Formula of solvent-free thermal-spraying environment-friendly heavy anti-corrosion coating and preparation method of coating
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A thermal spraying, heavy-duty anti-corrosion technology, used in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems of polluted environment, shortened pipeline length, low construction efficiency, etc., and achieves excellent anti-corrosion performance, good impact resistance, The effect of high construction efficiency
Inactive Publication Date: 2013-12-18
XINHE NEW MATERIALS CO LTD
View PDF6 Cites 45 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The construction process requires the coating to have a long potency period, which limits the drying speed of the coating and cannot meet the construction process with special requirements for quick drying, and the one-time ingredients should not be too much, and must be used up within the specified time, otherwise it will be damaged. Block the rubber hose; clean the equipment after each construction, consume a large amount of solvent, pollute the environment, and cannot carry out continuous construction the next day, and the construction efficiency is low; during construction in winter, the viscosity is high, the coating needs to be preheated before construction, and the pressure should be increased appropriately. Shorten the length of the pipe so that the paint can be sprayed normally
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0032] The present invention will be described in detail below in conjunction with the description of the drawings and specific embodiments.
[0033] The formula of solvent-free thermal spraying environment-friendly heavy-duty anticorrosion coating of the present invention comprises main paint and curing agent, and each composition composition of described main paint comprises:
[0034] 25 parts by weight of liquid epoxy resin
[0035] Active diluent 10 parts by weight
[0036] Auxiliary 1.5 parts by weight
[0037] Anti-rust pigment 25 parts by weight
[0038] Pigment 9 parts by weight
[0039] Filler 28 parts by weight
[0040] Thixotropic agent 3 parts by weight;
[0041] Each composition of described curing agent comprises:
[0042] Amine resin 60 parts by weight
[0043] Active diluent 18 parts by weight
[0044] Thixotropic agent 6 parts by weight
[0045] Filler 30 parts by weight.
[0046] After the main paint and curing agent are prepared, they are mixed and...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the technical field of preparation of functional coating, and provides a formula of solvent-free thermal-spraying environment-friendly heavy anti-corrosion coating which is quick to cure, energy-saving and environment-friendly, tough and wearable, strong in adhesive force, good in shock resistance and excellent in corrosion resistance and a preparation method of the coating. Each composition of primary lacquer comprises liquid epoxy resin, an active diluent, auxiliaries, an anti-rusting pigment, a pigment, a filler and a thixotropic agent; each composition of a curing agent comprises amine resin, an active diluent, an anti-rusting pigment and a filler. The preparation method of the coating comprises the following steps: (1), preparing primary lacquer, wherein the liquid epoxy resin, the active diluent and the auxiliaries are taken and added into a cylinder for stirring while the anti-rusting pigment, the pigment, the filler and the thixotropic agent are added to be uniformly dispersed, and then grinding and filtering; (2), preparing the curing agent, wherein the amine resin, the active diluent, the thixotropic agent and the filler are added into the cylinder in sequence for dispersing at low speed and then dispersing at high speed and filtering; and (3), carrying out mixed construction on the primary lacquer and the curing agent by adopting a double-component airless sprayer to form a coating layer.
Description
technical field [0001] The invention relates to the technical field of preparation of functional coatings, in particular to a formulation of a solvent-free thermal spraying environmentally friendly heavy-duty anti-corrosion coating and a preparation method thereof. Background technique [0002] As people's requirements for environmental protection become increasingly urgent and strict, the development of solvent-free systems has become a new research direction in the coatings industry. High-performance and low-pollution coatings will replace polluting and traditional solvent-based coatings. Solvent-free environmentally friendly heavy-duty anti-corrosion coatings have no air pollution, are safe and non-toxic, and have excellent anti-corrosion properties. They have obvious advantages in durability, wear resistance, and mechanical strength. Compared with traditional solvent-based coatings, they have edge coverage Good quality, not easy to produce cracks, high construction effic...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.