Imitation sheepskin ultrafine fiber polyurethane synthetic leather and manufacturing method thereof

A superfine fiber, sheepskin-like technology, applied in chemical instruments and methods, synthetic resin layered products, textiles and paper making, etc. To meet the requirements, the surface plastic feeling is strong, etc., to achieve the effect of soft feel, strong softness, and fine folds

Active Publication Date: 2013-12-18
HUAFON MICROFIBER SHANGHAI
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using the above method to produce imitation sheep leather veneer leather with a softer feel, although the crease will be better, but the softness of the product cannot meet the requirements, the surface has a strong plastic feel, no real leather feel at all, high softness and fineness Creases can't have both

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] (1) Dye the original base fabric A and then oil it, the process is as follows:

[0049] Oil formula composition: HY-911 rubbing agent 20 parts, water 80 parts;

[0050] Squeeze pressure: 3kg / cm 2 ;Vehicle speed: 6m / min;The cloth feeding method is over-position and fixed-width drying, and the drying temperature is divided into 96°C for 1 minute, 100°C for 1 minute, 110°C for 1 minute, 120°C for 1 minute, 126°C for 2 minutes, and 110°C. °C for 1 minute.

[0051] (2) The oiled and dried base cloth B obtained in step (1) is subjected to the dry method of film transfer of release paper, and the process is as follows: dry method resin slurry composition: 100 parts of JF-S-8032 polyurethane resin , 60 parts of DMF, 20 parts of MEK, 10 parts of TOL, 5 parts of black color film, 0.02 parts of leveling agent YLC-2803, 10 parts of hand feeling agent AX-Ⅰ cationic leather slip agent; The amount is 20g / m 2 ;

[0052] The polyurethane binder is: 100 parts of one and a half polyu...

Embodiment 2

[0056] (1) After the original base fabric A is obtained, it is dyed and then oiled. The process is as follows:

[0057] Oil formulation composition: 5 parts of 8#H20 softener, 95 parts of water;

[0058] Squeeze pressure: 1kg / cm 2 ;Vehicle speed: 5m / min;The cloth feeding method is over-position and fixed-width drying, and the drying temperature is divided into 96°C for 1 minute, 100°C for 1 minute, 110°C for 1 minute, 120°C for 1 minute, 126°C for 2 minutes, and 110°C. °C for 1 minute.

[0059] (2) The oiled and dried base cloth B obtained in step (1) is subjected to the dry method of film transfer of release paper, and the process is as follows: dry method resin slurry composition: 100 parts of JF-S-8030 polyurethane resin , 40 parts of DMF, 40 parts of MEK, 1 part of UV-325 ultraviolet absorber, 1.5 parts of 2606 white color chip, 5 parts of 2A005 yellow color chip, 0.05 part of YLC-2803, 5 parts of AX-Ⅰ cationic leather slip agent;

[0060] The surface layer is coated on...

Embodiment 3

[0065] (1) After the original base fabric A is obtained, it is dyed and then oiled. The process is as follows:

[0066] Oil formula composition: 10 parts of HY-911 rubbing agent, 90 parts of water;

[0067] Squeeze pressure: 4kg / cm 2 ;vehicle speed: 7m / min; cloth feeding method is over-position fixed width drying, the drying temperature is divided into 96°C for 1 minute, 100°C for 1 minute, 110°C for 1 minute, 120°C for 1 minute, 126°C for 2 minutes, 110°C °C for 1 minute.

[0068] (2) The oiled and dried base cloth B obtained in step (1) is subjected to the dry method of film transfer of release paper, and the process is as follows: dry method resin slurry composition: 100 parts of JF-S-8032 polyurethane resin , 35 parts of DMF, 30 parts of MEK, 5 parts of TOL, 2 parts of UV-325 ultraviolet absorber, 3 parts of white color chip, 4 parts of 2A003 yellow color chip, 1 part of 4689 red color chip, 0.05 part of YLC-2803, AX-Ⅰ 10 parts of cationic leather slip agent; the surfac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses imitation sheepskin ultrafine fiber polyurethane synthetic leather and a manufacturing method thereof. The manufacturing method comprises the following steps: (1) applying oil to raw base cloth A and drying to obtain base cloth B; (2) bonding a sizing agent of surface layer dry-method polyurethane resin to the base cloth B obtained in the step (2) through a polyurethane bonder by a release paper dry-method film-shifting and surface-making technology, and stripping release paper to obtain the imitation sheepskin ultrafine fiber polyurethane synthetic leather. According to the method, the moderately soft base cloth is selected, the base cloth subjected to oil application is high in softness and leather feel, and the surface-overlaid ultrafine fiber polyurethane synthetic leather obtained through a dry-method surface-making process is good in fold lines and smooth feel. The imitation sheepskin ultrafine fiber polyurethane synthetic leather provided by the invention is exquisite in fold lines and smooth in hand feel, has a very good genuine leather feel and successfully solves the problem that exquisite fold lines and high softness of conventional imitation genuine leather ultrafine fiber synthetic leather cannot be compatible.

Description

technical field [0001] The invention relates to a superfine fiber polyurethane synthetic leather and a manufacturing method thereof, in particular to a sheepskin-like superfine fiber polyurethane synthetic leather and a manufacturing method thereof. technical background [0002] Genuine leather goods have always been regarded as a symbol of high-end leather goods. With the improvement of people's environmental protection requirements and the strengthening and deepening of animal protection awareness, the appeal to develop a high-simulation artificial leather that can replace genuine leather is becoming stronger and stronger. Microfiber polyurethane synthetic leather is a high-grade artificial leather developed on the basis of fully analyzing the microstructure and properties of natural leather. Its strength, chemical resistance, wrinkle resistance, abrasion resistance, processability and quality uniformity It is superior to genuine leather in terms of other aspects, and over...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/14B32B27/02B32B27/40B32B38/18
Inventor 诸葛磊刘勇胜谯应斌王贺玲韩芹
Owner HUAFON MICROFIBER SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com