High-strength antistatic polyphenylene sulfide material and preparation method thereof

The technology of polyphenylene sulfide and antistatic agent is applied in the field of high-strength antistatic polyphenylene sulfide material and its preparation. Strength-enhancing effect

Inactive Publication Date: 2013-12-04
SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyphenylene sulfide itself has good strength, but it still cannot meet the requirements in some application industries that require ultra-high strength materials. At this time, materials with higher strength are needed to meet their requirements. At the same time, in aerospace, petrochemical In the field of static electricity, the generation of static electricity will lead to great production safety problems, so the materials used in these industries are required to have excellent antistatic properties, and the application of polyphenylene sulfide is greatly restricted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Prepare raw materials according to the following components and parts by weight: 45 parts of polyphenylene sulfide, 55 parts of continuous glass fiber (12 μm in diameter), 0.4 part of silicone, 0.1 part of antioxidant 1010, 0.1 part of antioxidant 1076, 0.6 parts of coupling agent KH-570, 0.5 parts of ethoxylated aliphatic alkylamine;

[0031] (2) Control the speed of the high mixer to 1000rmp, the temperature to 40°C, mix for 10 minutes, mix the above raw materials through the high mixer at high speed, control the temperature of the extruder at 295-310°C, and pass the mixed material through the twin-screw extruder The product can be obtained by cutting the strands into pellets. Example 2

Embodiment 2

[0032] (1) Prepare raw materials according to the following components and parts by weight: 50 parts of polyphenylene sulfide, 50 parts of continuous glass fiber (10 μm in diameter), 0.2 part of calcium stearate, 0.1 part of antioxidant 1010, 0.2 part of antioxidant 1076, 0.7 parts of coupling agent KH-570, 1 part of ethoxylated aliphatic alkylamine;

[0033] (2) Control the speed of the high mixer to 800rmp, the temperature to 60°C, and mix for 5 minutes. The above raw materials are mixed at high speed by the high mixer, and the temperature of the extruder is controlled at 285-300°C. The product can be obtained by cutting the strands into pellets. Example 3

Embodiment 3

[0034] (1) Prepare raw materials according to the following components and parts by weight: 55 parts of polyphenylene sulfide, 45 parts of continuous glass fiber (12 μm in diameter), 0.3 part of stearyl alcohol, 0.2 part of antioxidant P262, 0.8 part of coupling agent KH570 , 0.8 part of ethoxylated aliphatic alkylamine;

[0035] (2) Control the speed of the high mixer to 950rmp, the temperature to 40°C, mix for 10 minutes, mix the above raw materials through the high mixer at high speed, control the temperature of the extruder at 285-310°C, and pass the mixed material through the twin-screw extruder The product can be obtained by cutting the strands into pellets. Example 4

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of polymer materials, and discloses a high-strength antistatic polyphenylene sulfide material and a preparation method thereof. The material is prepared from following components by weight: 45-55 parts of polyphenylene sulfide, 45-55 parts of glass fiber, 0.2-0.4 part of a lubricant, 0.2-0.4 part of an antioxidant, 0.6-1 part of a coupling agent and 0.5-1 part of an antistatic agent. The preparation method comprises steps of mixing uniformly the 45-55 parts of the polyphenylene sulfide, the 45-55 parts of the glass fiber, the 0.2-0.4 part of the lubricant, the 0.2-0.4 part of the antioxidant, the 0.6-1 part of the coupling agent and the 0.5-1 part of the antistatic agent at a high speed by a high-speed mixer, adding the mixture into a screw extruder, and stretching and pelletizing by the screw extruder to obtain a product. The material has permanent antistatic performance, and the cost of the material is largely reduced because of addition of the low-cost glass fiber, thus extending the application range of the material largely.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a high-strength antistatic polyphenylene sulfide material and a preparation method thereof. Background technique [0002] Polyphenylene sulfide (PPS) is a special engineering plastic with excellent comprehensive properties. PPS has excellent high temperature resistance, corrosion resistance, radiation resistance, flame retardancy, balanced physical and mechanical properties, excellent dimensional stability, and excellent electrical properties. It is widely used as a structural polymer material. Through filling, After modification, it is widely used as special engineering plastics. At the same time, PPS can also be made into various functional films, coatings and composite materials, and has been successfully applied in the fields of electronics, aerospace, automobile transportation, machinery and chemical industry. [0003] In the current lightweight process, "replaci...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L81/02C08K13/04C08K7/14C08K5/17B29C47/92B29C48/92
Inventor 孙鹏
Owner SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap