Black water glass high-temperature paint and preparation method thereof

A technology of water glass and high-temperature paint, which is applied in the field of paint and paint, and can solve problems such as ozone pollution, difficulty in reaching chemical paint, and paralysis of the whole body

Inactive Publication Date: 2014-01-15
YUZHOU PASTEL HOME NANO EMULSIONI PAINT
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It not only produces ozone pollution to nature, but also causes headaches, general paralysis and other discomfort symptoms; however, lead, an organic compound, is one of the main culprits, and it is difficult for the chemical paints currently used to meet this standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] A black water glass high-temperature paint, characterized in that: it is composed of the following raw material components (by weight components)

[0011] Water glass 80~100 Glycerin 1.5~3 Zinc oxide 2~5 Zinc phosphate 2~5 Magnet powder 10~15 Glass powder 4~6 Dispersible rubber powder 1~3

[0012] Black water glass high-temperature paint, characterized in that: it is preferably made of the following raw material components (by weight components)

[0013] Water glass 80 Glycerin 1.5 Zinc oxide 2 Zinc phosphate 2 Magnet powder 10 Glass 4 Dispersible rubber powder 1

[0014] A method for preparing black water glass high-temperature paint, which is characterized in that: the above-mentioned raw materials are carried out according to the following sequence and steps, firstly the raw materials are mixed according to the above-mentioned ratio, and then stirred evenly; secondly, the paint slurry is transferred to the inside of a ball mill with a filling machine, Grind for 30-6...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a black water glass high-temperature paint and a preparation method thereof, and is characterized in that the paint is prepared by compatibility of the following raw material components by weight: 80-100 of water glass, 1.5-3 of glycerol, 2-5 of zinc oxide, 2-5 of zinc phosphate, 10-15 of a magnet powder, 4-6 of a glass powder, and 1-3 of a dispersible latex powder. The preparation method comprises the following order and steps: firstly, mixing the raw materials according to the proportion, and stirring evenly; secondly, transporting the paint slurry to the interior of a ball grinding mill by a filling machine, grinding for 30-60 minutes; thirdly, adding 5 parts of water and 1 part of a waterproof glue into a pot, slowly adding the ground slurry into the pot, successively adding 0.2 part of a defoaming agent and 2 parts of a lustre-enhancing agent (liquid wax), and thus obtaining the finished product. The paint has the advantages of corrosion prevention, rust protection, high-temperature resistance, strong adhesion force, acid resistance and water resistance, has the hardness which can reach 5 H, and has quite good corrosion prevention effect on steel in water.

Description

technical field [0001] The invention belongs to the technical field of paints and coatings, in particular to a black water glass high-temperature paint using water glass as a main raw material and a preparation method thereof. Background technique [0002] Paints and coatings are the last base material required for coating of buildings and various objects. After chemical paints and coatings are applied, they will continuously volatilize organic compounds (VOC) and free bodies (TDI). It not only produces ozone pollution to nature, but also causes discomfort symptoms such as headaches and general paralysis; however, lead, an organic compound, is one of the main culprits, and the chemical paints currently used are difficult to meet this standard. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies of the prior art, and provide a green, environmentally friendly, high-temperature resistant, fire-resistant, safe, low-cost, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/04C09D7/12C09D5/08
Inventor 李学法
Owner YUZHOU PASTEL HOME NANO EMULSIONI PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap