides organic silicon heat-resistant finish paint and a preparation method thereof. The organic silicon heat-resistant finish paint consists of an organic silicon resin, aluminum powder, mica powder, talcum powder, an anti-settling agent, a solvent and the like. The organic silicon heat-resistant finish paint has good high-temperature performance and high drying property, is subjected to surface drying within an hour and is subjected to hard drying within four hours; the adhesion force and corrosion resistance of the organic silicon heat-resistant finish paint are obviously improved.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an organosilicon heat-resistant topcoat and a preparation method thereof. Background technique [0002] Some equipment, such as exhaust pipes of automobiles, high-temperature reactors in petrochemical plants, and boilers in thermal power plants, are often in high-temperature and corrosive media. Their synergy will accelerate the corrosion and perforation of equipment, increase equipment maintenance costs, and affect production safety. pose great dangers. For the problem of high temperature oxidation corrosion of metal equipment, the use of high temperature resistant and anti-oxidation coating protection is an effective method. [0003] Most of the heat-resistant coatings used to coat high-temperature-resistant metal components and equipment on the market today, the paint film does not change color or fall off above 200°C, and still maintains appropriate physical and mechanical ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D183/04C09D5/10C09D7/12
Inventor 祝盆鑫孙巨福戴宇钧汪鹏程
Owner TIANCHANG JULONG TRAVEL PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap