Ceramic tile with dispersed shimmering powder and manufacturing method thereof

A manufacturing method and a dispersing technology, applied in the field of ceramic manufacturing, can solve the problems that the process material and the frit layer of the ceramic tile cannot be well integrated, the glitter is slightly thorny and easy to peel off, and the manufacturing method is simple and fast, and the surface is smooth. Noble, hard material effect

Active Publication Date: 2014-01-08
FOSHAN MAY ROSE CERAMIC
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this low-temperature firing process, the process material and the frit layer of the ceramic tile cannot be well integrated, so it is easy to absorb dirt during use, and it is easy to peel off when it is hit by collision. The patterns are pre-designed and distributed, and the patterns appear rigid and unnatural

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Present embodiment is a kind of black gold glaze white glitter ceramics, it comprises:

[0031] From top to bottom are the transparent frit layer, flash powder layer, colored glaze layer and white ceramic tile adobe with a water absorption rate lower than 3%; wherein the colored glaze layer includes two colored glazes of black and gold; its formula is as follows (mass ratio):

[0032] The black color glaze is: printing glaze 78%, black glaze pigment 6%, kaolin 10%, methyl cellulose 3% and sodium tripolyphosphate 3%;

[0033] The golden color glaze is: printing glaze 93%, golden glaze pigment 3%, methyl cellulose 3% and sodium tripolyphosphate 1%;

[0034] The flash powder layer is: 15% of the white mica flakes removed after passing through a 60-mesh sieve, 50% of the transparent frit dry particles and 35% of the printing glaze. ;

[0035] The transparent frit layer is: transparent frit dry granules.

[0036] The manufacturing method is as follows:

[0037] a. Accor...

Embodiment 2

[0054] Present embodiment is a kind of yellow and white glaze black gold flash powder ceramics, it comprises:

[0055] From top to bottom are the transparent frit layer, flash powder layer, colored glaze layer and white ceramic tile; wherein the colored glaze layer includes yellow and white colored glazes; its formula is as follows (mass ratio):

[0056] The yellow color glaze is: printing glaze 86%, yellow glaze pigment 4%, kaolin 10%;

[0057] The white color glaze is: printing glaze 87%, white glaze pigment 5%, kaolin 5%, methyl cellulose 1.5% and sodium tripolyphosphate 1.5%;

[0058] The flash powder layer is: a total of 15% of the black and yellow mica flakes removed after passing through a 40-mesh sieve, 35% of the transparent frit dry particles and 50% of the printing glaze;

[0059] The transparent frit layer is: transparent frit dry granules.

[0060] The manufacturing method is as follows:

[0061] a. According to the yellow and white distribution requirements of...

Embodiment 3

[0071] Present embodiment is a kind of yellow-brown glaze black gold flash powder ceramics, it comprises:

[0072] From top to bottom are the transparent frit layer, flash powder layer, colored glaze layer and white ceramic tile; wherein the colored glaze layer includes yellow and brown colored glazes; its formula is as follows (mass ratio):

[0073] The yellow color glaze is: printing glaze 86%, yellow glaze pigment 4%, kaolin 10%;

[0074] The brown color glaze is: printing glaze 80%, brown glaze pigment 6%, kaolin 10%, methyl cellulose 2% and sodium tripolyphosphate 2%;

[0075] The flash powder layer is: a total of 3% of the black and yellow mica flakes removed after passing through a 50-mesh sieve, 50% of the transparent frit dry particles and 47% of the printing glaze;

[0076] The transparent frit layer is: transparent frit dry granules.

[0077] The manufacturing method is as follows:

[0078] a. According to the yellow and brown distribution requirements of the til...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Widthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The ceramic tile with dispersed shimmering powder comprises a ceramic brick blank, a color glaze layer, a shimmering powder layer and a clear frit layer, wherein the color glaze layer comprises the following components in percentage by mass: screen printing glaze, glaze pigment, kaolin, methyl cellulose and sodium tripolyphosphate; and the shimmering powder layer comprises the following components in percentage by mass: mica sheet, oily stamp-pad ink and screen printing glaze. The manufacturing method comprises the following steps: manufacturing a flower screen, preparing the color glaze, preparing the shimmering powder, pushing the screen printing glaze and the shimmering powder, pushing the printing frit granules, firing, and sanding and polishing. The ceramic tile is hard, durable and beautiful; the shimmering powder mainly composed of mica sheet is suspended in the clear frit, and the shimmering powder is naturally dispersed to some extent; and the manufacturing method is simple and quick, can implement mass mechanical production under the condition of not greatly changing the existing equipment, is very simple to operate, and can be used for flexibly producing different design styles of ceramic tiles.

Description

technical field [0001] The invention relates to the technical field of ceramic manufacturing, in particular to a ceramic tile with scattered flash powder and a manufacturing method thereof. Background technique [0002] Ceramics is the general term for pottery and porcelain. The demand for ceramics in my country is very large. Statistics from China's ceramic industry show that my country's architectural ceramics output not only accounts for half of the world's total output, but also grows at an average annual rate of 16%. However, with the progress of society and the improvement of people's quality of life, people's requirements for ceramic tiles are not only limited to the role of ordinary building materials, but also require their beauty and natural and beautiful lines to make the owner look noble, generous and dignified. Taste and other temperament. [0003] In order to make the surface of the tiles show a flash powder pattern with a preset texture, the researchers inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/89
Inventor 刘春梅宫成伟黄胜群何钻华林典桥
Owner FOSHAN MAY ROSE CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com