Inorganic special historic building wall coating adopting flyash and preparation method thereof

A technology of fly ash and ancient buildings, applied in the field of fly ash inorganic special ancient building wall coatings and its preparation, can solve the problems of inability to achieve physical and chemical reactions, poor bonding performance, foaming and falling off, etc., and achieve adhesion Excellent knot performance, good adhesion and durability, and strong durability

Active Publication Date: 2015-06-17
GUANGXI UNIVERSITY OF TECHNOLOGY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Many ancient building walls need maintenance due to their age, but there are few special coatings on the market for ancient building walls
Although there are many types of wall coatings with different performances, most of the indoor and outdoor wall coatings on the market are not suitable as wall coatings for ancient buildings. They are prone to aging, blistering, fading, and whitening. The material of the paint is inconsistent with the material of the wall, and cannot have a physical and chemical reaction, resulting in poor bonding performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1: a kind of fly ash inorganic special ancient building wall coating, it is a kind of inorganic chemical component composition, and its each component and weight (Kg) are as follows:

[0024] Finely ground fly ash: 55

[0025] Quicklime Powder: 20

[0026] Edible sucrose: 5

[0027] Water: 25

[0028] The preparation method is as follows:

[0029] Put 55kg of finely ground fly ash, 20kg of quicklime powder, 5kg of edible sucrose, and 25kg of water into a blender, and stir at a constant speed for 15 minutes to prepare a fly ash inorganic special ancient building wall coating.

Embodiment 2

[0030] Embodiment 2: a kind of fly ash inorganic special ancient building wall coating, it is a kind of inorganic chemical component composition, and its each component and weight (Kg) are as follows:

[0031] Finely ground fly ash: 50

[0032] Slaked lime powder: 25

[0033] Edible sucrose: 8

[0034] Water: 20

[0035] The preparation method is as follows:

[0036] Put 50kg of finely ground fly ash, 25kg of slaked lime powder, 8kg of edible sucrose, and 20kg of water into a mixer respectively, and stir at a constant speed for 10 minutes to prepare a kind of fly ash inorganic special ancient building wall coating.

Embodiment 3

[0037] Embodiment 3: a kind of fly ash inorganic special ancient building wall coating, it is a kind of inorganic chemical component composition, and its each component and weight (Kg) are as follows:

[0038] Finely ground fly ash: 60

[0039] Quicklime powder: 25

[0040] Edible sucrose: 10

[0041] Water: 30

[0042] The preparation method is as follows:

[0043] Put 60kg of finely ground fly ash, 25kg of quicklime powder, 10kg of edible sucrose, and 30kg of water into a blender, and stir at a constant speed for 5 minutes to prepare a fly ash inorganic special ancient building wall coating.

[0044] In each embodiment of the present invention, the edible sucrose is yellow granulated sugar, and the finely ground fly ash refers to a powder whose fineness is less than 10% on a square hole sieve of 45 μm, and the lime is effective Ground quicklime powder or ground slaked lime powder with a calcium oxide content of more than 50%, wherein the fineness of the ground quicklime ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an inorganic special historic building wall coating adopting flyash and a preparation method thereof. The inorganic special historic building wall coating adopting flyash is prepared by utilizing industrial waste residues including levigated flyash and levigated quicklime powder or levigated slaked lime powder as cementing materials and edible cane sugar as an additive. The coating is an inorganic chemical component composition comprising the following components in parts by weight: 50-60 parts of flyash, 20-30 parts of lime, 5-10 parts of edible cane sugar and 20-30 parts of water. The coating has the advantages that by utilizing the characteristic that the flyash is grey and coincides with the colors of the historic grey bricks of historic building walls, the coating has good natural color and is resistant to fading, without adding color matching pigments; meanwhile, the coating has better caking property and durability and has the function of maintaining the natural colors of historic buildings; the coating is waterproof, fireproof, antibacterial, anti-aging, nontoxic, harmless and environment-friendly and insulates heat and sound; environmental pollution is avoided in the preparation process and the using process; the flyash is recycled, so that the coating has good social and economic benefits.

Description

technical field [0001] The invention relates to a coating and a preparation method thereof, in particular to a fly ash inorganic special ancient building wall coating and a preparation method thereof. Background technique [0002] Many ancient building walls need maintenance due to their age, but there are few special coatings on the market for ancient building walls. Although there are many types of wall coatings with different performances, most of the indoor and outdoor wall coatings on the market are not suitable as wall coatings for ancient buildings. They are prone to aging, blistering, fading, and whitening. The material of the paint is inconsistent with the material of the wall, and cannot have a physical and chemical reaction, resulting in poor bonding performance. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a kind of fly ash inorganic special ancient building wall coating which can react physically...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/10C04B18/08
CPCY02W30/91
Inventor 莫测先莫凯冬
Owner GUANGXI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com